＜前へ 1 2 .... 422 423 424 425 426 427 428 429 430 .... 453 454 次へ＞- This polyester film for optical uses having a coated layer having an easily bondable property with the curable resin on at least one of the film surfaces is characterized by having ≥0.7 density (number/mm^2) of projections having ≥5th interference patterns observed by a double beam interferometry, on the coated layer surface.
硬化性樹脂に対して易接着性を有する塗布層を少なくとも一方のフィルム面に有し、当該塗布層表面における二光束干渉法で観察される５次以上の干渉縞を有する突起の密度（個／ｍｍ^２）が０．７以上であることを特徴とする光学用ポリエステルフィルム。 - 特許庁 - The labeled polystyrene foam vessel is constituted of a polystyrene foam vessel with its outer circumferential surface of the body thereof being provided with a heat shrinkage label whose base material is made of heat shrinking polyester film on which a printing layer is formed and whose heat-shrinkage rate in the circumferential direction of the vessel at 80°C is 30% or above.
ラベル付き発泡ポリスチレン製容器は、発泡ポリスチレン製容器の胴部外周面に、熱収縮性ポリエステルフィルムからなるラベル基材に印刷層が形成され８０℃における容器周方向の熱収縮率が３０％以上である熱収縮性ラベルが装着されることによりなる。 - 特許庁 - In the magnetic recording medium wherein at least one magnetic layer formed by dispersing ferromagnetic powder in a binder is provided on a substrate, the binder formed by curing a hyper branch polyester in which a radiation curing functional group is introduced by irradiation with a radiation is contained in the magnetic layer.
支持体上に強磁性粉末を結合剤中に分散した磁性層を少なくとも一層設けた磁気記録媒体であって、該磁性層に、放射線硬化性官能基が導入されたハイパーブランチポリエステルを放射線照射により硬化した結合剤を含むことを特徴とする磁気記録媒体。 - 特許庁 - This thermosetting polyester film and the other objective transparent elastomer are each obtained by curing a resin composition comprising (A) a vinyl ester resin, (B) vinyl monomer(s) essentially comprising at least one kind selected from the group consisting of alkyl (meth)acrylates, alkoxyalkyl (meth)acrylates and alkoxypolyalkylene glycol (meth)acrylates, and (C) a polymerization initiator.
（Ａ）ビニルエステル樹脂、（Ｂ）アルキル（メタ）アクリレート、アルコキシアルキル（メタ）アクリレートおよびアルコキシポリアルキレングリコール（メタ）アクリレートからなる群から選択された少なくとも１種を必須成分として含有するビニルモノマーおよび（Ｃ）重合開始剤を含有してなる樹脂組成物を硬化せしめてなる熱硬化性ポリエステルフィルムおよび透明エラストマー。 - 特許庁 - To obtain a polyester resin composition capable of decreasing oligomers generated in melt extrusion and so capable of decreasing cleaning frequency for the oligomers and increasing productivity and capable of obtaining products excellent in surface properties such as having no defect like streak and flaw, and to provide a method for producing the resin composition.
溶融押出時に発生するオリゴマーを低減し、これにより、オリゴマー汚れによる清掃回数を低減でき生産性が向上できるとともに、且つ製品とした場合スジや傷といった欠点のない表面特性に優れた製品を得ることができるポリエステル樹脂組成物、およびその製造方法を提供する。 - 特許庁 - The biaxially oriented polyester film has at least a base layer B containing 0.25 wt.% or more and less than 1.0 wt.% of SiO_2 particles and 0.25 wt% or more and less than 1.0 wt% of TiO_2 particles.
少なくともベース層Ｂを有する二軸延伸ポリエステルフィルムであって、ベース層Ｂが、０．２５重量％以上１．０重量％未満の二酸化ケイ素粒子および０．２５重量％以上１．０重量％未満の二酸化チタン粒子を含有する二軸延伸ポリエステルフィルム、及び当該二軸延伸ポリエステルフィルムの製造方法。 - 特許庁 - The spun yarn comprises ≥20 wt% core-sheath type conjugate short fiber in which the sheath component is a polyamide and the core component is a polyester and the fineness is 0.5-7.0 dtex and the strength is 2.0 to 7.0 cN/dtex and the spun yarn is substantially twist-free.
