「cold rolling process」を含む例文一覧(68)
＜前へ 1 2- The copper rolled foil can be manufactured by repeatedly applying cold rolling and process annealing after applying a hot-rolling to a copper ingot to obtain a rolled copper foil, then heat-treating the obtained rolled copper foil at a temperature of 150°C or higher.
このような銅圧延箔は、銅鋳塊に熱間圧延を施した後、冷間圧延及び中間焼鈍を繰り返すことにより、圧延銅箔を得た後、この圧延銅箔に１５０℃以上の温度で、加熱処理を施して、製造することができる。 - 特許庁 - Otherwise, the square copper wire in which the copper strand whose volume resistance is 2.5 μΩ cm or less and which has been annealed at 300-800°C is applied with cold rolling or cold drawing process at work efficiency 0-15%, and after that, expansion of 0.5-1% is applied.
また、体積抵抗率が２．５μΩ・ｃｍ以下で、３００〜８００℃で焼鈍処理が施された銅素線に、０〜１５％加工率の冷間圧延又は冷間伸線加工が施された後に０．５〜１％の伸びを付与した平角銅線である。 - 特許庁 - To provide a device and a method for grinding a metallic belt capable of preventing a crack and a rupture of an end part in the direction of width of the metallic belt in the next cold rolling process even after the metallic belt like a thin cold rolled steel belt having a thickness of 0.8 mm or less is ground.
０．８ｍｍ以下の板厚の薄い冷延鋼帯の如き金属帯を研削した後であっても、次の冷間圧延工程において金属帯の幅方向端部の割れ、破断を防止可能な金属帯の研削装置及び研削方法を提供する。 - 特許庁 - To provide a process for cold-rolling an aluminum sheet at the lowest possible cost of producing a rolled aluminum sheet, which process comprises minimizing the concentration of an aliphatic alcohol or a fatty acid ester added in an amount within the scope not detrimental to the quality of the surface of the rolled aluminum sheet.
脂肪族アルコールや脂肪酸エステルの添加濃度をアルミニウム板の表面の品質低下を招くことなく最低限のものとすることにより、アルミニウム板の製造コストを極力低減するアルミニウム板の冷間圧延方法を提供する。 - 特許庁 - This is obtd. by subjecting a cast slab having ≥15 vol.% equi-axed crystal ratio to hot rolling, grinding the surface by ≥10 μm, next, subjecting it to cold rolling including process annealing or not including that according to Cr content or the like and moreover executing bright annealing or annealing and pickling.
これは、等軸晶率が15体積％以上である鋳造スラブを熱間圧延し、表面を10μm以上研磨し、次いで、Cr含有量等に応じて中間焼鈍を含むかあるいは含まずに冷間圧延し、さらに光輝焼鈍または焼鈍・酸洗を施して得られる。 - 特許庁 - To provide a rolled sheet tempered material which consists of an Al-Mg alloy, and has a heat treatment degree of H32 to 36, particularly, which stably has excellent bending workability as a thick sheet of about 0.8 mm by a process where process annealing during cold rolling is obviated.
Ａｌ−Ｍｇ系合金からなる調質度Ｈ３２〜Ｈ３６の圧延板調質材、特に０．８ｍｍ程度以上の厚い板として、冷間圧延中途の中間焼鈍を省略したプロセスで、曲げ加工性が安定して優れたものを提供する。 - 特許庁 - The method of manufacturing the ultra thin-walled seamless metallic tube is characterized in that the seamless metallic tube manufactured by a hot manufacturing process is used as the tube stock, thickness is reduced by performing the elongation rolling after reheating and the thickness is further reduced by a cold-manufacturing process.
熱間製造プロセスにより製造された継目無金属管を素管として、再加熱後、延伸圧延を行って肉厚を減じ、冷間製造プロセスによりさらに肉厚を減じることを特徴とする超薄肉継目無金属管の製造方法である。 - 特許庁 - To provide a rolled sheet tempered material which consists of an Al-Mg alloy, and has a heat treatment degree of H32 to 36, particularly, which has stably excellent bending workability as a thick sheet of about ≥0.8 mm by a process where process annealing during cold rolling is obviated.
Ａｌ−Ｍｇ系合金からなる調質度Ｈ３２〜Ｈ３６の圧延板調質材、特に０．８ｍｍ程度以上の厚い板として、冷間圧延中途の中間焼鈍を省略したプロセスで、曲げ加工性が安定して優れたものを提供する。 - 特許庁 - The aluminum foil for an electrolytic capacitor anode can easily be obtd. by subjecting an aluminum ingot to homogenizing treatment at 530 to 620°C for 1 to 30 hr and also under the conditions in the ranges satisfying specified conditions and thereafter executing hot rolling, cold rolling, process annealing, finish rolling and final annealing by well known conventional methods.
このような電解コンデンサ陽極用アルミニウム箔は、アルミニウム鋳塊に、温度５３０〜６２０℃、時間１〜３０時間であって、一定の条件を満たす範囲内の条件で均質化処理を施した後、従来公知の方法で、熱間圧延，冷間圧延，中間焼鈍，仕上圧延及び最終焼鈍を施せば、容易に得ることができる。 - 特許庁 - To provide a pickling method for a hot rolled steel strip superior in surface quality after pickling, without degradation of the surface quality such as sliver flaw or plating irregularity, in a post-process such as cold rolling or surface treatment.
