「nonoriented」を含む例文一覧(210)
＜前へ 1 2 3 4 5 次へ＞- AGE-HARDENABLE NONORIENTED ELECTROMAGNETIC STEEL SHEET HAVING EXCELLENT BLANKING PROPERTY AND CORE LOSS, PRODUCTION METHOD THEREFOR AND PRODUCTION METHOD FOR ROTOR USING THE SAME
打ち抜き性及び鉄損の優れた時効硬化性無方向性電磁鋼板、その製造方法及びそれを用いたローターの製造方法 - 特許庁 - To provide a nonoriented silicon steel sheet capable of giving high caulking force at caulking and having properties suitable for the application of caulking.
かしめに際して強いかしめ力が得られ、かしめ加工を行うのに好適な性質を有する無方向性電磁鋼板を提供する。 - 特許庁 - To produce a nonoriented silicon steel sheet small in magnetic anisotropy in a high-frequency area and, further, capable of obtaining good motor characteristics.
高周波域における磁気異方性が小さく、ひいては良好なモーター特性が得られる無方向性電磁鋼板を提供する。 - 特許庁 - To provide a low-cost producing method for a nonoriented silicon steel sheet excellent in magnetism including core loss and suppressed in the cost for slab heating, in the method for producing a nonoriented silicon steel sheet in which sheet bars are joined, and continuous hot rolling is carried out, by controlling the heating condition for a slab after casting.
シートバーを接合して連続熱延を行う無方向性電磁鋼板の製造法において、鋳造後のスラブの加熱条件を制御することにより、鉄損をはじめとした磁性に優れると共に、スラブ加熱コストを抑制して低コストな無方向性電磁鋼板の製造法を提供する。 - 特許庁 - To produce a nonoriented silicon steel sheet for attaining the returning torque of a handle which has been the problem peculiar to motor-driven power steering and to provide a method for producing the same.
電動パワステの固有問題であったハンドルの戻りトルクを出すための無方向性電磁鋼板とその製造方法を提供する。 - 特許庁 - To provide a nonoriented magnetic steel sheet which has small iron loss deterioration even under compressive stress in which high compressive stress of ≥10 MPa is imparted.
10MPa以上の高い圧縮応力が付与される圧縮応力下においても、鉄損劣化が小さい無方向性電磁鋼板を提供する。 - 特許庁 - To effectively improve magnetic properties of a nonoriented silicon steel sheet used for a motor, transformer or the like, keeping a cost as possible.
モータや変圧器等に使用される無方向性電磁鋼板について、コストアップを極力抑制しつつ、磁気特性の効果的な改善を図る。 - 特許庁 - To provide a nonoriented silicon steel sheet which does not cause deterioration in iron loss value when compressive stress is applied, and has reduced stress dependency.
圧縮応力が付与された際に鉄損値の劣化をまねくことのない、応力依存性の小さい無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented electrical steel sheet in which circumferential magnetic properties inside the steel face can be improved.
鉄心材料として無方向性電磁鋼板が使用される場合には、特に回転機鉄心の場合、鋼板面内での等方的に優れた磁気特性が要請される。 - 特許庁 - To provide a nonoriented silicon steel sheet combining the excellent magnetic properties of high magnetic flux density and low core loss and the excellent mechanical properties of high strength.
高磁束密度、低鉄損という優れた磁気特性と、高強度という優れた機械特性を兼ね備える無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet excellent in workability when it is produced and used and further having high electric resistance and good high frequency magnetic properties.
製造時並びに使用時の加工性に優れ、しかも高い電気抵抗と良好な高周波磁気特性を有する無方向性電磁鋼板を提案する。 - 特許庁 - To produce a nonoriented silicon steel sheet having a good boundary form giving remarkable influence on the reduction of core loss and to provide a method for producing the same.
低鉄損化に大きな影響を与える良好な界面形態を有する無方向性電磁鋼板及びその製造方法を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet which has improved high frequency core loss and fatigue characteristics without causing the remarkable embritleness and increase in the hardness thereof.
