「Graphite」を含む例文一覧(4640)
＜前へ 1 2 .... 78 79 80 81 82 83 84 85 86 .... 92 93 次へ＞- A powdery carbon, a powdery granite porphyry, a powdery tourmaline and a clay, and a powdery graphite silica if desired, are mixed, kneaded, formed and fired to form a substantially white porous body.
粉末状炭、粉末状麦飯石、粉末状トルマリンおよび粘土の各原料成分を混練し、必要に応じて上記原料成分に粉末状黒鉛硅石をも加えて混練し、該混練物を成形し、該成形体を焼成して得られる実質的に白色の多孔性焼成物を提供する。 - 特許庁 - In the ferrite based cast iron containing 2.5 to 4% C, 2 to 3.6% Si and 0.1 to 1.0% Mn, and containing 0.4 to 1.5% Al and 0.15 to 0.5% Ti and the balance iron with inevitable impurities, graphite particles are dispersed.
本発明のフェライト系鋳鉄は、Ｃ：２．５〜４％、Ｓｉ：２〜３．６％およびＭｎ：０．１〜１．０％を夫々含有すると共に、Ａｌ：０．４〜１．５％およびＴｉ：０．１５〜０．５％を含有し、残部が鉄および不可避的不純物からなり、且つ黒鉛粒子が分散したものである。 - 特許庁 - The concrete correlation between the metallic structure in which graphite particles are dispersed and breakage is obtained by using an inspection surface as a breakage surface 1a of a tensile test piece 1 in a tensile test, and much labor is not required for inspection by dispensing with polishing of the inspection surface or the like.
検査面を引張試験における引張試験片１の破断面１ａとすることにより、黒鉛粒が分散した金属組織と破断との具体的な関連付けができるようにするとともに、検査面の研磨等を不要として、検査に手間がかからないようにした。 - 特許庁 - In this heat pipe having a flat metallic member 1 having an internal space, and the operating fluid enclosed in the internal space, a sheet-like graphite 4 having heat conductivity in the main plane direction higher than that of a metallic member 1, is fixed to the inner wall in the main plane direction of the flat plate-shaped metallic member 1.
内部空間を有する平板状金属部材1と、内部空間に封入された作動液とを有するヒートパイプであって、平板状金属部材1の主平面方向の内壁には、金属部材1よりも主平面方向の熱伝導率の大きいシート状グラファイト4が固定されている。 - 特許庁 - The rubber composition containing the silicone rubber: 100 pts.mass, a silicone oil having kinematic viscosity at 23°C of 100-10,000 mm^2/sec: 0.1-20 pts.mass, and at least one kind of graphite and silica having a hydrophobized surface: 5-50 pts.mass at total is molded to make the wiper blade.
シリコーンゴム：１００質量部、２３℃における動粘度が１００〜１０，０００ｍｍ^２／秒のシリコーンオイル：０．１〜２０質量部、グラファイト及び表面を疎水化したシリカのうち少なくとも１種：合計で５〜５０質量部を含有するゴム組成物を成型して、ワイパーブレードとする。 - 特許庁 - A polyimide film having a thickness of 12.5 to 125 μm and a birefringence of ≥0.12 is heat-treated at ≤2,800°C or ≤3,000°C, so as to obtain the artificial film-like graphite in which electric resistance ratio in 77K to room temperature or electric resistance ratio in 4K to room temperature is low.
厚さ１２．５μｍ以上１２５μｍ以下、複屈折が０．１２以上のポリイミドフィルムを２８００℃以下又は３０００℃以下で熱処理することにより、室温に対する７７Ｋにおける電気抵抗比、又は室温に対する４Ｋにおける電気抵抗比が小さい人造のフィルム状グラファイトを得る。 - 特許庁 - In the negative electrode plate, a negative electrode mixture layer W4 containing a carbon material in which an amorphous carbon material of a main material and a graphite material of a sub-material are mixed as a negative electrode active material capable of insertion and desorption of lithium ions is formed on both sides of a rolled copper foil W3.
負極板では、リチウムイオンを挿入・脱離可能な負極活物質として主材料の非晶質炭素材および副材料の黒鉛材が混合された炭素材料を含む負極合剤層Ｗ４が圧延銅箔Ｗ３の両面に形成されている。 - 特許庁 - To provide a welding rod that is applicable to joining by welding between members made of spheroidal graphite cast iron and to repairing by welding of these members, that produces a weld zone having mechanical properties comparable to those of a base material, and that excels in welding workability as well as in appearance.
