The stainless cold rolled annealed steel sheet is subjected to alternating electrolytic treatment in an aqueous solution obtained by incorporating sulfuric acid ions and sodium ions into an aqueous solution comprising nitric acid of 50 to 200 g/l in such a manner that the concentration of the sulfate ions≥0.4 mol/l and the concentration of the sodium ions≥0.8 mol/l are satisfied, and having the pH of <1.例文帳に追加

ステンレス冷延焼鈍鋼板を、硝酸５０〜２００ｇ／ｌを含む水溶液中に、硫酸イオン濃度≧０．４ｍｏｌ／ｌかつナトリウムイオン濃度≧０．８ｍｏｌ／ｌを含み、さらにその水溶液のｐＨが＜１とした水溶液中で交番電解処理する。 - 特許庁

A stainless steel sheet is immersed in a molten alkali salt bath containing nitrate in an amount of 0. 5-8 mass % expressed in terms of sodium nitrate or is immersed in a molten alkali salt bath containing nitrate in an amount of 0.5-40 mass % expressed in terms of sodium nitrate and fluoride in an amount of 1-20 mass % expressed in terms of sodium fluoride, followed by acid pickling.例文帳に追加

ステンレス鋼板を、硝酸ナトリウムに換算して０．５〜８質量％の硝酸塩を含有する溶融アルカリ塩浴に浸漬するか、または硝酸ナトリウムに換算して０．５〜４０質量％の硝酸塩、およびふっ化ナトリウムに換算して１〜２０質量％のふっ化物を含有する溶融アルカリ塩浴に浸漬した後、酸洗する。 - 特許庁

After brass-plating is applied to the steel wire, a steel wire surface applied with the brass-plating is washed in hot water before wire drawing, and a lubricating coating film mainly composed of sodium silicate and/or potassium silicate is formed on the steel wire surface that has been washed in the hot water.例文帳に追加

鋼線に対しブラスめっきを施した後、伸線前に、ブラスめっきが施された鋼線表面を湯洗し、次いで、湯洗された鋼線表面に、ケイ酸ナトリウムおよび／またはケイ酸カリウムを主成分とする潤滑被膜を形成する。 - 特許庁

The surface of steel is brought into contact with a mixed aqueous solution containing sodium molybdate of 0.001 to 1.0 M and ammonium molybdate of 0.001 to 1.0 M, and is thereafter subjected to corrosion protective covering treatment.例文帳に追加

鋼材表面に、0.001M〜1.0Mのモリブデン酸ナトリウムと0.001M〜1.0Mのモリブデン酸アンモニウムとを含む混合水溶液を接触させる処理を施したのち、防食被覆処理を施す。 - 特許庁

As a container for housing the unit cells of the sodium-sulfur battery, a container made of a ferrite stainless steel which is superior in corrosion resistance against the corroding substance and has 16 wt.% or more of chromium content is used.例文帳に追加

ナトリウム−硫黄電池の単電池収納用の容器に、前記腐食性物質に対して耐食性に優れた、クロム含有率が１６重量％以上のフェライト系ステンレス鋼製の容器を用いる。 - 特許庁

The steel having the prior austenite grain boundary structure is immersed in a picric acid saturated aqueous solution, and then immersed in a thiosulfuric acid sodium saturated aqueous solution to selectively corrode the prior austenite (γ) grain boundaries.例文帳に追加

旧オーステナイト粒界を組織に持つ鋼をピクリン酸飽和水溶液に浸した後、チオ硫酸ナトリウム飽和水溶液に浸し、旧オーステナイト（γ）粒界を選択腐食させる。 - 特許庁

Chloride ion concentration in the inside surface of the steel pipe before forming the primer layer is 3 mg/m^2 or less in terms of the sticking amount of sodium chloride.例文帳に追加

プライマー層を形成する前の鋼管の内側表面における塩化物イオン濃度を塩化ナトリウム付着量に換算して３ｍｇ／ｍ^２以下とする。 - 特許庁

This method is characterized by electrolyzing the cold-rolled and annealed Cr-based stainless steel sheet in an aqueous solution, which includes sodium sulfate of 50-300 g/L, and nitrate ion of 20-250 g/L, and has pH of 3 or less.例文帳に追加