鞘成分がポリアミド、芯成分がポリエステルからなるとともに、繊度が０．５〜７．０ｄｔｅｘの範囲にあり、強度が２．０ｃＮ／ｄｔｅｘ〜７．０ｃＮ／ｄｔｅｘである芯鞘型複合短繊維を２０重量％以上含む紡績糸であって、かつ実質的に無撚りであることを特徴とする紡績糸。 - 特許庁 - To provide an undercoat material having superior adhesiveness to a polyester support and having satisfactory adhesiveness also as the undercoat layer of a photographic sensitive material, and to particularly provide an image recording material improved in scratch resistance of an undercoat layer in an un-heat-treated state and in density unevenness of emulsion application.
ポリエステル支持体に対して優れた接着性を有し、写真感光材料の下引層としても十分な接着性を有する下引素材を提供することにあり、更に詳しくは、熱処理していない状態の下引きの耐傷性、乳剤塗布の濃度ムラが改善された画像記録材料を提供する。 - 特許庁 - In the false twist yarn being the multifilament composed of the polyester-based core-sheath conjugate fiber containing the titanium oxide fine particle in the core part, the fineness of the multifilament is uniform in the length direction and the crosssectional shapes of the single filaments of the multifilament cross section are different, respectively.
芯部に酸化チタン微粒子を含有したポリエステル系芯鞘複合糸からなるマルチフィラメントである仮撚加工糸において、該マルチフィラメントの繊度が長手方向に均一であり、かつマルチフィラメント横断面の単糸断面形状が各々異なることを特徴とするポリエステル系芯鞘複合仮撚加工糸。 - 特許庁 - The polyester resin is controlled so that the content ratio of a stable isotope of at least one element of carbon, hydrogen and oxygen that are constituting elements is differed from a natural existing ratio thereof, and shows a vibration spectrum differed from that of a resin of the same kind with the content ratio of the isotope being the natural existing ratio.
構成元素である炭素、水素及び酸素のうちの少なくとも一種の元素の安定同位体の含有比率が天然存在比と異なるように制御され、前記同位体の含有比率が天然存在比である同種の樹脂の振動スペクトルと異なる振動スペクトルを示すポリエステル樹脂。 - 特許庁 - The thermally insulating lid is formed by mounting a thermally insulating material 13 which is formed by subjecting the preexpanded particles of a thermoplastic polyester resin to in-mold expansion molding and is ≤1 mm per 100 mm in thermal shrinkage when heated for 24 hours at 120°C between an upper lid body 11 and a lower lid body 12.
断熱蓋１は、上蓋体１１と下蓋体１２との間に、熱可塑性ポリエステル系樹脂の予備発泡粒子を型内発泡成形して形成された、１２０℃で２４時間加熱した際の熱収縮が、１００ｍｍあたり１ｍｍ以下である発泡成形体からなる断熱材１３を装着した。 - 特許庁 - This stretchable knitted fabric is characterized by including a side-by-side conjugated filament obtained by two kinds of polyester polymers along the longitudinal direction of the fiber in an amount of ≥10% based on the total weight of the composing yarn and having ≥55% average elongation in the length and width direction and ≥60% average recovering ratio of elongation therein.
２種類のポリエステル重合体が繊維長さ方向に沿ってサイドバイサイド型に貼り合わされた複合繊維フィラメントを構成糸の全体重量の１０％以上含み、タテ・ヨコ方向の平均伸長率が５５％以上、平均伸長回復率が６０％以上であることを特徴とするストレッチ編地とする。 - 特許庁 - The apparatus for manufacturing resin coated metallic seamless can bodies is characterized in that ironing is performed while keeping the surface temperature of the punch 10 at 35-100°C during forming and at proper temperature (A°C) within the range not higher than glass transition temperature (Tg) of the thermoplastic polyester resin by circulating cooling fluid in the punch 10 at that time.
その際パンチ内１０に冷却用液体を循環させて、成形時のパンチ１０の表面温度を３５〜１００℃で且つ前記熱可塑性ポリエステル樹脂のガラス転移点（Ｔｇ）以下の範囲内の適宜温度（Ａ℃）に保って、しごき加工を行うことを特徴とする樹脂被覆金属シームレス缶体の製造装置。 - 特許庁 - This method comprises a reacting step among a saturated polyester (A), a polyhydric alcohol component (B1) and at least one polybasic acid component (C1) selected from the group consisting of a saturated polybasic acid, an unsaturated polybasic acid and their anhydrides and a next step of adding an unsaturated polybasic acid or its anhydride (C2) to react them.