球状黒鉛鋳鉄製の部材同士の溶接接合、および、球状黒鉛鋳鉄製の部材の補修溶接に適用でき、溶接部が母材と同等の機械的特性を有し、溶接作業性および外観にも優れた溶接棒を提供することを目的とする。 - 特許庁 - To provide a heat treatment method, with which the heat treatment process can be executed in a machining line while avoiding the problems of the strain and machinability of a cast product, and to provide a spheroidal graphite cast iron-made parts improved in the hardness side without lowering the strength side so much.
鋳造品の歪みや被削性（加工性）の問題を回避しつつ、熱処理工程を機械加工ラインにおいて行なえる熱処理方法を提供するとともに、強度面をさほど低下させることなく硬度面が改善された球状黒鉛鋳鉄製部品を提供する。 - 特許庁 - Or the Cu plated layer 9 is formed on the nonthreaded metal contact part of either oneside of the pin 2 and box and the lubrication film of the inorganic high polymeric compound whose skeleton is the resin or M (metal)-O dispersed and mixed molybdenum disulfied and/or graphite is formed on the other nonthreaded metal contact part.
あるいは、ピンとボックスのいずれか一方のねじ無し金属接触部にＣｕめっき層を形成し、他方のねじ無し金属接触部に二硫化モリブデンおよび／または黒鉛を分散混合した樹脂またはＭ−Ｏを骨格とする無機高分子化合物の潤滑被膜を形成する。 - 特許庁 - The electroconductive composition contains graphite particles having an average particle diameter of 10-500nm which is obtained by heating and graphitizing at least one element selected from carbon black, a metal, boron and silicon or a compound containing the element(s) and a binder resin.
また、カーボンブラックと、金属、ホウ素及びケイ素から選ばれる少なくとも１種以上の元素の単体または該元素を含有する化合物とを加熱、黒鉛化して得られる平均粒子径１０￣５００ｎｍのグラファイト粒子とバインダー樹脂を含有してなることを特徴とする導電性組成物である。 - 特許庁 - Surfaces of a plurality of kinds of coated fuel particles 12A and 12B having different enrichment are coated with graphite matrix material to form overcoat layers 14A and 14B, and then, the fuel compacts 10 are manufactured out of coated fuel particles 12 each having an overcoat layer 14.
異なる濃縮度を有する複数の種類の被覆燃料粒子１２Ａ、１２Ｂの表面に黒鉛マトリックス材をコーティングしてオーバーコート層１４Ａ、１４Ｂを形成した後、オーバーコート層１４を有する被覆燃料粒子１２から燃料コンパクト１０を製造する。 - 特許庁 - To provide a hollow foamed molded object comprising a polyolefinic resin having heat insulating properties and lightweight properties, colored in black or gray by adding carbon black or graphite and suitably used as a duct for an automobile.
本発明は、断熱性、軽量性に優れ、カーボンブラックやグラファイトが添加されることにより黒色又は灰色に着色されたポリオレフィン系樹脂中空発泡成形体、更に、自動車用のダクトとして好適に使用可能な該中空発泡成形体を提供することを目的とする。 - 特許庁 - To provide a lithium secondary battery which has a large discharge capacity, excels in coulomb efficiency and cycle characteristics, and contains an electrode material for batteries with a small irreversible capacity, thereby solving a problem encountered when high crystallinity graphite is used and a problem encountered when an amorphous carbon layer is included.
高結晶性黒鉛を用いた場合の問題点及び非晶質炭素層を設けた場合の問題点を解消した、放電容量が大きく、クーロン効率、サイクル特性に優れ、不可逆容量の小さい電池用電極材料を含むリチウム二次電池を提供すること。 - 特許庁 - In addition, a manufacturing method of this sputtering target has a step in which a mixed powder of at least one of SbPt alloy powder and SnPt alloy powder, FePt alloy powder, Pt powder, and graphite powder or carbon black powder is hot-pressed in a vacuum or inert gas atmosphere.