著しい鋼板の脆化や硬度上昇を伴うこと無く、高周波鉄損と疲労特性を改善した無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet for a high speed rotary motor excellent in the corrosion resistance of sheared edge parts after blanked, and further excellent in strength properties.
打ち抜き後のせん断端部の耐食性に優れ、さらには強度特性にも優れた、高速回転モータ用の無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet minimal in magnetic anisotropy in high frequency region and accordingly excellent in motor characteristic and press workability.
高周波域における磁気異方性が小さく従ってモータ特性に優れ、しかもプレス加工性にも優れた無方向性電磁鋼板を提供する。 - 特許庁 - To provide a technique for stably producing a nonoriented silicon steel sheet excellent in magnetic properties in the longitudinal direction of a coil.
無方向性電磁鋼板の製造に際し、コイル長手方向の磁気特性の優れた無方向性電磁鋼板を安定して製造する技術を提供する。 - 特許庁 - The composition of the nonoriented silicon steel sheet is regulated to a prescribed range.
無方向性電磁鋼板について、その成分組成を所定の範囲に調整すると共に、エプスタイン試験片を用いた磁気特性測定値について、次式(1)〜(4)の関係を満足する。 - 特許庁 - To provide a nonoriented silicon steel sheet which exhibits low core loss in high frequency, and is suitable as electric materials such as core materials used in high frequency.
高周波において低い鉄損を示し、高周波で使用されるコア材等の電機材料として用いるのに適当な無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet having excellent magnetic properties in a frequency region of ≥1 kHz, and further ≥10 kHz, and advantageously suited to a high frequency reactor.
１kHz 以上、さらには10kHz 以上の周波数域で優れた磁気特性を有する高周波リアクトルに有利に適合する、無方向性電磁鋼板について提案する。 - 特許庁 - To provide a method for producing a Cu-containing nonoriented electrical steel sheet having excellent surface properties, high strength and low core loss at high frequency.
本発明は、表面性状に優れ、強度が高く高周波での鉄損の低いＣｕ含有無方向性電磁鋼板の製造方法を提供することを主目的とする。 - 特許庁 - To provide a nonoriented silicon steel sheet having, in a high frequency region, low core loss magnetic flux density in an allowable range, rigidity, durable calking properties and proper hardness.
高周波領域において、鉄損が低くかつ磁束密度が許容範囲であり、しかも、剛性やかしめ性が劣化せず、かつ、硬度が高くなりすぎない無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented electrical steel sheet for a high frequency excited iron core which has excellent iron loss properties, and in which iron loss properties after stress relieving annealing are equal in the circumferential direction of the blanked iron core.
鉄損特性に優れ、かつ、歪取り焼鈍後の鉄損特性が、打ち抜いた鉄芯の円周方向で均等な高周波励磁鉄芯用の無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet having excellent cold rolling properties, a high yield strength and a low core loss in high frequency, and to provide a method for producing the same.
本発明は、冷間圧延性に優れ、降伏強度が高く高周波での鉄損の低い無方向性電磁鋼板およびその製造方法を提供することを主目的とする。 - 特許庁 - The selecting method of the magnetic steel sheet for a motor core uses a nonoriented magnetic steel sheet having a plane anisotropy index S of 0.06 or less for the core.
上記用途の鉄心に、面内異方性指標Ｓが０．０６以下の無方向性電磁鋼板を使用することを特徴としたモーター鉄心用電磁鋼板の選定方法である。 - 特許庁 - To provide a nonoriented silicon steel sheet for a high efficiency motor by which, in a stacking stage for a motor core, fixed motor characteristics can stably be obtained whether staggered stacking is performed or not.
モータコアの積層工程において、回し積みをするとしないとに係わらず、一定のモータ特性を安定して得ることができる高効率モータ用の無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet combinedly having excellent mechanical properties and magnetic properties required as a rotor for a motor rotating at a high speed, and to provide a production method therefor.
