vinyl graft polymerizationとは 意味・読み方・使い方

The graft copolymer is obtained by using a polymerization initiator having ≥1.0 g/100 cm^3 aqueous solubility in graft-copolymerization of a vinyl-based monomer in the presence of an acrylic rubber, and the thermoplastic resin composition comprises the graft copolymer and a vinyl-based copolymer.例文帳に追加

アクリルゴムの存在下にビニル系単量体をグラフト共重合する際、水への溶解度が１．０ｇ／１００ｃｍ^3以上の重合開始剤を使用して得られるグラフト共重合体及び該グラフト共重合体とビニル系共重合体からなる熱可塑性樹脂組成物。 - 特許庁

The kind of the thermoplastic resin (A) is not limited but it is preferably a graft polymer prepared by graft polymerization of at least an aromatic vinyl monomer in the presence of a rubber-like monomer and/or a polystyrene resin prepared by polymerization of an aromatic vinyl monomer.例文帳に追加

（Ａ）熱可塑性樹脂の種類は特に限定されないが、ゴム質重合体の存在下に少なくとも芳香族ビニル単量体をグラフト重合させたグラフト重合体及び／又は少なくとも芳香族ビニル単量体を重合させてなるポリスチレン系樹脂であることが好ましい。 - 特許庁

A graft copolymer is used to manufacture a laser engravable relief printing plate, and the graft copolymer is obtained by a free radical polymerization of a vinyl ester in the presence of a polyalkylene oxide and a subsequent hydrolysis of an ester group.例文帳に追加

グラフト共重合体がレーザー彫刻可能な凸版印刷版の製造に使用され、グラフト共重合体が、ポリアルキレンオキシドの存在下でビニルエステルのラジカル重合、次いでエステル基の加水分解により得られる。 - 特許庁

The functional graft compound includes a main chain made of at lest one diol having one or more double bonds in the molecule, and a side chain joined to the main chain through graft polymerization of a functional monomer having a vinyl group.例文帳に追加

少なくとも分子内に一つ以上の二重結合を有する一種以上のジオールを主鎖とし、この主鎖にビニル基を有する機能性単量体をグラフト重合により結合させて側鎖とした。 - 特許庁

The thermoplastic resin composition comprises 0.1-99.9 mass % of a polylactic acid-based polymer (A) and 99.9-0.1 mass % of a graft copolymer (B) prepared by the graft-polymerization of a rubber-based polymer with vinyl monomers.例文帳に追加

ポリ乳酸系重合体（Ａ）０．１〜９９．９質量％と、ゴム質重合体にビニル系単量体をグラフト重合して得られたグラフト共重合体（Ｂ）９９．９〜０．１質量％とからなる熱可塑性樹脂組成物。 - 特許庁

To provide a process for producing a vinyl chloride resin that reduces an amount of a scale adhered to a vessel wall, a jacket and the like of a polymerization vessel during the graft polymerization of a vinyl monomer composed mainly of a vinyl chloride monomer onto an acrylic copolymer and attains a short production time and excellent productivity.例文帳に追加

本発明は、アクリル系共重合体に塩化ビニル単量体を主体とするビニル系単量体をグラフト重合する際に重合器の器壁、ジャケット等にスケールの付着量の少なく、製造時間が短くて生産性の優れた塩化ビニル系樹脂の製造方法を提供する。 - 特許庁

In producing the graft polymer latex by performing emulsion graft polymerization of a vinyl monomer in the presence of a rubbery polymer latex, the rubbery polymer latex is beforehand heated to a temperature substantially higher than the reaction temperature in the emulsion graft polymerization and then supplied to the reactor for the emulsion graft reaction.例文帳に追加

ゴム質重合体ラテックスの存在下にビニル系単量体を乳化グラフト重合してグラフト重合体ラテックスを製造するに際し、予め該ゴム質重合体ラテックスを該乳化グラフト重合時の反応温度より実質的に高い温度まで加温した後、乳化グラフト反応槽に供給することを特徴とするグラフト重合体ラテックスの製造方法。 - 特許庁

The method for producing the graft copolymer comprises subjecting a gummy polymer latex formed by the emulsion polymerization to devolatilization treatment, carrying out graft polymerization of a vinyl monomer in the presence of the gummy polymer latex after the devolatilization treatment to afford the graft copolymer latex, and recovering the graft copolymer therefrom as the powder, by using a circulation type spray drier.例文帳に追加

乳化重合により得られるゴム質重合体ラテックスを脱揮処理し、脱揮処理後のゴム質重合体ラテックスの存在下で、ビニル単量体をグラフト重合して得られるグラフト共重合体ラテックスを、循環式噴霧乾燥機を用いて粉体として回収する、グラフト共重合体の製造方法。 - 特許庁