また、このスパッタリングターゲットの製造方法は、ＳｂＰｔ合金粉およびＳｎＰｔ合金粉の少なくとも一方と、ＦｅＰｔ合金粉と、Ｐｔ粉と、グラファイト粉またはカーボンブラック粉と、の混合粉末を、真空または不活性ガス雰囲気中でホットプレスする工程を有している。 - 特許庁 - An inoculation stage of inoculating an inoculation agent, and an addition stage of adding an N-containing addition material are performed to control each component into the prescribed one, and, casting is next performed, so that the flake graphite cast iron having excellent machinability can be obtained.
Ｆｅ、Ｃ、Ｓｉ、Ｍｎ、Ｐ及びＳを含有した溶湯に対して、接種剤を接種する接種工程と、Ｎを含有した添加材を添加する添加工程とを行って各成分を所定量となるように調製し、次いで鋳造することにより、被削性に優れた片状黒鉛鋳鉄が得られる。 - 特許庁 - To provide an electrode material suppressing increase of the irreversible capacity by conservation in the atmosphere which is a problem when a non-graphite carbon material with high capacity is used as an electrode material for a nonaqueous solvent secondary battery without reducing the adhesive strength of the electrode layer formed.
非水溶媒二次電池用電極材料として、高容量の非黒鉛質炭素材料を用いる場合に、問題であった大気中での保存による不可逆容量の増大を、形成される電極層の接着強度の低下を招かずに、抑制した電極材料を与える。 - 特許庁 - The under-water sliding member includes a laminate of a carbon fiber cloth containing a phenol resin composition consisting of one or two or more types of 5-40 wt.% fillers selected from graphite, ethylene resin tetrafluoride, boron nitride and amorphous carbon, and a phenol resin for the rest.
グラファイト、四フッ化エチレン樹脂、窒化ホウ素および無定形炭素から選択される１種または２種以上の充填材５〜４０重量％と残部フェノール樹脂からなるフェノール樹脂組成物を含有した炭素繊維布の積層体からなる水中用摺動部材。 - 特許庁 - The yarn 1 for grand packing is formed by filling fibrous expanded graphite 4 having a cross section having an aspect ratio of 1-5 as value of the width w divided by the thickness t in a cylindrical material 3 composed by weaving or braiding Inconel wires 2 having 0.1mm diameter.
０．１ｍｍ径インコネル線２を編む又は組むことによって成る筒状部材３内に、幅ｗを厚みｔで除した値である縦横比が１〜５に設定される断面を有する繊維状の繊維状膨張黒鉛４を充填して、グランドパッキン用のヤーン１を形成する。 - 特許庁 - In the actuator having a moving member and a stator for supporting the moving member to reciprocate freely, sliding surface of the moving member is applied with a coating layer formed of an inorganic compound and sliding surface of the stator is applied with a coating layer containing graphite particles.
すなわち、可動子とその可動子を往復動自在に支持する固定子とを有するアクチュエータにおいて、前記可動子の摺動面には無機化合物から形成されたコーティング層を有し、前記固定子の摺動面にはグラファイト粒子を含有するコーティング層を有することを特徴とする。 - 特許庁 - This lithium secondary battery comprises a positive electrode using the lithium transition metal composite oxide as its positive-electrode active material and a carbon substance mixture made by mixing a boron-added non-spherulitic graphite material with an easily graphitizable carbon material as its negative-electrode active material.
リチウム二次電池を、リチウム遷移金属複合酸化物を正極活物質として用いた正極と、ホウ素を添加した非球晶黒鉛質材料と易黒鉛化性炭素材料とを混合した炭素物質混合物を負極活物質として用いた負極とを備えてなるように構成する。 - 特許庁 - The electromagnetic wave absorber is obtained with high efficiency and absorbency in the special high-frequency band of 1 GHz or more, the electromagnetic wave absorbency and a performance as an inexpensive construction material by combining the layers consisting mainly of graphite, microballoon and binder to form a multiple layer.
本発明では、主にグラファイトとマイクロバルーンとバインダとからなる層を組み合わせて複層化することにより、１ＧＨｚ以上の特定の高周波帯で効率が高く、電磁波吸収性を有し、安価な建築用材料としての性能も有した電磁波吸収体を得る。 - 特許庁 - The fluoride resin solid lubricant at a ratio of 5 to 100 pt.wt. or the graphite solid lubricant at the ratio of 10 to 100 pt.wt. and the silicone surface active agent at the ratio of 1 to 10 pt.wt. are contained to 100 pt.wt. in total of the epoxy resin and a curing agent.
