＜前へ 1 2 .... 853 854 855 856 857 858 859 860 861 .... 976 977 次へ＞- This explosive composition contains one or ≥2 kinds of a nitro compound or nitrate which is a single combined explosive and further contains one or ≥2 kinds of an oxidizing agent or metallic powder or fuel at need in porous prill ammonium nitrate.
本発明の爆薬組成物は、ポーラスプリル硝酸アンモニウムに単一化合爆薬であるニトロ化合物又は硝酸エステルを１種或いは２種以上含有し、さらに必要に応じて酸化剤又は金属粉又は燃料の１種或いは２種以上を含有する。 - 特許庁 - To provide spherical titanium oxide particulate powder enabling its own spherical titanium particles to be controlled to a size larger than 100 nm, with the particles being uniformly spherical, and having a sufficient ultraviolet light-blocking effect, and to provide a cosmetic containing the same.
球状チタン粒子を１００ｎｍより大きい粒子径に制御でき、均一な球形で且つ十分な紫外線遮断効果を示す球状酸化チタン微粒子粉体とその球状酸化チタン微粒子粉体を含有する化粧料を提供する。 - 特許庁 - The anti-solidification agent for the powdery cement dispersing agent contains calcium carbonate fine powder which is first surface-treated with a compound having an amino group and/or quaternary ammonium group and then surface-treated with a compound having an anionic group.
アミノ基及び／又は４級アンモニウム基を有する化合物で表面処理した後、更にアニオン基を有する化合物で表面処理してなる炭酸カルシウム微粉体を含むことを特徴とする粉末状セメント分散剤の固結防止剤を提供する。 - 特許庁 - The manufacturing method of the spherical granules comprises spraying a liquid containing a solid content to the nuclear particles while tumbling the nuclear particles containing a sugar by rotating a rotary tray set horizontally without scattering powder component.
糖を含有する核粒子を水平に設置した回転皿を回転させることにより転動させながら、粉末成分を散布することなく、該核粒子に固形分を含有する液を噴霧することを含むことを特徴とする球形顆粒の製造方法である。 - 特許庁 - This abrasive sheet for semiconductor wafers manufactured by impregnating and attaching urethane based emulsion resin liquid with fine- powder abrasive uniformly dispersed into soft polyurethane foam or semi-hard polyurethane foam, especially its surface, and by compression molding into a resin form.
微粉末状の研磨材を均一に分散せしめたウレタン系エマルジョン樹脂液を、軟質ポリウレタンフォームまたは半硬質ポリウレタンフォーム、特にその表面部に含浸・付着させ、樹脂状に圧縮成形して成ることを特徴とする半導体ウェハー用研磨シートである。 - 特許庁 - A paint that prevents attachment of marine lives is painted on the bottom of the ship a wharf, or the like with which seawater contacts, and comprises tar like material gathered from the bottom layer of precipitated pyrolignous acid and mixed with powder activated carbon and pigments.
海水の付着する船底、岸壁等に木酢液を塗布し、海洋生物の着生を防止する塗料であって、木酢液を沈殿させて最下層のタール状物質を採取し、そのタール状物質に、粉状の活性炭及び色素剤を混合した。 - 特許庁 - A conductive paste for forming an electrode on a semiconductor substrate for photoelectric conversion elements comprises a metal powder, having A1 as the main constituent and has oxidation starting temperature in the air, in a temperature range of 600°C or higher and 660°C or lower.
光電変換素子用の半導体基板に電極を形成するための導電性ペーストであって、Ａｌを主体とする金属粉末を含有し、かつ６００℃以上６６０℃以下の値域範囲内に空気中における酸化開始温度を有する無機粉末を備える。 - 特許庁 - Further, the negative electrode material is obtained by heat treatment of a compound mixed with carbon at temperature ranging from 400 to 1,000°C under a non-oxidizing atmosphere, after drying and solidifying the above compound against sol composite containing lithium hydrate and titanium oxide powder.
また，負極材料は，水酸化リチウムと酸化チタン粉末とを含有するゾル状混合物に対しカーボンを混合した混合物を準備し，該混合物を乾燥固化させた後，非酸化性雰囲気下，温度４００〜１０００℃において熱処理することで得られる。 - 特許庁 - The paste for a laminated ceramic electronic component is used by being applied on a ceramic green sheet and dried, and contains a polyvinyl acetal resin, an organic solvent and inorganic powder, wherein the organic solvent contains butylene glycol di-acetate.
