A gardening block is manufactured by throwing a concrete including: a binder (B); a fine aggregate (S); a coarse aggregate (WC); water (W); and a pigment (G) in a form.例文帳に追加

ガーデニングブロックは、結合材（Ｂ）と、細骨材（Ｓ）と、粗骨材（ＷＣ）と、水（Ｗ）と、顔料（Ｇ）とを含むコンクリートを型枠内に投入することにより製作される。 - 特許庁

In a manufacturing method, cemente c, fine aggregate s, coarse aggregate S and mixing water W which are components of concrete are prepared according to the proportional ratio, the mixing water W is divided into two parts of primary mixing water W1 and secondary mixing water W2, and they are primarily kneaded.例文帳に追加

製造方法では、配合比に従って、コンクリートの構成材料であるセメントｃ，細骨材ｓ,粗骨材Ｓ，練り混ぜ水Ｗが準備され、練り混ぜ水Ｗは、一次練り混ぜ水Ｗ１と、二次練り混ぜ水Ｗ２の二つに分割されて、一次混練が行われる。 - 特許庁

The water-permeable/water-retentive concrete or mortar is obtained by solidifying the composition containing fine aggregate obtained by milling original aggregate, cement a CMC aqueous solution having ≥100 mPa s viscosity and is used as a paving block, a roadbed block, porous concrete or a mortar product.例文帳に追加

本発明の透水・保水性コンクリート又はモルタルは、骨材を磨砕処理した細骨材と、セメントと、粘度１００mPa・s以上のＣＭＣ水溶液とを含む組成物を固化したものであり、例えば、舗装ブロック、路面ブロック、多孔質コンクリート又はモルタル製品に利用できる。 - 特許庁

The repairing material for cross sectional deficits of a concrete structure contains cement, fine aggregate, a water-soluble organic solvent with a boiling point of 30-100°C, and a thickener and its viscosity at 20°C is higher than 20 Pa s to 200 Pa s.例文帳に追加

セメントと、細骨材と、沸点が３０〜１００℃の水溶性有機溶剤と、粘稠化材とを含有し、２０℃での粘度が２０Ｐａ・ｓを超え２００Ｐａ・ｓ以下であることを特徴とするコンクリート構造物断面欠損の修復材。 - 特許庁

The hydraulic composition for ultrahigh strength concrete includes cement, an inorganic powder, fine aggregate, coarse aggregate, a specific dispersant composition and water, and has a W/P ratio of 10-14.5 wt.%, an S/a ratio of 20-33 vol.% and an initial slump value of 0-5 cm.例文帳に追加

セメント、無機粉末、細骨材、粗骨材、特定の分散剤組成物、及び水を含有し、Ｗ／Ｐが１０〜１４．５重量％、Ｓ／ａが２０〜３３体積％、初期スランプ値が０〜５ｃｍである、超高強度コンクリート用水硬性組成物。 - 特許庁

The mortar may contain fine aggregate of a maximum particle diameter of 0.8 mm or less in the range of 1.5 or less as the mass ratio (S/B) with binding material consisting of cement and a quick-hardening material.例文帳に追加

前記モルタルは、最大粒子径０．８ｍｍ以下の細骨材を、セメントおよび急硬材からなる結合材との質量比（Ｓ／Ｂ）が１．５以下の範囲で含有してもよい。 - 特許庁

The high fluidity mortar composition contains portland cement, inorganic powder, an inorganic expanding material, fine aggregate, and a thickener, wherein the thickener has viscosity of 10-2,000 mPa s in the form of 2 mass% aqueous solution at 20°C.例文帳に追加

ポルトランドセメント、無機粉体、無機系膨張材、細骨材及び増粘剤を含み、増粘剤は、２０℃における２質量％水溶液の粘度が１０〜２０００ｍＰａ・ｓである、高流動モルタル組成物。 - 特許庁

The repairing material for cross sectional deficits of a concrete structure comprises cement, fine aggregate, a water-soluble organic solvent with a boiling point of 30-100°C, and a thickener and has a viscosity at 20°C of higher than 500 Pa s and 3,000 Pa s or less.例文帳に追加

セメントと、細骨材と、沸点が３０〜１００℃の水溶性有機溶剤と、粘稠化材とを含有し、２０℃での粘度が５００Ｐａ・ｓを超え３０００Ｐａ・ｓ以下であることを特徴とするコンクリート構造物断面欠損の修復材。 - 特許庁