また、エポキシ樹脂及び硬化剤の合計１００重量部に対し、該フッ素樹脂系固体潤滑剤を５〜１００重量部又は該グラファイト系固体潤滑剤を１０〜１００重量部、シリコーン系界面活性剤を１〜１０重量部の割合で含むことを特徴とする。 - 特許庁 - The quartz glass 7 is formed by hot forming through providing a quartz powder-coated film layer 8 on the inner wall surface of a container with which the quartz glass 7 contacts when formed by hot forming in a graphite container having a desired shape (comprising an upper plate 4, a cylindrical part 5, and a lower plate 6).
被加工物である石英ガラス7を所望の形状を有する黒鉛製の容器（上板部4、円筒部5、下板部6で構成）内で熱間成形する際、被加工物が接触する容器の内壁面に、石英粉末からなる被覆層8が設けて石英ガラスの熱間成形を行う。 - 特許庁 - The extruded foam comprises ≥20 wt.% of a polyolefin-based resin and 0.1-6 pts.wt. of a graphite fine powder having 1-100 μm average particle diameter based on 100 pts.wt. of the resin, and has 5-35 kg/m^3 density and 0.1-2 mm foam diameter.
ポリオレフィン系樹脂を２０重量％以上含有し、平均粒径が１〜１００μｍである黒鉛微粉末を、樹脂１００重量部に対して０．１〜６重量部含有する、密度が５〜３５ｋｇ／ｍ^３、気泡径が０．１〜２ｍｍであることを特徴とする押出発泡体。 - 特許庁 - The component adjusting material for steelmaking is the one, in which a base material of at least one kind of graphite waste, defective formed material and carburizing material is graded after crushing into the granular material or granulated after crushing into the powdery material and formed to grain of 1-8 mm diameter and further, the oxidizing resistance is given.
鉄鋼用成分調整材は、黒鉛の廃棄物、不良成形物及び加炭材の少なくとも１種の基材を、粒状物に破砕した後に整粒し、又は粉粒物に粉砕した後に造粒して、１〜８ｍｍの粒径に形成し、さらに耐酸化性を付与したものである。 - 特許庁 - To stably manufacture graphite powder having ≥350 mAh/g discharge capacity which is approximately the theoretical capacity, having the discharge efficiency as high as ≥90%, hardly decreasing the efficiency of charging and discharging even for discharge with a large current or for discharge at low temperature, and suitable for the negative pole material of a lithium ion secondary cell.
放電容量が350 mAh/g 以上と理論容量に近く、充放電効率が90％以上と高く、大電流放電や低温放電でも充放電効率が低下しにくい、リチウムイオン二次電池の負極材料に適した黒鉛粉末を安定して製造する。 - 特許庁 - In its manufacturing method, the graphite powder is mixed and kneaded with a resin solution prepared by dissolving the the novolac type phenol resin with the resin properties in an organic solvent; thereafter the organic solvent is removed by volatilizing it; and then, molding powder obtained by crushing the kneaded substance is filled in a molding die, and molded with heat and pressure.
その製造方法は、この樹脂性状のノボラック型フェノール樹脂を有機溶剤に溶解した樹脂溶液に黒鉛粉末を混合して混練した後、有機溶剤を揮散除去し、次いで混練物を粉砕して得られた成形粉を成形型に充填して熱圧成形する。 - 特許庁 - The graphite crucible for pulling up a silicon single crystal has a thermal expansion coefficient at 293-673 K of 3.0-4.0×10^-6/K, a thermal conductivity at 293 K of ≥120 W/(m×K), a coefficient of thermal shock resistance of ≥80 kW/m and an anisotropy ratio of thermal expansion coefficient of ≤1.1.
２９３〜６７３Ｋの熱膨張係数が３．０〜４．０×１０^−６／Ｋ、２９３Ｋでの熱伝導率が１２０Ｗ／（ｍ・Ｋ）以上、耐熱衝撃係数が８０ｋＷ／ｍ以上、熱膨張係数の異方比が１．１以下であるシリコン単結晶引上用黒鉛ルツボである。 - 特許庁 - This flat heat pipe comprises a casing formed of an upper plate and a bottom plate constituted by thin plates of a composite body of graphite and metal, at least one of the upper plate and the bottom plate being grooved, and a working fluid sealed in the grooves within the casing.