セラミックグリーンシート上に塗工、乾燥することによって使用される積層セラミック電子部品用ペーストであって、ポリビニルアセタール樹脂、有機溶剤及び無機粉末を含有し、前記有機溶剤は、ブチレングリコールジアセテートを含有する積層セラミック電子部品用ペースト。 - 特許庁 - This collagen synthesis accelerator contains a powder or an extract, as it is or roughly purified or purified, of at least one plant selected from among plants of the genera Pfaffia and Ajuga as the effective component.
パフィア属に属する植物およびキランソウ属に属する植物からなる群から選ばれる少なくとも１種の植物の粉末、抽出物または該抽出物の粗精製物もしくは精製物を有効成分として含む生体コラーゲンの合成促進剤を提供する。 - 特許庁 - To provide a separator material for solid polymer type fuel cell having an excellent gas impermeability, electric resistance, strength, moisture resistance and the like by binding graphite powder by a novolac type phenol resin with resin properties specified and having excellent flowability; and to provide its manufacturing method.
樹脂性状を特定した流動性に優れたノボラック型フェノール樹脂により黒鉛粉末を結着し、気体不透過性、電気抵抗、強度、耐湿性などに優れた固体高分子型燃料電池用のセパレータ材とその製造方法を提供する。 - 特許庁 - The total content of an inorganic filler containing the metal hydroxide powder is 20-80 vol.% based on the total volume of the resin solid and the inorganic filler.
さらに、金属水酸化物粉末を樹脂固形分１００質量部に対して５０〜１００質量部含有し、前記金属水酸化物粉末を含む無機充填材の総含有量が樹脂固形分と無機充填材の総体積の中で２０〜８０体積％である。 - 特許庁 - The metallic plating layer is preferably formed by applying electric plating on electroless-plated layer, and an electric plating liquid is mixed with the powder for generating the anion, thus realizing a product with higher negative ion and electromagnetic wave shield effects.
金属メッキ層は、無電解メッキした上に電気メッキを施すことにより形成するのが好ましく、電気メッキの際に、電気メッキ液に前記粉末を混合使用することにより、マイナスイオン効果及び電磁波シールド効果いずれも、より高度な製品を得ることができる。 - 特許庁 - When a rare earth sintered magnet is produced by sintering a molding of material alloy fine powder containing a rare earth element, a transition metal element and boron, de-binding process is performed by ohmic-resistance heating and then sintering is performed by high frequency induction heating.
希土類元素、遷移金属元素及びホウ素を含む原料合金微粉を成形した成形体を焼結し、希土類焼結磁石を製造するに際し、抵抗加熱により脱バインダー処理を行った後、高周波誘導加熱により焼結を行う。 - 特許庁 - To a biological calcium phosphate bone filling cement mixture and a method for manufacturing the biological cement mixture that can be inexpensively and simply mixed at a high powder/liquid ratio and is free from sundry germs and foreign matter.
生体用補綴物として有用な高粘度の生体用リン酸カルシウム骨充填セメント練和物の提供、及び高い粉液比での練和が安価、簡便にでき、かつ雑菌や不純物の混入する恐れの少ない生体用セメント練和物の製造方法の提供。 - 特許庁 - The powder coating composition contains an epoxy group-containing vinylic copolymer having ≥40°C glass transition temperature, an epoxy group-containing vinylic copolymer having ≤0°C glass transition temperature and having an organosiloxane side chain, and a polybasic carboxylic acid as essential components.
４０℃以上のガラス転移温度を有するエポキシ基含有ビニル共重合体、０℃以下のガラス転移温度を有し、オルガノシロキサン側鎖を有するエポキシ基含有ビニル共重合体及び多価カルボン酸を必須の成分として含有する粉体塗料組成物。 - 特許庁 - To prevent offset of toner carried on a recording medium and to prevent the offset of the toner induced by paper powder in a fixing device heating, pressuring and fixing by feeding the recording medium carrying toner images into a pressure contact part between a fixing rotating body and a pressure member.
トナー像が担持された記録媒体を定着回転体と加圧部材との圧接部に送り込み、加熱及び加圧して定着する定着装置において、記録媒体に担持されたトナーのオフセットを防止するとともに紙紛に誘発されるトナーのオフセットをも防止する。 - 特許庁 - In the magnetic recording medium wherein the metal magnetic layer containing magnetic powder and the bonding agent is formed on a non- magnetic substrate, the bonding agent contains alkyl acetalized polyvinyl alcohol and has 60-80°C glass transition temperature and the magnetic layer contains a silane coupling agent and a carboxylic acid.