飽和ポリステル（Ａ）と、多価アルコール成分（Ｂ１）と、飽和多塩基酸、不飽和多塩基酸およびこれらの酸無水物よりなる群から選択される１種以上の多塩基酸成分（Ｃ１）とを反応させ、次いで、不飽和多塩基酸またはその無水物（Ｃ２）を添加して反応させる不飽和ポリエステルの製造方法である。 - 特許庁 - In the heat-shrinkable polyester film, the concealing degree of the whole of the film is not more than 0.2, a layer containing cavities is provided at least on the single surface of the film and the center line average roughness of the surface of the layer containing the cavities is not less than 0.1 μm.
熱収縮性ポリエステル系フィルムであって、フィルム全体の隠蔽度がＯ．２以下であり、少なくとも片面に空洞を含有する層を設けてあり、空洞を含有する層の表面の中心線平均粗さが０．１μm以上であることを特徴とする積層熱収縮性ポリエステル系フィルム。 - 特許庁 - In addition, it is desirable that the constituent fiber is a filament comprising a polyester long fiber, is made up of a fine size fiber whose single fiber size is less than 0.6 dtex and a thick size fiber whose single fiber size is 0.6 to 2.0 dtex, and at least one face of the napkin is mainly formed of the thick size fiber.
さらに構成繊維が、ポリエステル長繊維からなる糸条であり、単繊維繊度が０．６ｄｔｅｘ未満の細繊度繊維と、単繊維繊度が０．６〜２．０ｄｔｅｘの太繊度繊維とからなり、少なくとも一方の布帛面が主として太繊度繊維で形成されていることが好ましい。 - 特許庁 - To provide a method for producing a polyester film suitable for a backside protection film of a solar cell with high productivity, which prevents the deterioration of mechanical properties even when being used in an environment of high temperature and humidity for a long period of time, and simultaneously has uniform and low thermal shrinkage in a lengthwise direction over in a width direction of the film.
高温・多湿な環境下での長時間使用における機械的性質の低下が抑制され、同時にフィルム幅方向に渡って均一な低い縦方向熱収縮率を有する太陽電池裏面保護膜に好適なポリエステルフィルムを生産性高く製造する方法を提供する。 - 特許庁 - The deep drawing film comprises at least an amorphous polyester resin layer, a high density polyethylene resin layer with a density of 0.940-0.965 being an intermediate layer, and an easy peel layer being the innermost layer having cohesive failure properties, wherein the internal haze of the film is 2.5% or below and the loop stiffness test value of the film is within a specific range.
非晶性ポリエステル樹脂層と、中間層として密度０．９４０以上、０．９６５以下の高密度ポリエチレン樹脂層、及び最内層として凝集破壊性を有するイージーピール層を少なくとも有し、フィルム内部ヘーズ値が２．５％以下であり、ループスティフネス試験値が特定範囲である深絞り成形用フィルム。 - 特許庁 - This polyester monofilament for the screen gauze has a sheath core type conjugate cross sectional surface wherein, the core component of a polyethylene naphthalate is obtained by copolymerizing 1-5 mol% isophthalic acid component based on the naphthalenedicarboxylic acid, and the sheath component is a polyethylene terephthalate, and also has (80/20) to (60/40) weight ratio of the core component/the sheath component.
芯鞘型複合横断面を有し、芯成分がナフタレンジカルボン酸成分に対してイソフタル酸成分を１〜５ｍｏｌ％共重合したポリエチレンナフタレート、鞘成分がポリエチレンテレフタレートとし、芯成分／鞘成分の重量比率が８０／２０〜６０／４０であるスクリーン紗用ポリエステルモノフィラメントとする。 - 特許庁 - The film has 1 nm or more and less than 600 nm retardation value, is composed of a polylactic acid based resin as the aliphatic polyester based resin, has 0.1% or more and 1,000% or less stretch ratio, has 0 or more and less than 20 (×10^-12/Pa) photoelastic coefficient, and is molded with extrusion molding or cast molding.
