cold rolled finishとは 意味・読み方・使い方

As for the method for producing the same, the average surface roughness (Ra) of the cold rolled sheet is controlled to ≤0.45 μm, and, moreover, the partial pressure ratio between hydrogen and water vapor (PH2O/PH2) in an annealing atmosphere in finish annealing is controlled to ≤0.02.例文帳に追加

その製造方法として、冷延板の平均表面粗度（Ra）を0.45μm 以下とし、また、仕上焼鈍における焼鈍雰囲気の水素水蒸気分圧比(PH_2O/PH_2)を0.02以下とする。 - 特許庁

The rolled copper alloy foil can be produced by performing annealing in a thickness of 150 to 400% of the foil thickness of the product, next performing cold rolling to a thickness of ≤103% of the thickness of the product foil, thereafter performing annealing as well and subsequently performing finish rolling or/and flattening treatment with applied tension.例文帳に追加

この圧延銅合金箔は、製品の箔厚さの１５０〜４００％の厚さにおいて焼鈍を行い、次いで製品箔の厚さの１０３％以下の厚さまで冷間圧延後さらに焼鈍を行い、その後仕上げ圧延又は／及び張力を加えた平坦化処理を行うことにより製造できる。 - 特許庁

To provide a work roll for rolling and a rolling method for reducing required rolling power by lowering rolling load while preventing the defective biting of a material to be rolled or the like caused by slip in the hot finish rolling and/or cold-rolling of an aluminum plate or an aluminum-alloy plate.例文帳に追加

アルミニウム板又はアルミニウム合金板の熱間仕上げ圧延及び／又は冷間圧延において滑りを原因とする被圧延材の咬み込み不良等を防止しつつ圧延荷重を低下して所要圧延動力を低減できる圧延用ワークロール及び圧延方法を提供する。 - 特許庁

On the route, it is desirable to transfer a part or the whole of slabs to be finish-rolled after being ejected from the DHCR exclusive heating furnace or the other heating furnace (HCR (Hot Charge Rolling) or CCR (Cold Charge Rolling)exclusive heating furnace 1, 2) besides the slab to be charged into the heating furnace transferred from the continuous caster.例文帳に追加

前記ルートには、連続鋳造設備から送られてきた加熱炉未装入スラブのほか、ＤＨＣＲ専用加熱炉またはその他の加熱炉（ＨＣＲ・ＣＣＲ専用加熱炉１、２）から抽出後に圧延未了となっているスラブも一部あるいは全部乗せることが好ましい。 - 特許庁

To provide a manufacturing method for a cold-rolled steel sheet with a finish thickness of ≤0.2 mm, capable of suppressing defects of flatness, such as an edge wave and a center buckle, and also effectively suppressing defects of shape, which are caused by minute irregularities generated on the whole surface of the steel sheet.例文帳に追加

耳伸びや、腹伸びなどの平坦度不良を抑制するとともに、鋼板全面に発生する微小な凹凸による形状不良についても有効に抑制することができる、仕上げ厚みが0.2ｍｍ以下の冷延鋼板の製造方法を提供することにある。 - 特許庁

In the method for producing the hot rolled wire rod for cold forging, the steel having the above steel components is subjected to finish rolling in the temperature range from an Ar3 point to an Ar3 point+150°C and is thereafter cooled in the range from an Ar1 point to 300°C at a cooling rate of 5 to 40°C/s.例文帳に追加

及び上記鋼成分を有する鋼を、Ａｒ３点からＡｒ３点＋１５０℃の温度範囲で仕上圧延後、Ａｒ１点から３００℃の間を５〜４０℃／秒の冷却速度で冷却することを特徴とする冷間鍛造用熱間圧延線材の製造方法。 - 特許庁

The decorative film comprises a metal foil such as an aluminium and stainless steel foil and the like which has an uneven pattern on its surface by the working of a hairline finish, a sand finishing operation and the like and a transparent resin film which are laminated together, and the decorative metal sheet comprises this decorative film which is laminated on a substrate such as a cold-rolled steel and the like.例文帳に追加

ヘアライン加工やサンド仕上げなどの加工を施して表面に凹凸模様を付与したアルミニウムやステンレススチールなどの金属箔と透明樹脂フィルムとを積層して化粧フィルムとし、この化粧フィルムを冷延鋼板などの基板に積層して化粧板とする。 - 特許庁

The manufacturing method comprises, hot rolling a slab; cold rolling it to obtain a final sheet thickness, after annealing the hot rolled sheet when needed, or directly after hot rolling, subsequently final annealing it, and temper rolling it to finish the surface roughness so as to be larger than 3.0 μm.例文帳に追加

製造に当たっては、スラブの熱間圧延を行い、必要により、熱延板焼鈍を行ってから、あるいは熱間圧延まま、冷間圧延を行い最終板厚とし、次いで仕上げ焼鈍、調質圧延を行い表面粗さを0.3 μｍ以上に仕上げる。 - 特許庁