非磁性支持体上に磁性粉末と結合剤を含有する金属磁性層を形成した磁気記録媒体の前記結合剤が、アルキルアセタール化ポリビニルアルコールを含みかつそのガラス転移温度が60〜80℃であり、磁性層にシランカップリング剤とカルボン酸を含む。 - 特許庁 - The recycled asphalt mixture preservable at room temperature includes the aggregate collected and recycled from the waste asphalt pavement whose surface is covered with an asphalt film whereas cement powder is adhered to the outer surface of the asphalt film covering the surface of the aggregate.
廃棄アスファルト舗装から回収再生され、その表面がアスファルト膜で覆われている骨材を有し、前記骨材の表面を被覆するアスファルト膜の外表面にセメント粉が付着されていることを特徴とする常温保存可能再生アスファルト混合物。 - 特許庁 - This method for producing the tofu excellent in elasticity and strength by using fine whole fat raw soybean powder without separating the soybean curd refuse is provided by fermenting and coagulating by using only a pro-biotic lactobacillus and transglutaminase enzyme without using the coagulating agent.
全脂微細生大豆粉末を用いて、おからを分離せずに全豆腐を製造することにおいて、凝固剤を使わずに、プロバイオティック乳酸菌とトランスグルタミナーゼ酵素のみで醗酵し凝固させることによって、弾力性と強度に優れた豆腐を製造する。 - 特許庁 - Such the alkali metal (meth)acrylate powder can suitably be produced by feeding an aqueous solution of the alkali metal (meth)acrylate to a spray drier having 260-400°C inlet hot air temperature to spray-dry the aqueous solution of the alkali metal (meth)acrylate.
このような（メタ）アクリル酸アルカリ金属塩粉体は、入口熱風温度が２６０〜４００℃の噴霧乾燥装置に、（メタ）アクリル酸アルカリ金属塩水溶液を供給して、該（メタ）アクリル酸アルカリ金属塩水溶液を噴霧乾燥することで、好適に製造できる。 - 特許庁 - The product proves to be a crystal by powder X-ray diffraction and gives a maximum endothermic peak at a temperature of 180°C or higher by DST to prove to be a uniform crystalline α-lipoic acid lysine salt in its chemical composition and crystalline shape.
生成物は粉末Ｘ線回折により結晶であることを示し、ＤＳＴにおいて１８０℃以上の温度において最大吸熱ピークを示し、化学組成および結晶形態において均一な結晶性α−リポ酸リジン塩であることが証明された。 - 特許庁 - This resin composition for powder molding is obtained by dry- blending a plasticizer to a vinyl chloride-based resin and characterized by including hydroxystearic acid and a foaming agent having 1-10 μm mean particle diameter in the composition.
塩化ビニル系樹脂に可塑剤をドライブレンドした粉体成形用の樹脂組成物であって、該組成物中にヒドロキシステアリン酸及び平均粒径１μｍ〜１０μｍの発泡剤を含有せしめたことを特徴とする粉体成形用発泡性塩化ビニル系樹脂組成物。 - 特許庁 - To provide a label capable of effectively intercepting ultraviolet rays having a fear of exerting a bad influence on food and visible light without using a special ink containing an aluminum paste, an aluminum powder, a titanium white pigment or the like, and a container covered with the label.
アルミペースト、アルミ粉末、チタン白顔料等を含有する特殊なインキを用いることなく、食品に悪影響を及ぼすおそれのある紫外線や可視光線を有効に遮断することのできるラベル及びそのラベルにて被覆された容器を提供することである。 - 特許庁 - To prevent crack caused at firing by integrally forming zirconia-graphite material at a powder line part and a material containing a clinker contained of CaO as a mineral phase at the other portion, in a continuous casting immersion nozzle for preventing the alumina deposition.
アルミナ付着防止を目的とする連続鋳造用の浸漬ノズルで、パウダーライン部のジルコニア・黒鉛材質と、その他の部分の鉱物相としてのＣａＯを含有するクリンカーを含む材質を一体成形して焼成した際に発生する亀裂を防止すること。 - 特許庁 - A pulverized powder obtained by pulverizing at least one kind of carbonates of biomass selected from ligneous biomass, a plant-based residue generated in a plantation and the like with a pulverized coal such as coal are mixed and burnt, whereby NOx contained in combustion exhaust gas is reduced.
