reheating furnaceとは 意味・読み方・使い方

This method for producing the seamless steel pipe, by which, after reheating the steel pipe obtained by pipe-making through a plug-mill, with a reheating furnace, a reduced-rolling is performed with a reducing mill, is improved.例文帳に追加

プラグミルで造管して得た鋼管を再加熱炉で再加熱した後、絞り圧延機で製品サイズに絞り圧延する継目無鋼管の製造方法を改良した。 - 特許庁

The method for producing the steel sheet includes: rapidly heating the steel sheet to ≥0.7×T_1(°C) when continuously annealing the steel sheet after water-quenching, wherein T_1(°C) represents the furnace temperature in the reheating zone; and applying tempering heat-treatment to the steel sheet in the reheating zone.例文帳に追加

本発明の鋼板の製造方法は、鋼板を連続焼鈍するにあたり、水焼入れ後、再加熱帯炉温をT_1（℃）とした時、0.7×T_1（℃）以上まで鋼板を急速加熱し、次いで鋼板を再加熱帯にて焼戻し熱処理する。 - 特許庁

This heat treatment method includes processes of quenching a work 2 by cooling the work by a refrigerant in a quenching treatment furnace 3; and tempering the quenched workpiece 2 by reheating the workpiece in a tempering treatment furnace 4.例文帳に追加

熱処理方法は、ワーク２を焼き入れ処理炉３にて冷媒で冷却して焼き入れする工程と、焼き入れされたワーク２を焼き戻し処理炉４にて再加熱して焼き戻しする工程とを備える。 - 特許庁

To provide a hot rolling method which can control hot finishing temperature at a proper, designated temperature, even when edges of a slab are overheated because of short retention time in a slab reheating furnace.例文帳に追加

スラブの在炉時間が短くてスラブの端部過加熱が生じたような場合でも、仕上圧延機出側温度を適正な所望値に制御することができる熱間圧延方法を提供する。 - 特許庁

A slab cast with a continuous caster 1 is directly fed to a rogher rolling mill 2 without passing through a slab reheating furnace and formed to the crude bar with the rougher-rolling.例文帳に追加

連続鋳造機１で鋳造されたスラブは、スラブ再加熱炉を通過することなく、粗圧延機２に直接送られ、粗圧延によって粗バーとされる。 - 特許庁

After reheating a panel B2 after preforming up to the austenitizing temperature with a heating furnace 3, the shape of a pressed part is adjusted by performing the restrike forming by press quenching method by supplying the panel to a drawing die 2.例文帳に追加

予備成形後のパネルＢ２をオーステナイト化温度まで加熱炉３にて再度加熱した上で、絞り成形型２に投入してプレス焼入れ法によるリストライク成形を行うことにより成形品の形状を整える。 - 特許庁

The wall thickness of the steel pipe subjected to fixed diameter rolling is set at ≤4 mm, the soaking time at a predetermined temperature in the heating furnace is set at the billet diameter (mm)×0.14-0.35 min, and the soaking time at a predetermined temperature in the reheating furnace is set at the bare pipe wall thickness (mm)×3.0-10.0 min.例文帳に追加

定径圧延後の鋼管の肉厚を４ｍｍ以下とし、加熱炉における所定温度での均熱時間をビレット直径（ｍｍ）×０．１４〜０．３５分とし、再加熱炉における所定温度での均熱時間を素管肉厚（ｍｍ）×３．０〜１０．０分とする。 - 特許庁