本発明は、高速回転するモータの回転子として必要な優れた機械特性と磁気特性とを兼備する無方向性電磁鋼板およびその製造方法を提供することを主目的とする。 - 特許庁 - The nonoriented magnetic steel sheet comprises characteristic components, further comprises 0.003 to 0.01% rare earth metals, >0.0015 to 0.005% Ti, 0.01 to 0.1% Sn, 0.0020 to 0.0050% O, and the balance substantially iron.
特性成分を含有し、ＲＥＭ：０．００３〜０．０１％、Ｔｉ：０．００１５超〜０．００５％、Ｓｎ：０．０１〜０．１％、Ｏ：０．００２０〜０．００５０％を含み、残部は実質的に鉄よりなる。 - 特許庁 - To provide a nonoriented silicon steel sheet combinedly having excellent mechanical properties and magnetic properties required as a rotor for a motor rotating at a high speed, and to provide a production method therefor.
本発明は、高速回転するモータの回転子として必要な優れた機械特性と磁気特性とを兼備する無方向性電磁鋼板およびその製造方法を提供することを主目的とする。 - 特許庁 - A nonoriented polyester film is cast-formed by limiting an electrostatic resistant value (a quantity of an additive metal catalyst) of resin used, and at the same time, setting the position of a die into a range.
使用する樹脂の静電抵抗値（添加する金属触媒量）をある範囲に限定すると同時に、ダイ位置をある範囲内に設定することにより、未延伸ポリエステルフィルムをキャスト製膜する。 - 特許庁 - To provide a method for producing a nonoriented silicon steel sheet having excellent magnetic properties in such a manner that not only magnetic flux density required as that of an iron core material in electrical equipment is particularly high but also core loss is low.
電気機器の鉄心材料として要求される、磁束密度が特に高いばかりでなく鉄損も低い、優れた磁気特性を有する無方向性電磁鋼板の製造方法に関する。 - 特許庁 - The nonoriented silicon steel sheet has a composition comprising ≤0.040% C, 0.05 to 3.5% Si, ≤3.0%
Ｃ：０．０４０％以下、Ｓｉ：０．０５〜３．５％、Ｍｎ：３．０％以下、Ａｌ：３．５％以下、Ｓ：０．０５５％以下、Ｐ：０．２５％以下、Ｎ：０．０４０％以下を含み、（Ｂ_0＋Ｂ_90）／２−Ｂ_45≦０．０４０ を満たす無方向性電磁鋼板。 - 特許庁 - The nonoriented silicon steel sheet has a composition consisting of, by weight, ≤0.005% C, ≤4% Si, 0.05-1.5% Mn, ≤0.2% P, ≤0.02% S, ≤0.005% N, 0.01-1% Al, ≤0.003% O and the balance essentially Fe.
重量％でＣ：0.005％以下、Si：４％以下、Mn：0.05〜1.5％、Ｐ：0.2％以下、Ｓ：0.02％以下、Ｎ：0.005％以下、Al：0.01％〜１％、Ｏ：0.003％以下を含有し、残部が実質的にFeからなる無方向性電磁鋼板。 - 特許庁 - To provide a nonoriented silicon steel sheet in which magnetic properties in the direction of 45° from the rolling direction are particularly excellent, the average of the magnetic properties in the plane is high, and the anisotropy thereof in the plane is extremely reduced, and to provide its production method.
特に圧延方向から４５°方向の磁気特性が優れおり、磁気特性の板面内平均が高く板面内異方性が極めて小さい無方向性電磁鋼板とその製造方法を提供する。 - 特許庁 - To provide a nonoriented electric steel sheet which has crystal grains of small diameter and excellent workability before stress relief annealing, and has crystal grains of a largely grown diameter, and an excellent iron loss property after stress relief annealing, and to provide a method for producing the steel sheet.
歪取焼鈍前に結晶粒径が小さく加工性が良好であり、歪取焼鈍後に結晶粒が大きく成長し鉄損の優れた無方向性電磁鋼板を、及びその製造方法を提供する。 - 特許庁 - To provide an inexpensive and highly productive method for melting a nonoriented silicon steel sheet by which while S inevitably intruded into molten steel is made harmless, an increase in Ti harmful for magnetic properties similarly to S can be suppressed.