木質系バイオマスやプランテーションにおいて発生する植物系残渣などから選ばれる少なくとも一種のバイオマスの炭化物を微粉砕した微粉体と、石炭等の微粉炭と、を混合燃焼させることにより、燃焼排ガス中のＮＯｘを低減させる。 - 特許庁 - To provide a method for producing ultrafine semiconductor particles in which the ultrafine semiconductor particles synthesized in a solvent containing water, particularly composed mainly of water, is separated as a powder which can be redispersed safely at a low cost without impairing characteristics thereof.
水を含有する溶媒中、特に水を主成分とする溶媒中で合成された半導体超微粒子をその特性を損なうことなく、低コストで安全に再分散可能な粉末として分離する半導体超微粒子の製造方法を提供する。 - 特許庁 - The method of manufacturing the molded coil, which seals an air-core coil 1 with a magnetic mold resin 5 having magnetic powder dispersed using a plastic forming method, uses a forming mold including a cavity 4 formed from a plurality of molds and a positioning pin 2a.
プラスチック成形法を用いて、磁性体粉末を分散させた磁性体モールド樹脂５で空芯コイル１を封止してなるモールドコイルの製造方法において、複数の金型から形成されるキャビティ４と、位置出しピン２ａを有する成形金型を用いる。 - 特許庁 - The glass raw material contains the abrasive in which content of cerium oxide is ≥95 mass % and glass fine powder occurring from polishing using the abrasive and chlorine content in the abrasive is ≤0.2 mass %.
本発明のガラス原料は、酸化セリウムの含有率が９５質量％以上である研磨材と、該研磨材を用いた研磨により生じたガラス微粉末とを含むガラス原料であって、研磨材中の塩素の含有率が０．２質量％以下であることを特徴とする。 - 特許庁 - To provide a composition for a nickel electrode of an alkaline battery capable of realizing uniform filling-up of an active material powder as a primary component of nickel hydroxide to a porous base board regarding the non-sintered nickel electrode and supplying an alkaline battery with suitable characteristics.
非焼結式ニッケル電極に関して、水酸化ニッケルを主成分とする活物質粉末の多孔質基板への均一な充填を実現し、良好な特性を有するアルカリ電池を提供可能なアルカリ電池ニッケル電極用組成物を提供する。 - 特許庁 - The electrode in the varistor is formed of conductive paste of, principally comprising particles of Pd and containing metal powder where the content of particles having grain size of 0.1 μm or smaller is under 20 mass%.
このバリスタにおける電極は、Ｐｄからなる粒子を主成分として含み、且つ、０．１μｍ以下の粒径を有する粒子の含有量が２０質量％未満である金属粉末を含有している本発明の導電性ペーストから形成されたものである。 - 特許庁 - The method for manufacturing magnetite particulate powder includes; adding one or more coupling agents containing silicon, aluminum or titanium to a magnetite cake obtained by an aqueous iron salt solution neutralization-oxygen-containing gas oxidation method; and carrying out kneading, drying and heat treatment.
鉄塩水溶液中和−酸素含有ガス酸化法にて得られたマグネタイトケーキに、１種又は２種以上のケイ素、アルミニウム、またはチタニウム含有のカップリング剤を加え、混練し、乾燥、熱処理を行うことを特徴とするマグネタイト粒子粉末の製造方法。 - 特許庁 - Material powder consisting rare earth-iron-nitrogen-hydrogen magnetic material that a rhombohedral or a hexagonal crystal structure is formed into a molded body by compaction, and the molded body is shock- compressed and solidified into the solid material for magnet by the use of underwater shock waves.
原材料として菱面体晶又は六方晶の結晶構造を有する希土類−鉄−窒素−水素系磁性材料を含む原料粉末を圧粉成形し、この成形体を水中衝撃波を用いて衝撃圧縮固化して磁石用固形材料を得る。 - 特許庁 - The thermoplastic resin composition comprises 100 pts.wt. of a thermoplastic resin, 0.1 to 20 pts.wt. of an acrylic copolymer, and 0.1 to 50 pts.wt. of polytetrafluoroethylene-containing mixture powder comprising polytetrafluoroethylene particles and an organic polymer.
