cerium (IV) oxideとは 意味・読み方・使い方

Thereby, the cerium(IV) oxide nanotubes each having such a tubular structure that the diameter is 20-500 nm and the length is several hundred nm to several μm can be obtained.例文帳に追加

これにより、直径２０〜５００ｎｍで長さ数百ｎｍ〜数μｍのチューブ構造を有する酸化セリウム（IV）ナノチューブを得ることができる。 - 特許庁

To provide a method for manufacturing a molding of an adsorbent for removing a sulfur compound, by which an inorganic oxide of a metal of group III or group IV of a periodic table such as cerium oxide can be molded even when the inorganic oxide is subjected to extrusion molding so that the desulfurizing performance of the molded inorganic oxide can be kept high.例文帳に追加

酸化セリウム等の周期律表第３族もしくは第４族金属の無機酸化物を、押出し成形する際においても、成形が可能で、かつ脱硫性能を高く維持できる硫黄化合物除去用吸着剤成形体の製造方法を提供する。 - 特許庁

After producing a suspension of a cerium hydroxide (III) which reacts with a cerium (III) salt and an alkaline substance in the aqueous media under the inert gas atmosphere, it is manufactured from the process which produces the sol containing the crystalline cerium oxide (IV) by immediately blowing oxygen or gas containing oxygen into the suspension, and the process which wet crushes the obtained sol.例文帳に追加

不活性ガス雰囲気下に水性媒体中でセリウム（III）塩とアルカリ性物質を反応させて水酸化セリウム（III）の懸濁液を生成した後、直ちに該懸濁液に酸素又は酸素を含有するガスを吹き込み結晶性酸化第二セリウム粒子を含有するゾルを生成する工程、及び得られたゾルを湿式粉砕する工程から製造する。 - 特許庁

Silica of ≤0.1 μm in grain size and cerium (IV) oxide are respectively added at 2 to 6 wt.% and 0 to 45 wt.% to a slurry or aqueous solution of acidic sulfate and the viscosity of the slurry or solution is specified to 5 to 90 Pa.S.例文帳に追加

酸性硫酸塩のスラリーあるいは水溶液に、粒径０．１μｍ以下のシリカおよびセリアを、それぞれ２〜６ｗｔ％、０〜４５ｗｔ％添加し、粘度を５〜９０Ｐａ・ｓにする。 - 特許庁

The sol containing the crystalline cerium oxide (IV) is as follows: the particle size which is converted from the specific surface area by the gas adsorption method is 10-200 nm and the ratio of the particle size measured by the dynamic light scattering method and the particle size converted from the specific surface area by the gas adsorption method is between 2 and 6.例文帳に追加

ガス吸着法による比表面積から換算した粒子径が１０〜２００ｎｍであり、且つ（動的光散乱法で測定した粒子径）／（ガス吸着法による比表面積から換算した粒子径）の比が２〜６の範囲にある結晶性酸化第二セリウム粒子を含有するゾル。 - 特許庁

When the inorganic oxide of the metal of group III or group IV of the periodic table is molded, at least one compound of the metal selected from the group consisting of cerium, zirconium and titanium is added to the inorganic oxide as a binder, cellulose is added to the inorganic oxide as an auxiliary molding agent and the obtained mixture is molded.例文帳に追加

周期律表第３族もしくは第４族金属の無機酸化物を成形するに際して、セリウム、ジルコニウム及びチタンからなる群から選ばれる少なくとも一種の化合物をバインダーとし、セルロースを成形助剤として添加して成形することを特徴とする無機酸化物成形体の製造方法である。 - 特許庁