レターデーションが１ｎｍ以上６００ｎｍ未満である、脂肪族ポリエステル系樹脂が、ポリ乳酸系樹脂、延伸倍率が、０．１％以上１、０００％以下である、光弾性係数が、０以上２０（×１０^−１２／Ｐａ）未満である押し出し成形又は、キャスト成形で成形されたフィルムである。 - 特許庁 - The fabric containing the polyester fibers processed by polymerizing a hydrophilic compound on the surfaces of the fibers and having the moisture-absorbing exothermic property/the moisture-releasing cooling property, is characterized in that a temperature rise due to the moisture-absorbing heat generation is ≥0.5°C and that the temperature drop due to the moisture-releasing cooling is ≥0.5°C.
親水性化合物を繊維表面で重合させることにより加工されたポリエステル繊維を含む布帛であって、加工前の繊維を含む布帛に対比して、吸湿発熱による温度上昇が０．５℃以上であり、放湿冷却による温度降下が０．５℃以上である、吸湿発熱性／放湿冷却性布帛。 - 特許庁 - To provide a laminated film which is excellent in the highly adhesive properties of a coating layer to the active energy beam-cured resin layer as a finishing agent, and also is excellent in the adhesive properties with the finishing agent with respect to the laminated film provided with a highly adhesive coating layer and an active energy beam-cured resin layer in succession on the surface of a polyester film.
ポリエステルフィルムの表面に易接着性塗布層と活性エネルギー線硬化樹脂層とを順次に備えてなる積層フィルムであって、上塗り剤としての活性エネルギー線硬化樹脂層に対する塗布層の易接着性が優れ、上塗り剤との密着性が優れた積層フィルムを提供する。 - 特許庁 - To solve problems that the surface quality of a knitted or a woven fabric comprising a spun yarn of polyester staple fibers is deteriorated by occurrence of pilling when the fabric is worn and to obtain a core-sheath composite spun yarn and the knitted or the woven fabric maintaining strength properties and having excellent pill resistance and bulkiness and further stiffness, body, feeling, lightweight feeling and heat retaining properties in combination.
ポリエステル短繊維の紡績糸からなる編織物はピリング着用時ピリング発生による表面品位劣化問題があり、強度物性を維持し、かつ抗ピル性、嵩高性にすぐれ、さらに張り腰、風合い、軽量感、保温性を併せ持つ芯鞘型複合紡績糸および編織物を提供すること。 - 特許庁 - The polycarbonate resin composition comprises (A) 100 pts.mass of a resin blend comprising (a-1) 60-97 mass% of an aromatic polycarbonate resin and (a-2) 40-3 mass% of a fatty acid polyester, (B) 4-50 pts.mass of a nonmetallic inorganic filler and (C) 0.01-1 pt.mass of a phosphoric acid-based compound.
（Ａ）（ａ−１）芳香族ポリカーボネート樹脂６０〜９７質量％及び（ａ−２）脂肪酸ポリエステル４０〜３質量％からなる樹脂混合物と、その１００質量部当り、（Ｂ）非金属系無機充填剤４〜５０質量部及び（Ｃ）リン酸系化合物０．０１〜１質量部を含むポリカーボネート樹脂組成物である。 - 特許庁 - The side-by-side type conjugate polyester fiber obtained by conjugating components having different viscosities in which the high viscosity component comprises a polytrimethylene terephthalate into a side-by-side form, has a plateau strength of 1.0 cN/dtex or more and 1.5 cN/dtex or less and a dispersion of yarn tensions after being rubbed on a mirror finished surface of 30% or less.
高粘度成分がポリトリメチレンテレフタレートからなる粘度の異なる成分がサイドバイサイド型に複合された複合ポリエステル繊維であって、繊維のプラトー強度が１．０ｃＮ／ｄｔｅｘ以上１．５ｃＮ／ｄｔｅｘ以下であり、かつ鏡面擦過後の糸張力バラツキが３０％以内であることを特徴とするサイドバイサイド型複合ポリエステル繊維。 - 特許庁 - This sPS cover film is useful as an overlay film for a sign 1 and other outdoor applications, and is equal to an acrylic film added with an ultraviolet absorbing agent in ultraviolet light shielding or resistance, and thus can provide an alternative choice which can replace an acrylic resin, a polyester and a fluoro-polymer overlay film and is competitive to a product from such a resin in the aspect of production cost.