熱可塑性樹脂１００質量部に対し、アクリル系高分子共重合体０.１〜２０質量部と、ポリテトラフルオロエチレン粒子及び有機系重合体からなるポリテトラフルオロエチレン含有混合粉体０.１〜５０質量部とが添加されてなる熱可塑性樹脂組成物。 - 特許庁 - The low noise pavement body is constituted by filling an elastic paving material 2 comprising asphalt and an ethylene vinylacetate copolymer as a binder, aggregate and rubber chips and/or rubber powder, in voids near a surface layer part in the porous pavement body 1.
多孔質舗装体１における表層部近傍の空隙内部に、バインダーとしてのアスファルトおよびエチレン酢酸ビニル共重合体と、骨材と、ゴムチップおよび／またはゴム粉末とを含む弾性舗装材料２が充填されてなる低騒音舗装体である。 - 特許庁 - To be concrete, one of zeolite, sepiolite and diatomaceous earth is preferable as the porous granules and powder having adsorptivity to a harmful substance and one of titanium dioxide, zinc oxide, in dioxide and silver oxide is preferable as the semiconductor generating the photocatalytic reaction respectively.
具体的には、有害物質に対して吸着性のある多孔質粉粒体はゼオライト、セピオライト、ケイソウ土のいずれか、また、光触媒反応を生じる半導体としては二酸化チタン、酸化亜鉛、二酸化スズおよび酸化銀のいずれかがそれぞれ好適である。 - 特許庁 - To provide a minus ion generator which appropriately controls the amount of generation of minus ion or the amount of irradiation generated from an exciting agent and, further, decreases the pressure loss caused by a mixture of powder having spontaneous polarization and the exciting agent.
マイナスイオンの発生量または励起剤から発生する放射線量を適切に調節することが可能であり、さらには、自発分極を有する粉体と、励起剤との混合物に起因する圧力損失を小さくするマイナスイオン発生装置を提供する。 - 特許庁 - To treat a powder to as to ensure a reduced transport cost by to increasing the loadage at the time of transport, downsized storage equipment by reducing the storage space, improved reactivity by increasing the surface area and improved flowability.
粉体について、輸送時の積載量を増大させて輸送コストを低下させ、貯蔵スペースを縮小させて貯蔵設備を小型化させ、同時に表面積を増大させることで反応性を改善し、流動性を良好にする粉体処理方法を提供する。 - 特許庁 - The aluminum alloy brazing filler metal in powder state having the mean grain size of 10-100 μm obtained by spraying the molten aluminum alloy in vacuum or in inert gas and quenching it is sprayed on the object on which the flux is spray-coated.
アルミニウム合金ろう材も、アルミニウム合金溶湯を真空中又は不活性ガス中で噴霧して急冷することにより得られた１０〜１００μｍの平均粒径を有する粉末状のものを、前記フラックスをスプレー塗布した接合対象部上に散布する。 - 特許庁 - The negative electrode for the lithium secondary battery comprises: a metal collector; and an active material layer formed on the metal collector and containing active material powder and a cellulose-based polymer binder having an esterification degree above 1.3 and a molecular weight above 100,000.
本発明のリチウム二次電池用負極は、金属集電体;及び金属集電体に形成された活物質粉末及びエステル化度が１．３以上であって、分子量が１００、０００以上であるセルロース系高分子バインダーを含む活物質層からなる。 - 特許庁 - A fiber-reinforced plastic composite molding formed by laminating a fiber-reinforce plastic and a resin mortar is obtained by mixing a ground material or a powder of the resin molding containing the fiber-reinforced plastic with the resin mortar.
繊維強化プラスチック及び樹脂モルタルを積層することにより形成される繊維強化プラスチック複合成形体において、繊維強化プラスチックを含有する樹脂成形物の粉砕物又は粉体を上記樹脂モルタルに混入することを特徴とする。 - 特許庁 - The cylindrical magnet which is formed by molding a mixture mainly composed of ferromagnetic powder and a resin binder has the cylindrical magnet imbedded with a plurality of numbers of magnet pieces that are repulsed magnetically from each other in an indention in an outer periphery section.