冷間圧延や表面処理などの後工程で、スリバー疵やめっきの付着むらなどといった表面品質低下のない、酸洗後の表面性状に優れる熱延鋼帯の酸洗方法を提供する。 - 特許庁 - The filter aid 24 used for a filtering process step of the cold rolling mill lubricant for performing pressure filtration by forming a coating layer of the filter aid on the filter paper 22 is composed of fibriform powder 24f and activated clay 24h.
濾紙２２の上に濾過助剤のコート層を形成し加圧濾過を行う冷間圧延油の濾過工程に使用される濾過助剤２４において、前記濾過助剤は、繊維状粉体２４ｆと、活性白土２４ｈとにより構成した。 - 特許庁 - To provide a looper device capable of simplifying constitution as much as possible and capable of achieving compactification of the device and lowering costs in the looper device placed in the process line of the surface- processing unit such as the pickling machine in the cold rolling equipment.
冷間圧延設備における酸洗装置等の表面処理装置のプロセスラインに配置されたル−パ装置において、構成をできる限り簡素化し、装置のコンパクト化とコスト低減を図る様にしたものを提供することを課題とする。 - 特許庁 - To provide a steel composition intended to be used in a process comprising a cold rolling step, for the production of uncoated, electro-galvanized or hot dip galvanized TRIP steel products; a method for producing the steel products; and the steel products.
被覆されていない、電気ガルバナイジングされた又は熱浸漬ガルバナイジングされたＴＲＩＰ鋼製品の製造のための、冷間圧延工程を含む方法に使用されることを意図される鋼組成物、さらに、前記鋼製品の製造方法および鋼製品を提供する。 - 特許庁 - To provide a non-oriented electrical steel sheet having an excellent high frequency core loss, in which a decarburization load in a steel making process is reduced, the oxidized-layer of a product is not produced, and precipitation of carbide and an aging deterioration are not caused in the product, by controlling an oxygen potential in the annealing atmosphere to a suitable range in a finish annealing process after cold rolling to the last product thickness.
最終製品厚に冷間圧延した後の仕上焼鈍工程において、焼鈍雰囲気の酸素ポテンシャルを適正な範囲に制御することで、製鋼での脱炭負荷を低減し、かつ製品の酸化層を生じさせず、炭化物析出や時効劣化の起きない高周波鉄損の優れた無方向性電磁鋼板を提供する。 - 特許庁 - To provide a shaft member of a rolling bearing device for a wheel, which can further increase the rigidity and strength of a flange, and can extend a life of a metal mold by dispersing stress generated by a raw material in a cold forging process.
フランジ部の剛性・強度をより大きくすることが可能な車輪用転がり軸受装置の軸部材、そして冷間鍛造工程において素材による応力を分散して金型の寿命をより長くすることが可能な車輪用転がり軸受装置の軸部材を提供する。 - 特許庁 - Further, the process for producing the titanium alloy sheet is characterized in that a final annealing is performed within a temperature range of 650 to 830°C, or that a hot-rolled-sheet annealing or intermediate annealing is performed within a temperature range of 650 to 830°C while a final annealing after cold rolling is performed within a temperature range of 600 to 650°C.
また、最終焼鈍を、６５０〜８３０℃の温度域にて行う、あるいは、熱延板焼または中間焼鈍を、６５０〜８３０℃の温度域にて行い、冷間圧延後の最終焼鈍を６００〜６５０℃の温度で行うことを特徴とする該チタン合金板の製造方法。 - 特許庁 - Cut pieces 6 obtained by cutting a material which cannot be fed to a hot and cold rolling process due to its surface flaw and inclusions in its inside and is used as iron scrap among slabs and blooms mass-produced in a blast furnace and an electric furnace in a manufacturer to predetermined size are piled up and required parts are welded at several portions to integrate them.
高炉や電気炉メーカーで量産されるスラブやブルームのうち、表面疵や内部に介在物があって熱冷延工程に送ることができない鉄スクラップとして使用されるものを所定の大きさに切断して得た切断片６を積み重ね、所要部を数か所溶接して一体化する。 - 特許庁 - The aluminum alloy is composed of 0.90-1.60 mass % Fe, 0.03-0.20 mass % Si, 0.0005-0.030 mass % Cu and the balance Al with unavoidable impurities, wherein the tensile strength is 170-120 MPa without process annealing in cold rolling.
アルミニウム合金は、Ｆｅ：０．９０乃至１.６０質量％、Ｓｉ：０.０３乃至０.２０質量％及びＣｕ：０.０００５乃至０.０３０質量％を含有し、残部がＡｌ及び不可避的不純物からなる組成を有し、冷間圧延時に中間焼鈍を行わず、引張強度が１７０乃至２１０ＭＰａである。 - 特許庁
- 特許庁
- Copyright © Japan Patent office. All Rights Reserved.