本発明の sPSカバーフィルムは、標識（１）及び他の屋外用途のオーバーレイフィルムとして有用であり、紫外線遮断または耐性において紫外線吸収体を添加したアクリルフィルムに匹敵し、アクリル、ポリエステル、及びフルオロポリマオーバーレイフィルムに取って代わるコスト面で負けない選択肢を提供する。 - 特許庁 - A mold releasable film is a polyester film having a lamination structure of 2 or more layers wherein a particle is contained in at least one outermost surface layer, a ratio t/d of the thickness t of outermost surface layer to the average diameter d of the particle being 0.2≤t/d≤5, and the mold reasable film has surface resistance of less than 1×1010 Ω.
少なくとも２層以上の積層構造からなるポリエステルフィルムであって、少なくとも片面の最表層に粒子を含有し、該最表層の厚さｔと該粒子の平均粒径ｄの関係が ０．２≦ｔ／ｄ≦５ の範囲にあり、表面抵抗率が１×１０^10Ω未満であることを特徴とする離型フィルム。 - 特許庁 - A manufacturing method for biaxially oriented polyester film is characterized in that after an aqueous resin or a water dispersing resin is applied on one side or on both sides of a non-oriented film or a longitudinally oriented film, the film is laterally oriented in a stenter oven wherein the amount of dust with a particle diameter of 0.3 μm or less is 5,000/ft^3 or less.
未延伸フィルムまたは、長手方向延伸後のフィルムの、 片面又は両面に、水系樹脂または水分散系樹脂を塗布した後、 粒径０．３μｍ以下の塵埃が５０００個／ｆｔ^３以下のステンターオーブン内で横延伸する事を特徴とする、二軸延伸ポリエステルフィルムの製造方法。 - 特許庁 - This biaxially oriented polyester film having many fine protrusions formed on the ground surface portions, characterized in that the fine protrusions contain the protrusions having heights of 3 to 5 nm in the total protrusion number of 3,000,000 to 100,000,000 protrusions/mm2 and in that the average size of grains is 10 to 100 nm, when the height threshold value of the protrusions is 3 nm.
表面の地肌部分に微細な突起が多数形成された二軸配向ポリエステルフィルムであって、該微細突起は、突起高さが３〜５ｎｍである突起の総突起個数が３００万〜１億個／ｍｍ^2であり、かつ、突起の高さのしきい値が３ｎｍの時のグレインサイズの平均値が１０〜１００ｎｍである。 - 特許庁 - A powder mixture for a sublimation type dye thermal transfer receptor sheet, consisting of 100 pts.wt. of powdered coating composition containing a coloring agent and a saturated polyester resin having acid value of 1.0-20 mgKOH/g and the glass transition temperature of 50-70°C blended with the range of 0.5-15 pts.wt. of hydrophobic inorganic fine grain, is provided.
着色剤と、酸価1.０〜２０ｍｇＫＯＨ／ｇ、ガラス転移温度５０〜７０℃の飽和ポリエステル樹脂とを含む粉体塗料組成物１００重量部に対して、疎水性無機微粒子を0.５〜１５重量部の範囲で配合してなる昇華型染料熱転写受像シート用粉体混合物を提供する。 - 特許庁 - The carboxyl functional polyester resin is obtained by reacting the following components under certain reaction conditions: (a) for example, 1,4-cyclohexane dicarboxylic acid, (b) a compound having one hydroxyl group and one tertiary aliphatic carboxyl group, (c) according to demand, a diol compound, (d) according to need, a dihydroxymonocarboxylic acid compound, and (e) optionally, a trihydroxyalkane or tetrahydroxyalkane.
ａ）例えば、1,4-シクロヘキサンジカルボン酸； ｂ）１つのヒドロキシル基及び１つの３級脂肪族カルボキシル基を含有する化合物； ｃ）場合により、ジオール化合物； ｄ）場合により、ジヒドロキシモノカルボン酸化合物；および ｅ）場合により、トリヒドロキシアルカン又はテトラヒドロキシアルカンを、特定の反応条件下に反応させる。 - 特許庁 - This coating agent comprises, as a hardening component, a carboxyl-containing urethane(meth)acrylate provided with a carboxyl concentration corresponding to an acid value of ≥10 and obtained by reacting (A) a lactone-based polyester polyol produced by subjecting a lactone to ring-opening addition polymerization using an initiator of dihydroxy carboxylic acid, (B) a polyisocyanate, and (C) a hydroxyl-containing urethane(meth)acrylate.
