In a polyester film for a battery outer package, a thermal shrinkage stress Y_MD in an MD direction and a thermal shrinkage stress Y_TD in a TD direction at 200°C satisfy the following expressions, and at least one surface of the polyester film is subjected to corona discharge treatment or surface coating treatment.例文帳に追加

２００℃におけるＭＤ方向の熱収縮応力Ｙ_ＭＤ、ＴＤ方向の熱収応力Ｙ_ＴＤが下記式を満たし、少なくとも片面がコロナ放電処理、または表面コーティング処理された電池外装用ポリエステルフィルム。 - 特許庁

The film has a difference in the thermal shrinkage at 180°C of 0.2-1.5% between STD in the transverse direction and SMD in the longitudinal direction of the film and a difference in curling in terms of absolute values of 20% or smaller between CMD in the longitudinal direction and CTD in the transverse direction.例文帳に追加

フィルムの幅方向と長手方向の１８０℃における熱収の差｜Ｓ_TD−Ｓ_MD｜が０．２〜１．５％であり、かつフィルムの長手方向と幅方向のカールの差｜Ｃ_MD−Ｃ_TD｜が２０％以下である芳香族ポリアミドフィルムとする。 - 特許庁

The sum D_S80 of the flexural rigidity D_M80 of the protective sheet at 80°C in an MD (Machine Direction) and the flexural rigidity D_T80 of the protective sheet at 80°C in a TD (Transverse Direction) is 0.1×10^-6 to 1.2×10^-6 Pa m^3.例文帳に追加

前記保護シートの温度８０℃におけるＭＤについての曲げ剛性値Ｄ_Ｍ８０、およびＴＤについての曲げ剛性値Ｄ_Ｔ８０の合計値Ｄ_Ｓ８０は、０．１×１０^−６〜１．２×１０^−６Ｐａ・ｍ^３である。 - 特許庁

In the primary stretching-thermofixing process, the sheet is subjected to uniaxial primary stretching to an MD (machine direction) by two to three times at stretching temperature of 90-120°C, and is thereafter subjected to primary thermofixing at a temperature higher than the stretching temperature by 5 to 20°C.例文帳に追加

一次延伸熱固定工程において、延伸温度９０〜１２０℃でＭＤ（縦方向）に２〜３倍に一軸一次延伸した後、延伸温度より５〜２０℃高い温度で一次熱固定する。 - 特許庁

(1) A film MOR-c value is ≥1.05 and ≤5.0; (2) a molecular-chain principal-axis orientation angle is -30° to 30° against an MD direction; and (3) a difference between the maximum and the minimum values of the film MOR-c is 1.0 or below.例文帳に追加

（１）フィルムのＭＯＲ−ｃ値が１．０５以上５．０以下、（２）分子鎖主軸配向角がＭＤ方向に対して−３０から３０度、（３）フィルムＭＯＲ−ｃ値の最大値と最小値の差が１．０以下 - 特許庁

The uniaxially stretched A-PET sheet layer is formed by heating an A-PET sheet to 90-120°C to uniaxially stretching the heated A-PET sheet in an MD direction (longitudinal direction) by 2-5 times and subsequently thermally fixing the stretched sheet at a temperature higher than the stretching temperature by 5-20°C.例文帳に追加

一軸延伸Ａ−ＰＥＴシート層が、Ａ−ＰＥＴシートを９０〜１２０℃に加熱してＭＤ方向（縦方向）に２〜５倍一軸延伸した後、延伸温度より５〜２０℃高い温度で熱固定したものである。 - 特許庁

In the biaxially oriented film of polylactic acid, the melting starting temperature is 110-155°C, the heat-shrinkage rate at 100°C in the MD direction is 5-10%, and the rate in the TD direction is 5% or below.例文帳に追加

熱融解開始温度が１１０〜１５５℃であり、かつ１００℃での熱収縮率がＭＤ方向で５〜１０％、ＴＤ方向で５％以下であるポリ乳酸系二軸延伸フィルム。 - 特許庁

Practically, when the resin substrate of CD is molded, the gas of 70-80°C is ejected, and when the resin substrate of a hard disk(HD) or a photomagnetic disk (MD) is molded, the gas of 120-130°C is ejected.例文帳に追加

具体的には、ＣＤの樹脂基板を成型する場合には、７０〜８０℃の温度のガスをブローし、ハードディスク（ＨＤ）や光磁気ディスク（ＭＯ）の樹脂基板を成型する場合には、１２０〜１３０℃の温度のガスをブローする。 - 特許庁