溶鋼中に不可避的に混入しているSの無害化を図りながら、Sと同じく磁性に有害なTiの増加を抑制できる低コストで生産性に優れた無方向性電磁鋼板の溶製方法を提供する。 - 特許庁 - To provide a method for producing a nonoriented silicon steel sheet having excellent magnetic properties which have not been obtained heretofore in such a manner that not only magnetic flux density required as that of an iron core material in electrical equipment is particularly high but also core loss is low.
電気機器の鉄心材料として要求される、磁束密度が特に高いばかりでなく鉄損も低い、これまでにない優れた磁気特性を有する無方向性電磁鋼板の製造方法に関する。 - 特許庁 - To provide a nonoriented magnetic steel sheet having excellent magnetic properties which avoids a load on steel making by the reduction of Ti and Sol.Al contents in the steel making, and in which nitriding in stress relieving annealing is suppressed, and the growth of grains at the time of finish annealing and stress relieving annealing is satisfactory.
製鋼でのＴｉ、Ｓｏｌ．Ａｌ量低減の製鋼負荷を回避し、歪取焼鈍で窒化を抑制し、仕上焼鈍、歪取焼鈍時の粒成長の良い磁気特性の優れた無方向性電磁鋼板。 - 特許庁 - To produce a nonoriented silicon steel sheet excellent in mechanical strength property and magnetic property in which high magnetic flux density, low core loss and high strength required for an iron core stock for a reluctance motor, or the like, are combined in high dimensions.
リラクタンスモータ等の鉄心素材に必要とされる、高磁束密度、低鉄損および高強度を高い次元で兼ね備えた機械強度特性および磁気特性に優れた無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet for a semiprocess which contains 0.015 to 0.035% S, and has excellent blanking workability and magnetic properties after magnetic annealing, and to provide a method for industrially and inexpensively producing the steel sheet.
Ｓを０．０１５〜０．０３５％含有した、打抜き加工性および磁性焼鈍後の磁気特性に優れたセミプロセス用無方向性電磁鋼板およびその鋼板を工業的にも安価に製造し得る方法の提供。 - 特許庁 - To provide an adhesive composition which exhibits excellent adhesion even to a film such as a biaxially oriented polypropylene film or a nonoriented polypropylene film, is excellent in workability, and can reduce cost.
二軸延伸ポリプロピレンフィルム／無延伸ポリプロピレンフィルムなどのフィルムに対しても優れた接着性を発揮し、作業性に優れ、工業的にコストダウンを達成することのできる接着剤組成物を提供するものである。 - 特許庁 - To provide a nonoriented magnetic steel sheet having adequate workability due to a small size of crystal grains before stress relief annealing, and having excellent iron loss due to large growth of the crystal grains during the stress relief annealing, and a manufacturing method therefor.
歪取焼鈍前の結晶粒径は小さく加工性が良好であり、歪取焼鈍時に結晶粒が大きく成長することにより鉄損の優れた無方向性電磁鋼板、及びその製造方法を提供する。 - 特許庁 - To provide a method for producing a nonoriented silicon steel sheet by which when a sheet bar formed by rough rolling at the time of hot rolling is joined to a preceding sheet bar, and finish rolling is continuously perform, deterioration in the magnetic properties of the sheet bar joint part is prevented.
熱延時、粗圧延で成形したシートバーを先行するシートバーに接合し、連続して仕上圧延する際に、シーとバー接合部の磁気特性の劣化を防止する無方向性電磁鋼板の製造方法を提供する。 - 特許庁 - To provide a nonoriented electrical steel sheet which has reduced deterioration in core loss even if compressive stress is acted thereon, by which deterioration in core loss caused by assembling of an iron core can be suppressed, and finally, which can contribute to the improvement in the efficiency of a high performance motor or the like.