ジヒドロキシカルボン酸を開始剤として、ラクトン類を開環付加重合させて得られるラクトン系ポリエステルポリオール（Ａ）、ポリイソシアネート（Ｂ）、及びヒドロキシ基含有（メタ）アクリレート（Ｃ）を反応させて得られる、カルボキシル基濃度が酸価１０以上であるカルボキシル基含有ウレタン（メタ）アクリレートを硬化成分として含有するフィルムコート用組成物。 - 特許庁 - To provide a polyester resin composition for light reflector base that generates little gas even when molded into a light reflector base or used as a light reflector, and is excellent in adhesion to a metallic thin layer deposited on a surface of the light reflector base, and also maintains a highly bright feeling even when exposed to a high-temperature atmosphere.
光反射体基体の成形時や光反射体とした際に於いても、発生ガスが少なく、光反射体基体表面に設けた金属薄膜層との密着性に優れ、さらに高温雰囲気に曝した場合にも高輝度感を保持する、光反射体基体用ポリエステル樹脂組成物を提供する。 - 特許庁 - In the polyester film for a molding transfer foil, the surface on the side of at least a transfer surface has an elongation at break at 120°C of at least 400%, a stress at 120°C at 400% elongation of 15 MPa or below, and a thermal shrinkage rate when heated at 100°C for 30 min of -0.5 to 0.5%.
少なくとも転写面側の表面において、１２０℃における破断伸度が４００％以上、かつ１２０℃における４００％伸長時の応力が１５ＭＰａ以下、 １００℃において３０分加熱した場合の熱収縮率が−０．５〜０．５％、 であることを特徴とする、成型転写箔用ポリエステルフィルム。 - 特許庁 - This electroconductive resin composition is constituted with (A) 100 pts.wt. of a liquid crystal polyester resin forming an anisotropic molten phase, (B) 0.01-30 pts.wt. of a carbodiimide, (C) 50-3,000 pts.wt. of electroconductive carbonaceous powder, (D) 0-10,000 pts.wt. of a filler.
本発明が採用した導電性樹脂組成物の構成は、（Ａ）異方性溶融相を形成する液晶ポリエステル樹脂 １００重量部、（Ｂ）カルボジイミド化合物 ０．０１〜３０重量部、（Ｃ）導電性炭素質粉末 ５０〜３０００重量部、（Ｄ）充填材 ０〜１００００重量部よりなることを特徴とする。 - 特許庁 - To provide a fine foam-containing film imparting sharp printing, improved in surface appearance, surface release strength, glossiness, whiteness or the like and suitable for a label, a poster, recording paper, a packaging material, a medical sticking plaster substrate, an artificial leather substrate or the like, and a fine foam-containing polyester film having a pressure-sensitive adhesive layer.
印字や印刷が鮮明であり、表面外観、表面剥離強度や光沢性、白色性などが改良され、ラベル、ポスター、記録紙、包装材料、薬用貼り付剤基材、人工皮革基材などに適した微細気泡含有フィルムおよび粘着層を有する微細気泡含有ポリエステルフィルムを提供する。 - 特許庁 - The liquid composition is prepared by mixing: the liquid crystal polyester; the solvent; and a surface treated silica containing silica having a volume average particle diameter of from 0.1 to 1.5 μm, the surface of which is treated with a silane compound having at least one kind of group selected from the group consisting of a methacryloyloxy group, a phenyl group, a vinyl group and an epoxy group.
液晶ポリエステルと、溶媒と、体積平均粒径０．１〜１．５μｍのシリカがメタクリロイルオキシ基、フェニル基、ビニル基及びエポキシ基からなる群から選ばれる少なくとも１種の基を有するシラン化合物で表面処理されてなる表面処理シリカとを混合して、液状組成物とする。 - 特許庁 - The film is prepared by the tubular blown film extrusion of a resin composition comprising 50-90 wt% of a polyester resin (A), 5-50 wt% of an ethylenic polymer (B) having a density of 0.850-0.910 g/cm^3, and 1-20 wt% of a carboxylic acid-modified or epoxy-modified ethylenic copolymer (C).