強磁性体粉末と樹脂バインダーを主体とする混合物を成形してなる円筒状マグネットにおいて、該円筒状マグネットが、外周部の凹部に互いに磁気的に反発する複数個のマグネットピースを埋設しているマグネットローラにより上記課題が解決できる。 - 特許庁 - To provide a method for producing a granular composition containing soybean isoflavone, lysine and useful components such as minerals and calcium contained in a seaweed by using a turbid liquid obtained by adding soybean powder to pulverized seaweeds such as wakame seaweed and sea tangle as a raw material.
この発明は、破砕した海藻ワカメ及び海藻昆布等に大豆粉末を加えた混濁液を原料として用い、大豆イソフラボン、リジン及び海藻に含まれているミネラル、カルシウム等有用成分の含有した粒状組成物の製造方法に関するものである。 - 特許庁 - The objective powder is characterized in that its surface is coated with an acryl-silicone graft copolymer obtained by copolymerizing an organopolysiloxane compound having a radically polymerizable group on one end of the molecular chain and a radically polymerizable monomer mainly comprising a 12-30C alkyl(meth)acrylate.
分子鎖の片末端にラジカル重合性基を有するオルガノポリシロキサン化合物と炭素数１２〜３０のアルキル（メタ）アクリレートを主体とするラジカル重合性モノマーとを共重合して得られるアクリル−シリコーン系グラフト共重合体で表面被覆した粉体。 - 特許庁 - The readily handleable electric wave shielding material having excellent conductivity and electric wave shielding performances and usable in various applications can be obtained by mixing a general-purpose two-pack mixing type foamable urethane with conductive metal powder and conductive carbon fibers.
汎用の２液混合型の発泡ウレタンに、導電性金属粉と導電性のカーボン繊維を混合することで、導電性及び電波シールド性能に優れ、尚且つ様々な用途に使用可能で取り扱いも容易なである電波シールド材料を得ることができた。 - 特許庁 - Electrolysis is applied using a silver salt aqueous solution obtained by adding weak acid, particularly, carboxylic acid having two or more carboxyl groups such as malic acid and citric acid as an electrolytic solution, thus the silver powder having a relatively small grain size, and also having a dendrite shape can be obtained.
弱酸、特にリンゴ酸やクエン酸、酒石酸のようにカルボキシル基を２つ以上有するカルボン酸を添加してなる銀塩水溶液を電解液に用いて電解することにより、粒度が比較的小さく、且つデンドライト状を呈する銀粉を得ることができる。 - 特許庁 - BaTiO_3 powder is added to the electrode paste 22, so that the deterioration of the adhesiveness between the dielectric layer 12 and the internal electrode layer 14 after the calcination is significantly suppressed and the temperature of starting sintering approaches that of the green sheet 20.
この電極ペースト２２には、ＢａＴｉＯ_３粉末が添加されているため、焼成後の誘電体層１２と内部電極層１４との密着性低下が有意に抑制されており、その焼結開始温度はグリーンシート２０の焼結開始温度に近づいている。 - 特許庁 - (2) By anodizing the metal base material or the porous sintered compact of metal powder in an electrolyte of mixed acid ammonium fluoride and hydrogen peroxide, a nanoporous oxide layer is formed on the surface of the base material or the surface of the porous sintered compact.
（２）金属基材、または金属粉末の多孔質焼結体を、酸性フッ化アンモニウムと過酸化水素水の混合電解溶液中で陽極酸化することにより、前記基材表面または多孔質焼結体の表面にナノポーラス酸化物層を形成する。 - 特許庁 - The composition (i) includes at least one polyamide and at least one copolymer (A) of ethylene with at least one comonomer chosen from unsaturated carboxylic acids, esters of unsaturated carboxylic acids or vinyl esters of saturated carboxylic acids and (ii) is in powder form.
(i) 少なくとも１種のポリアミドと、少なくとも１種のエチレンと不飽和カルボン酸、不飽和カルボン酸エステルおよび飽和カルボン酸ビニルエステルの中から選択される少なくとも１種のコモノマーとのコポリマー(A) とで構成され且つ(ii)粉末であることを特徴とする組成物。 - 特許庁 - To provide a manufacturing method in which a rare earth permanent magnet can be produced industrially easily by preliminarily compressing rare earth-iron-nitrogen magnet powder and then compacting the preform.
希土類−鉄−窒素系磁石粉末を予備圧縮成形した後、この予備成形体を圧密化することにより、工業的に容易に生産可能とした希土類永久磁石の製造方法、及びこれにより得られ磁気特性に優れた希土類永久磁石を提供する。 - 特許庁