黒鉛と金属の複合体からなる薄板によって構成された上板および底板からなる筐体と、前記上板および底板の少なくとも１枚に溝が形成され、前記筐体内の溝に封入された作動流体とからなる平面型ヒートパイプである。 - 特許庁 - The electric double-layer capacitor polarized electrode is manufactured by using a carbonaceous material in which a raw material is for example activated with non-baked coke originating from coal or oil, in which the thermal coefficient of expansion measured by an artificial graphite electrode testing method is adjusted within 0.8-2 as the raw material.
人造黒鉛電極試験法によって測定される熱膨張係数を０．８〜２の範囲内に調整した石炭または石油由来の未か焼コークスを原料として、この原料を例えば賦活処理した炭素材を用いて電気二重層キャパシタ分極性電極を製造する。 - 特許庁 - To provide a manufacturing method of a seamless steel tube by a mandrel mill tube-making line by which the generation of carburized layer on the inside surface is prevented even when a mandrel bar to which graphite is stuck is used and seamless alloy steel tube excellent in corrosion resistance which is manufactured by this method.
黒鉛が付着したマンドレルバーを用いる場合でも、内面に浸炭層が発生するのを抑制することが可能なマンドレルミル製管ラインによる継目無鋼管の製造方法とこの方法によって製造された耐食性に優れた継目無合金鋼鋼管を提供する。 - 特許庁 - Above problem can be solved by a monolithic refractory for a blast furnace main trough metal line in which the monolithic refractory is composed of Al_2O_3-MgO-SiC-a carbonaceous material, and into which pre-molded granules that contain Al_2O_3, MgO and graphite are added as aggregate.
上記課題は、Ａｌ_2 Ｏ_3 −ＭｇＯ−ＳｉＣ−炭素質の不定形耐火物であって、予め成型された、Ａｌ_2 Ｏ_3 とＭｇＯと黒鉛とを含有する造粒体が、骨材として添加されている高炉主樋メタルライン用不定形耐火物によって解決することができる。 - 特許庁 - To provide a high quality SiC-covered graphite material which is excellent in resistance to heat, acid corrosion, and oxidation, has a good electric conductivity, for example, has a resistivity of 10^-3-10^-5 Ωm, and can be used in a heater or the like of the device for producing a semiconductor vulnerable to contamination.
高純度で耐熱性、耐酸食性、耐酸化性に優れ、特に電導性が良好で、例えば１０^−３〜１０^−５Ωｍの固有抵抗を有し、汚染を嫌う半導体製造用装置のヒータなどとして好適なＣＶＤ−ＳｉＣ被覆黒鉛材及び製造方法を提供する。 - 特許庁 - The surface of the sand core 7 is coated with a three-layered structure consisting of a primer coating agent containing TiO2 applied on the lowermost layer, a ceramic coating agent essentially consisting of SiO2 and MgO applied as a second layer and a flaky graphite coating agent applied as a third layer.
砂中子７の表面は、最下層に塗布されるＴｉＯ_2を含有する下塗りコート剤、第２層として塗布されるＳｉＯ_2とＭｇＯを主成分とするセラミック系コート剤、第３層として塗布される鱗片状黒鉛コート剤とからなる３層構造で被覆されている。 - 特許庁 - The method for manufacturing film-like graphite comprises a step of heat-treating the polyimide film at 2,400-2,800°C, which has ≤2.5×10^-5 cm/cm/°C average coefficient of linear expansion in the facial direction thereof at 100-200°C and 100-200 μm thickness.
１００〜２００℃の範囲におけるフィルム面方向の平均線膨張係数が２．５×１０−５ｃｍ／ｃｍ／℃以下であり、厚さが１００〜２００μｍのポリイミドフィルムを２４００℃以上２８００℃以下の温度で熱処理することを特徴とするフィルム状グラファイトの製造方法によって解決しうる。 - 特許庁 - The flame resistant aromatic polycarbonate resin composition comprises (A) a 100 pts.wt. aromatic polycarbonate resin (component A), (B) 5-100 pts.wt. carbon fiber (component B), (C) 5-100 pts.wt. graphite (component C), and (D) a 0.001-1 pt.wt. an organic metal salt compound (component D).
