両層の接着性に優れ、成形後の熱収縮や硬化収縮などの伸び縮み及び使用時の荷重付加などにより、界面剥離が生じることがなく、美観に優れ意匠性が高い、繊維補強不飽和ポリエステル樹脂成形品を得る。例文帳に追加

To provide a molded product of a fiber-reinforced unsaturated polyester resin which is excellent in outstanding adhesive properties between both layers, and does not produce interfacial peeling due to a stretch/contraction such as heat shrinkage or cure shrinkage after molding and the addition of a load during use, and has a good appearance with excellent designing properties. - 特許庁

又、成形収縮率が０．５〜０．８％であること、９５℃雰囲気下で５．０ＭＰａの引張荷重をかけた高温クリープ特性において、破壊に至るまでの時間が１０００時間以上であること、前記混練後の樹脂組成物の成形前の含水量が２５０ｐｐｍ未満であることを個別の特徴とする。例文帳に追加

The elements are further characterized in each of a mold shrinkage of 0.5-0.8%, a high temperature creep property of ≥1,000 h till breakdown under conditions of 95°C atmosphere and 5.0 MPa tension load, and a moisture content in the resin composition, of <250 ppm after kneading and before molding. - 特許庁