ポリエステル樹脂（Ａ）５０〜９０重量％、密度が０．８５０〜０．９１０（ｇ／ｃｍ3）のエチレン系重合体（Ｂ）５〜５０重量％、カルボン酸変性またはエポキシ変性したエチレン系共重合体（Ｃ）１〜２０重量％とから構成された樹脂組成物をインフレーション成形したフィルムである。 - 特許庁 - To eliminate problems in deterioration of surface grade due to the occurrence of pilling in knitted or woven fabrics comprising spun yarns of polyester staple fibers when wearing the fabric and to obtain a spun yarn and a knitted or a woven fabric maintaining the strength physical properties, excellent in pilling resistance and further having body, stiffness, repulsion, a touch feeling, a lightweight feeling and heat retaining properties in combination.
ポリエステル短繊維の紡績糸からなる編織物はピリング着用時ピリング発生による表面品位劣化問題があり、強度物性を維持し、かつ抗ピル性にすぐれ、さらに張り腰反発風合い、軽量感、保温性を併せ持つ紡績糸および編織物を提供すること。 - 特許庁 - The in-mold decorating method of the molded product has a step for forming a primer layer on an in-mold decorating side of the molded product made of the unsaturated polyester resin and an in-mold decorating step for forming the in-mold decorating layer on this primer, wherein at least the in-mold decorating side of the molded product is plasma-treated before the primer layer is formed.
不飽和ポリエステル樹脂製の成形品の加飾面にプライマー層を形成する工程と、このプライマー層の上に加飾層を形成する加飾工程とを備える成形品の加飾方法において、プライマー層形成前に成形品の少なくとも加飾面をプラズマ処理することを特徴としている。 - 特許庁 - This thermoplastic elastomer composition comprises 100 pts.wt. of the resin composition including (A) a hydrogenated alkenylaromatic compound-conjugated diene block copolymer and (B) a softening agent for rubber at a weight ratio of 30/70-70/30 and (C) 2-40 pts.wt. of a melt-kneaded resin composition including (C1) a polyphenylene ether and (C2) a saturated polyester.
水素添加アルケニル芳香族化合物−共役ジエンブロック共重合体（Ａ）：ゴム用軟化剤（Ｂ）＝３０：７０〜７０：３０（重量比）である樹脂組成物１００重量部に対し、ポリフェニレンエーテル（Ｃ１）と飽和ポリエステル（Ｃ２）を含む溶融混練樹脂組成物（Ｃ）２〜４０重量部を含有してなる熱可塑性エラストマー組成物。 - 特許庁 - To provide a polyester film suitable as the base film of a mold-releasing film capable of realizing a high degree of the accuracy of examination in the case of performing the checking of the presence or absence of defects such as distortion or unevenness or a foreign material by a visual examination by using a crossed Nichol method on the polarizing plate in a state of being pasted with the releasing film.
離型フィルムが貼り合わされた状態の偏光板について、歪みやムラのような欠陥や異物の有無の検査をクロスニコル法による目視検査によって行う場合において、高度な検査の精度を実現することのできる離型フィルムのベースフィルムとして好適なポリエステルフィルムを提供する。 - 特許庁 - In this heating and crystallizing apparatus for the saturated polyester hollow object, the heater unit 30 is equipped with a near infrared heater 313 for irradiating the mouth part 11 of a preform 10 with light, a shield plate 319 for reflecting the irradiated light, an exhaust port 60 for forcibly exhausting air in the periphery of the heated mouth part 11 and a valve 62 for controlling exhaust quantity.
加熱結晶化装置１は、ヒータユニット３０が、プリフォーム１０の口部１１に光を照射する近赤外線ヒータ３１３と、照射された光を反射する遮蔽板３１９と、加熱された口部１１周囲の空気を強制的に排気する排気口６０と、排気量制御用のバルブ６２とを備えている。 - 特許庁 - There is provided a monofilament for a core material for clothes, that comprises a polyester resin composition comprising 5 to 40 wt% of polyethylene naphthalate and 60 to 95 wt% of polyethylene terephthalate, in which a Young's modulus, a dry heat shrinkage ratio at 140°C, and the number of reciprocating bending times required for breaking in MIT bending fatigue test of the monofilament each satisfy a specific number.
