＜前へ 1 2- The plastic substrate 1 contains at least one of polyolefins, polyamides, polyimides, polyesters, polycarbonates, polyacrylonitrile, polystyrene, polyvinyl chloride, cellulose, triacetyl cellulose, polyvinyl alcohol and polyurethanes, among which the polymers may be copolymers and/or chemically modified products.
プラスチック基材１は、ポリオレフィン、ポリアミド類、ポリイミド類、ポリエステル類、ポリカーボネート、ポリアクリロニトリル、ポリスチレン、ポリ塩化ビニル、セルロース、トリアセチルセルロース、ポリビニルアルコール、ポリウレタン類（ただし、前記ポリマー類は共重合体および／または化学修飾体であってもよい）のいずれか１種類以上を含む。 - 特許庁 - This finishing lubricant for elastic fibers is such as to contain 0.5-10 wt.% of a stabilizer capable of preventing the elastic fibers from discoloration and/or getting brittle due to UV or light such as a ultraviolet light absorber, hindered amine-based stabilizer, lactone-based stabilizer or hindered phenol- based antioxidant each highly compatible with polyurethanes.
ポリウレタンに対して相溶性の高い紫外線吸収剤、ヒンダードアミン系安定剤、ラクトン系安定剤、ヒンダードフェノール系酸化防止剤などＵＶや光による着色や脆化を防止する安定剤を０．５〜１０重量％含有する弾性繊維用仕上げ油剤。 - 特許庁 - The composition is useful as a refrigerant, cleaning agent, expansion agent for polyolefins and polyurethanes, refrigerant, aerosol propellant, heat transfer medium, gaseous dielectric, fire extinguishing agent, power cycle working fluid, polymerization medium, particulate removal fluid, carrier fluid, buffing abrasive agent and displacement drying agent.
該組成物は、冷媒、洗浄剤、ポリオレフィン類およびポリウレタン類用発泡剤、冷媒、エーロゾル噴射剤、熱伝達媒体、気体状誘電体、消火剤、パワーサイクル作動油、重合媒体、粒子除去用流体、担体流体、バフ研磨剤および置換乾燥剤として有効性を示す。 - 特許庁 - To provide a compsn. excellent in elongation at a low stress and adhesiveness with a substrate, and having small residual strain and high recovery stress after elongation, by compounding thermoplastic polyurethanes each contg. a polymer polyol unit or a polyether polyol unit and having a specified nitrogen atom content and crystallization enthalpy.
Ｔ−ダイ型押出機などで溶融押出成形する際に生じるネックイン現象や、インフレーション成形機で溶融成形する際に生じる厚み斑や割れをさらに改善し、基材との接着性に優れたフィルムやシートなどの成形品を、高生産性で製造することができる熱可塑性ポリウレタンを提供する。 - 特許庁 - To provide a urethane polyol composition which has good workability on a urethanization operation, because of being liquid at the ordinary temperature and having a low viscosity, and can give polyurethanes having good flexibility and stretchability under a low temperature condition and having good heat resistance, and to provide a polyurethane composition using the urethane polyol composition.
常温で液状であることはもとより粘度が低いのでウレタン化操作に際しての作業性が良好である上、低温条件下においても柔軟で伸びが良好でありかつ耐熱性も良好であるポリウレタンを与えることのできるウレタンポリオール組成物を提供すること、およびそのようなウレタンポリオール組成物を用いたポリウレタン組成物を提供することを目的とする。 - 特許庁 - The aqueous dispersion of the fluorine-containing polymer comprises the fluorine-containing polymer, at least one species of polymers selected from a group consisting of styrene-butadiene-based copolymers, acrylonitrile-butadiene-based copolymers, acrylic copolymers, polyurethanes and fluorine-based rubbers and a polyoxyethylene alkyl ether-based surfactant having ≤1.15 polydispersity (the value obtained by dividing the weight average molecular weight Mw by number average molecular weight Mn).
含フッ素重合体と、スチレン−ブタジエン系共重合体、アクリロニトリル−ブタジエン系共重合体、アクリルコポリマー、ポリウレタンおよびフッ素系ゴムからなる群から選ばれた少なくとも１種の重合体と、多分散度（重量平均分子量Ｍｗを数平均分子量Ｍｎで割った値）が１．１５以下であるポリオキシエチレンアルキルエーテル系界面活性剤とを含む含フッ素重合体水性分散液。 - 特許庁 - The surface of the material has a portion selected from the group consisting of polyamides, polyureas, polyhydrazides and polyurethanes which individually comprise a functional group selected from the group consisting of a functional amine group, functional amine and hydrazine groups, functional hydrazine group and functional amine group in an amount sufficient to impart a microorganism-resistant activity to the surface and thus exhibit intrinsic microorganism-resistant properties.
材料表面がこの表面に抗微生物活性を与えるに充分な量の官能基アミン基、官能基アミン基およびヒドラジン基、官能基ヒドラジン基、ならびに官能基アミン基からなる群より選ばれる官能基を、それぞれ含んでなる固有の抗微生物性を示す、ポリアミド、ポリ尿素、ポリヒドラジド、ならびにポリウレタンからなる群より選ばれる部分 - 特許庁 - The manufacturing process of a phenol resin comprises adding and reacting an organic inorganic composite (3) composed of at least one inorganic compound (1) selected from among the group consisting of silicon oxides, metal oxides, metal hyroxides and metal carbonates, and at least one organic polymer (2) selected from among polyamides, polyurethanes and polyureas, when an aldehyde and phenol are catalytically reacted.
アルデヒド類とフェノール類とを触媒下反応させる際に、酸化ケイ素類、金属酸化物類、金属水酸化物類、及び、金属炭酸化物類からなる群から選ばれる少なくとも一種の無機化合物（１）と、ポリアミド、ポリウレタン、及び、ポリ尿素から選ばれる少なくとも一種の有機ポリマー（２）と、から成る有機無機複合体（３）を、添加反応させることを特徴とするフェノール樹脂の製造方法。 - 特許庁 - To obtain a safe and highly functional polyurethane improved in stability to heat during processing and stability to hydrolysis during use, while keeping its favorable characteristics and functionality which is a favorable material from the view point that functional polyurethanes are easy in hardness control and good in biocompatibility, but have problems in sterilizing treatment, the decrease in strength by hydrolysis during use in living bodies, and the generation of elusion materials in the conventional technology.
硬度調整の容易さ、良好な生体適合性などの観点から好ましい材料でありながら、従来の技術においては滅菌処理や生体内での使用の際に加水分解反応などによる強度低下や溶出物の生成が問題となっていた機能性ポリウレタン類について、好ましい特性と機能性を維持し、且つ加工時の熱に対する安定性や使用時の加水分解に対する安定性が改善された安全性の高い機能性ポリウレタン類を提供する。 - 特許庁
- 特許庁