圧縮応力が作用しても、鉄損の劣化が小さい無方向性電磁鋼板を提供することにより、鉄心組み立てによる鉄損劣化を小さく抑えることができ、最終的に高性能モーターなどの効率向上に寄与する。 - 特許庁 - To provide a method for producing a nonoriented silicon steel sheet uniform in magnetic propertiess in which the joining of sheet bars is executed under the specified temperature condition to effectively suppress the variation of core loss in the vicinity of the sheet bar joint part.
特定の温度条件を満足する温度条件でシートバーの接合を行うことにより、シートバー接合部付近の鉄損の変動を効果的に抑制し得る、磁気特性の均一な無方向性電磁鋼板の製造方法を提供する。 - 特許庁 - To provide a nonoriented silicon steel sheet in which the problem that high electric resistance obtainable by high Si-high Cr incorporation is not sufficiently made the most of is advantageously solved, and which has excellent high frequency magnetic properties in the region of several hundreds to 10 kHz.
高Ｓｉ並びに高Ｃｒ含有によって得られる高い電気抵抗が十分に活用されていない問題を有利に解決し、数百〜１０ｋＨｚ 域での高周波磁気特性に優れた無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented magnetic steel sheet having excellent magnetic properties which avoids a load on steel making by the reduction of a Ti content in the steel making, and in which the time for hot rolled sheet annealing is short, also, nitriding is suppressed, and the growth of grains at the time of finish annealing and stress relieving annealing is satisfactory.
製鋼でのＴｉ量低減の製鋼負荷を回避し、短時間の熱延板焼鈍でかつ窒化を抑制し、仕上焼鈍、歪取焼鈍時の粒成長の良い磁気特性の優れた無方向性電磁鋼板を提供する。 - 特許庁 - To provide a nonoriented electromagnetic steel sheet having excellent surface properties without the need of aging heat treatment, and also, combining excellent mechanical properties and magnetic properties necessary as those of a rotor in a rotating machine rotating at high speed, and to provide its production method.
本発明は、時効熱処理を必要とせず、表面性状に優れ、かつ高速回転する回転機の回転子として必要な優れた機械特性と磁気特性とを兼備する無方向性電磁鋼板およびその製造方法を提供することを主目的とする。 - 特許庁 - To provide a high strength and low core loss nonoriented silicon steel sheet used in a method for constructing a motor core as a motor iron core material for an electric car where a rotor and a stator are blanked from the same steel sheet, so as to be stacked, and further, only the stator is subjected to stress relief annealing.
電気自動車用のモータ鉄心材料として、ロータとステータを同一の鋼板から打ち抜いて積層し、更にステータのみを歪取焼鈍するモータコアの工法に使用される高強度かつ低鉄損の無方向性電磁鋼板を低コストで提供する。 - 特許庁 - The nonoriented magnetic steel sheet has a composition comprising C, Si, Al, Mn, P, S and N in specified ranges, further comprising 0.003 to 0.01% rare earth metals, >0.0015 to 0.005% Ti, 0.01 to 0.1% Sn and 0.0020 to 0.0050% O, and the balance substantially iron.
特定の範囲のＣ、Ｓｉ、Ａｌ、Ｍｎ、Ｐ、Ｓ、Ｎを含有し、さらにＲＥＭ：０．００３〜０．０１％、Ｔｉ：０．００１５超〜０．００５％、Ｓｎ：０．０１〜０．１％、Ｏ：０．００２０〜０．００５０％を含み、残部は実質的に鉄よりなる無方向性電磁鋼板。 - 特許庁 - The nonoriented silicon steel sheet excellent in corrosion resistance and high frequency magnetic properties has a composition consisting of 2.5-10 mass % Si, 1.5-20 mass % Cr, C and N in amounts reduced to ≤0.0010 mass % and ≤0.0050 mass %, respectively, and the balance Fe with inevitable impurities.
Siが2.5 〜10mass％及びCrが1.5 〜20mass％を含有し、かつ、Ｃ及びＮをそれぞれ0.0010mass％以下及び0.0050mass％以下に低減し、残部がFe及び不可避的不純物からなることを特徴とする耐食性及び高周波磁気特性に優れる無方向性電磁鋼板。 - 特許庁
- 特許庁