ポリエチレンナフタレート５〜４０重量％およびポリエチレンテレフタレート６０〜９５重量％からなるポリエステル樹脂組成物からなり、ヤング率、１４０℃における乾熱収縮率、およびＭＩＴ屈曲疲労試験における往復折り曲げ回数が特定の数値満たす被服芯材用モノフィラメント。 - 特許庁 - To provide a composite woven fabric or woven fabric having a soft swelling, excellent firmness, stiffness and color development, a surface feeling of spun yarn-like elegant casual sense, a slight massive feeling and a lightweight feeling or stretchability and biodegradability friendly to the environment which can not be attained by a conventional polyester fiber.
ソフトなふくらみを有し、張り、腰、発色性優れ、スパン調の上品なカジュアル感覚の表面感をもち、重量感の少ない軽量感覚を持つ、あるいはストレッチ性を有すると共に、従来ののポリエステル繊維では不可能であった環境にやさしい生分解性を有する複合編織物を提供する。 - 特許庁 - In the method for producing a polyester resin for toners by making a di- or higher valent acid component react with a di- or higher alcohol component, a reaction product is discharged from a polymerization tank, while forcedly cooling the resin in the polymerization tank at a cooling rate of 1-100°C/h or lower.
２価以上の酸成分と２価以上のアルコール成分を反応させてポリエステル樹脂を製造する方法において、重合釜内の樹脂を１〜１００℃／ｈ以下の冷却速度で強制冷却しながら、反応物を重合釜から吐出させることを特徴とするトナー用ポリエステル樹脂の製造方法。 - 特許庁 - The diffusion film is a lamination film made by laminating a resin layer having a micro ruggedness shape on at least one side surface of a base material film principally consisting of polyester, wherein the inner haze of the lamination film is 20 to 90% and the diffusion anisotropy is 2 to 500.
本発明の拡散フィルムは、ポリエステルを主構成成分とする基材フィルムの少なくとも一方の面に、微細凹凸形状を有する樹脂層を積層してなる積層フィルムであって、該積層フィルムの内部ヘイズが２０％〜９０％であって、かつ、拡散異方度が２〜５００であることを特徴とするものである。 - 特許庁 - To provide a textile product finishing agent imparting a textile product with a softening performance of a satisfiable level and exhibiting soil releasing effect not only to a fiber having high hydrophobicity such as polyester fiber but also to a fiber having a relatively high hydrophilicity such as cotton fiber independent of the conditions, and to provide a finishing method with the agent.
繊維製品に満足出来るレベルの柔軟性能を付与すると共に、ポリエステル繊維等の疎水性の高い繊維だけでなく、木綿繊維等の比較的親水性の高い繊維に対しても諸条件に左右されず汚れ放出効果を発揮できる繊維製品処理剤及びその処理方法を提供する。 - 特許庁 - The toner composition is prepared by using a polyester resin having low molecular weight as a binder resin, for example, a condensed product of polyoxyethylene[2,2-bis(4-hydroxyphenyl)]propane and glycerin with terephthalic acid or an ethylene-butyl methacrylate copolymer having low molecular weight, and by compounding a UV absorbent and an antioxidant in the binder resin.
結着樹脂として低分子量のポリエステル樹脂、例えばポリオキシエチレン〔２，２−ビス（４−ハイドロオキシフェニル）〕プロパンおよびグリセリンとテレフタル酸との縮合体、または低分子量のエチレンーメタクリル酸ブチル共重合体を用い、結着樹脂中に紫外線吸収剤および老化防止剤を配合したトナー組成物。 - 特許庁 - A fire retardant filter medium is formed by bonding a fiber web containing no halogen by a binder based on a thermoplastic resin containing no halogen and at least 50% or more of the fibers of the fiber web are constituted of polyester fibers and a hydrated metal compound type fire retardant and a phosphorus type fire retardant are added to the binder.
ハロゲン不含有の繊維ウェブをハロゲン不含有の熱可塑性樹脂を主体とするバインダーで結合した難燃ろ材であって、上記繊維ウェブの少なくとも５０％以上の繊維をポリエステル繊維で構成し、バインダーに水和金属化合物系難燃剤とリン系難燃剤とを含有して成る。 - 特許庁