（Ａ）芳香族ポリカーボネート樹脂(Ａ成分)１００重量部、（Ｂ）炭素繊維（Ｂ成分）５〜１００重量部、（Ｃ）黒鉛（Ｃ成分）５〜１００重量部、および（Ｄ）有機金属塩化合物（Ｄ成分）０．００１〜１重量部からなる難燃性芳香族ポリカーボネート樹脂組成物。 - 特許庁 - Graphite particles, Cu powder, carbon fiber, ZnO whisker or the like is applied as the filler, an average particle size of these Gr particles and Cu particles is 10 μm or less, and the carbon fiber and ZnO whisker has a fiber diameter of 5 μm or less, and an aspect ratio (fiber length/fiber diameter) of 2 or more.
充填材として、グラファイト粒子、Ｃｕ粉、カーボンファイバー、ＺｎＯウィスカー等を採用すると共に、それらＧｒ粒子及びＣｕ粉の平均粒径を１０μｍ以下とし、カーボンファイバー及びＺｎＯウィスカーを、繊維径５μｍ以下且つアスペクト比（繊維長／繊維径）２以上とする。 - 特許庁 - In a method for producing graphite fiber comprising graphitizing a fiber 2 to be graphitized in which silicon compound is contained by continuously traveling the fiber in a muffle furnace kept in inert atmosphere having 2,200-3,000 temperature, the distance between a muffle side wall 4 and the fiber 2 to be graphitized is kept within the range of 3-25 mm.
温度２２００〜３０００℃の不活性雰囲気としたマッフル内に、ケイ素化合物が含まれる被黒鉛繊維を連続的に走行させて黒鉛化する黒鉛繊維の製造方法であって、該マッフル側壁と被黒鉛繊維との距離を３〜２５ｍｍの範囲とする黒鉛繊維の製造方法。 - 特許庁 - After a powdery graphite nano-fiber is subjected to a vacuum annealing treatment at an annealing temperature of about 1,000°C for about 1 hour, it is dipped in pure water and then it is irradiated with 420 KHz ultrasonic wave for 3 hours by use of an ultrasonic generator under atmospheric temperature and pressure conditions of about 0 to 30°C and 1 atm..
パウダー状グラファイトナノファイバを、約１０００℃のアニール温度で約１時間真空アニール処理を行った後、純水に浸漬した状態にして、おおむね０〜３０℃及び１気圧の常温常圧条件下で、超音波発生装置により４２０ＫＨｚの超音波を３時間照射する。 - 特許庁 - The characteristic of this lubricant is to have a lubricant A comprising ≤50 wt.% graphite powder, an organic and/or inorganic water-soluble binder and water and boron carbide powder in an amount of ≤20 wt.% based on the lubricant A and to form dried film after applying it to a sliding part.
黒鉛粉末５０重量％以下、有機系およびまたは無機系の水溶性バインダおよび他を水とする潤滑剤Ａと、この潤滑剤Ａに対して２０重量％以下の炭化ホウ素粉末とを有し、摺動部への塗布後に乾燥被膜を形成することを特徴とする。 - 特許庁 - To prevent the delamination and cracking of a mixture layer while keeping high capacity without increasing a quantity of binding agent which inhibits the charging and discharging reaction, in a case when a rolled copper foil capable of providing high capacity and the lumped graphite powder easily causing the delamination of the mixture layer layer, are used in the negative electrode active material.
高容量化が期待できるが圧延銅箔と合剤層の剥離が生じやすい塊状黒鉛粉末を負極活物質に用いる場合に、充放電反応を阻害するような結着剤を増加させずに、高容量を維持したまま合剤層の剥離やクラックの発生を防止する。 - 特許庁 - After the machining stage, the raceway grooves of the outer ring are subjected to induction hardening and tempering treatment, so that, in the surface layer parts thereof, a hardness is controlled to ≥60 HRC, the content of retained austenite is controlled to ≥10 vol.%, and the grain size of graphite present therein is controlled to ≤1.0 μm.
切削工程の後に、外輪軌道溝に対して高周波焼入れと焼戻しを施すことにより、外輪軌道溝の表層部分を、硬さＨＲＣ６０以上、残留オーステナイト量１０体積％以上、存在する黒鉛の粒子径１．０μｍ以下にする。 - 特許庁 - The conductive monolithic refractory for stamping work of the hearth of the DC electric furnace contains a refractory raw material composition consisting of 3-20 mass% scaly graphite, 0.5-8 mass% magnesia fine powder and the balance being a fired magnesia-carbonaceous raw material and a liquid organic binder.
りん状黒鉛粉３〜２０質量％、マグネシア微粉０．５〜８質量％、残部を焼成されたマグネシア−カーボン質原料とする耐火性原料組成と、液状有機質結合剤とを含む、直流電気炉炉床スタンプ施工用導電性不定形耐火物である。 - 特許庁 - The negative electrode material for a lithium ion secondary battery that adhere to a high-molecular compound and a metal oxide have a carboxyl group onto the surface of a negative electrode active substance chosen from among a carbon material, a graphite material, and a metallic material which can store or discharge lithium ions, and the negative electrode and the secondary battery.
リチウムイオンを吸蔵、放出可能な炭素材料、黒鉛材料および金属材料から選ばれる負極活物質の表面に、カルボキシル基を有する高分子化合物および金属酸化物が付着してなるリチウムイオン二次電池用負極材料、負極および二次電池。 - 特許庁 - The battery 1 is constituted of a current collector 14 and a negative electrode 10 which consists of active material layers 15 and 16 having as a main material a granule body adhering a plurality of natural graphite and in which the bulk density of the granule body is 0.20 g/cm^3 or more and 0.70 g/cm^3 or less.
電池１を、集電体１４と、複数の天然黒鉛の接着による造粒体を主たる材料とする活物質層１５及び１６とからなり、前記造粒体のかさ密度が、０．２０ｇ／ｃｍ^３以上０．７０ｇ／ｃｍ^３以下とされた負極１０によって構成する。 - 特許庁 - The invention also concerns composition of an iron based powder, graphite and a solid lubricant particle having a vaporising temperature less than the sintering temperature, preferably less than about 800°C and a maximum particle size less than about 0.3 of the maximum size of the iron based powder as measured by laser diffraction measurement.
本発明は、鉄基粉末、黒鉛、および焼結温度より低い（好ましくは約８００℃未満）蒸発温度とレーザー回折測定法により測定した鉄基粉末の最大径の約０．３倍より小さい最大粒子径とを有する固体粒子潤滑剤の組成にも関係がある。 - 特許庁 - In an organic solvent where carbon nanotubes are dispersed, a voltage is applied to the fuel cell separator consisting of resin and graphite as an anode and the carbon nanotubes are deposited to the surface of the fuel cell separator, and then the film forming of the carbon nanotube is performed on the surface of the fuel cell separator.
カーボンナノチューブの分散した有機溶媒中で、樹脂と黒鉛からなる燃料電池セパレータを陽極として電圧を印加し、燃料電池セパレータの表面上にカーボンナノチューブを付着させることで、燃料電池セパレータの表面上にカーボンナノチューブを製膜する。 - 特許庁 - The water based antistatic coating composition comprises an aqueous epoxy resin or an epoxy emulsion resin and conductive fine particles, wherein the conductive fine particles are composed of a conductive pigment wherein zinc, titanium, tin or its oxide is coated with or added with aluminum, iron, silver, nickel, phosphorus or antimony, or are of graphite.
水性エポキシ樹脂又はエポキシエマルション樹脂及び導電性微粒子を含有し、導電性微粒子が亜鉛、チタン、スズ又はそれらの酸化物にアルミニウム、鉄、銀、ニッケル、リンもしくはアンチモンを被覆又は付加した導電顔料或いはグラファイトである水系帯電防止塗料。 - 特許庁 - A resin composition containing a non-carbonaceous thermoplastic resin (a polyphenylene sulfide resin or the like) and an electrically conductive agent (graphite particles, electrically conductive carbon black or the like) is molded into a sheet and the obtained sheet is subjected to stamping molding by using a grooved die to obtain the objective separator.
非炭素質熱可塑性樹脂（ポリフェニレンスルフィド系樹脂など）と導電剤（黒鉛粒子、導電性カーボンブラックなど）とを含む樹脂組成物をシート成形し、得られたシートを溝付き金型を用いてスタンピング成形することにより、燃料電池用セパレータを製造する。 - 特許庁
- 特許庁
- Copyright © Japan Patent office. All Rights Reserved.