「nm」を含む例文一覧(14378)
＜前へ 1 2 .... 181 182 183 184 185 186 187 188 189 .... 287 288 次へ＞- The silica porous film having fine pore diameters of 10 to 40 nm is obtained by coating a mixed liquid composed of a polysilazane, a resin such as an acrylic resin and a solvent such as xylene on a ceramic substrate and then subjecting the coated substrate to heat treatment at a temperature of ≤450°C.
セラミック基板上にポリシラザン、アクリルなどの樹脂及びキシレン等を溶媒とする混合液を塗布し、４５０℃以下の熱処理をすることにより、１０〜４０ｎｍの大きさの細孔径を有するシリカ多孔膜を作る。 - 特許庁 - An external oxidation type oxide film having 2 to 500 nm film thickness and ≤30% proportion of a low density layer and composed essentially of silica is formed between the tension-imparting insulation film and the finish- annealed grain-oriented silicon steel sheet.
張力付与性絶縁皮膜と仕上げ焼鈍済みの一方向性珪素鋼板との間に膜厚２ｎｍ以上５００ｎｍ以下で密度低下層比率３０％以下のシリカを主体とする外部酸化型酸化膜を形成させる。 - 特許庁 - The organic light emitting display element has a transparent moisture absorption film containing a metal oxide and/or metal salt with a grain size of 100 nm or smaller, a binder, and a transparent light absorbing material absorbing the light of a specific area.
平均粒径が１００ｎｍ以下の金属酸化物及び／または金属塩、バインダー及び特定領域の光を吸収する選択的吸光物質を含有する透明吸湿膜を備えた有機発光表示素子である。 - 特許庁 - The colored resin film 2 has semitransparency in succinic color (auburn), grey color or colors similar to these colors and light transmissiveness of 15-55% in the range of 380-800 nm in wavelength by dispersion of a dye into the resin film.
樹脂フィルム中に染料を分散させて、琥珀色（アーバン）、グレー色、またはこれらに類似する色の半透明、あるいは波長が３８０〜８００ｎｍの範囲にある光の透過率を１５〜５５％の着色樹脂フィルム２とした。 - 特許庁 - The pathogenic microorganism sterilization method is provided in which a composition containing an oxidizing agent is brought into contact with an object and the object is irradiated with light beams including light having a single or a plurality of wavelengths within the range of 400-1,000 nm.
酸化剤含む組成物を対象物に接触させ、４００ｎｍ〜１０００ｎｍの範囲における単一又は複数の波長を有する光を含む光線を該対象物に照射する病原性微生物の殺滅方法。 - 特許庁 - Especially, the optical waveguide is provided by using a polyimide having (a) ≤1 dB/cm transmission loss, (b) ≥1.55 refractive indices of both in TE mode and TM mode and (c) ≤0.02 birefringence index, at 830 nm wavelength as the core material.
特に波長８３０ｎｍにおける（ａ）伝送損失が１ｄＢ／ｃｍ以下、（ｂ）屈折率がＴＥモード、ＴＭモードともに１．５５以上、（ｃ）複屈折率が０．０２以下であるポリイミドをコア材料に用いた光導波路。 - 特許庁 - Fine particle formation requires suitable conditions, and when arc discharge is caused in a reactive gas comprising 20-40 kPa of helium and 0-20 kPa of the air, no CNT grows and a spherical material of several hundred nm to several μm is formed.
微粒子生成には好適な条件があり、ヘリウム２０〜４０ｋＰａ、大気０〜２０ｋＰａの反応ガスでアーク放電させると、ＣＮＴは成長せず、数百ｎｍから数μｍまでの球状物質が形成される。 - 特許庁 - In the method for producing a planographic printing plate, the photosensitive layer of the photosensitive planographic printing plate is imagewise exposed with active light of ≥700 nm wavelength and the exposed parts are dissolved in an alkaline developing solution and removed.
また、平版印刷版の作成方法では、上記の感光性平版印刷版の感光層を、波長７００ｎｍ以上の活性光線によって画像露光した後、露光した部分をアルカリ性現像液で溶解して除去する。 - 特許庁 - More specifically, the primary particles of the oxide-ceramic materials have an average particle size in the range from 10 to 1,000 nm and are coated with the coloring components.
より具体的には、酸化物−セラミック材料の一次粒子であって、該一次粒子は、１０ｎｍ〜１０００ｎｍの範囲の平均粒子径を有し、発色成分でコーティングされている、一次粒子を提供することにより達成される。 - 特許庁 - The sintered compact essentially consisting of the copper is high in the reflectivity of the laser beam of a wavelength band including 780 nm and is therefore suitable for use as the rotary polyhedral mirror for an optical deflector such as a laser printer mounted with a laser beam source.
また、銅を主成分とする焼結合体は７８０ｎｍを含む波長帯域のレーザビームの反射率が高いので、レーザ光源が搭載されたレーザプリンタ等の光偏向器用の回転多面鏡として用いるのに適している。 - 特許庁 - The oxide particle dispersion liquid obtained is composed of oxide particles of a cubic or rectangular parallelepiped form whose one side is 5-150 nm, all or a part of the oxide particles being chipped of at least one part of their corners.
得られた酸化物粒子分散液は、一辺が５〜１５０ｎｍの立方体もしくは直方体形状を有する酸化物粒子と分散媒からなり、前記酸化物粒子の全部又は一部は角の少なくとも一部が欠けている。 - 特許庁 - The optical polyester film comprises a base material film, a 5-100 nm thick binder layer applied on the base material sheet, and a convex lens-like particle having an average particle diameter of 5-100 μm and carried on the base material film by the binder layer.
基材フィルム、その上に塗設された厚み５〜１００ｎｍのバインダー層および該バインダー層により基材フィルム上に担持された平均粒径５〜１００μｍの凸レンズ状粒子からなることを特徴とする、光学用ポリエステルフィルム。 - 特許庁 - The reference layer has such a structure as more than one CoPt layer containing Pt by 20-50 atom% and having a film thickness of 1-5 nm is laminated with an Ru layer interposed therebetween.
参照層は、２０原子％以上５０原子％以下のＰｔを含有し、１ｎｍ以上５ｎｍ以下の膜厚を有する、少なくとも２以上のＣｏＰｔ層が、Ｒｕ層を介して積層された構造を有するものとする。 - 特許庁 - In this case, the number of the nitrogen compounds with a grain size of 10 to 200 nm in the region within 3 μm to the sheet thickness direction from the sheet surface is controlled to ≥2 times compared with the number of nitrogen compounds with the above size in the central part of the sheet thickness.
その場合、板表面から板厚方向３μm以内の領域における粒径10nm以上200nm以下の窒素化合物の個数が、板厚中心部の前記大きさの窒素化合物の個数に比較して、２倍以上とする。 - 特許庁 - Preferably, the arithmetic mean roughness (Ra) of the surface of the ceramic green sheet for obtaining the layer 2 be set at a roughness of lower than 100 nm and that the electrodes 8 and 9 be constituted of a metal film formed through a thin-film forming method.
好ましくは、セラミック層２を得るためのセラミックグリーンシートの表面の算術平均粗さ（Ｒａ）を１００ｎｍ以下とし、内部電極８，９を薄膜形成法によって形成された金属膜をもって構成する。 - 特許庁 - In the optical member for photolithography used in a specified wavelength band lower than 400 nm, the rotationally asymmetric component of wavefront aberration of the optical member has RMS value of 0.0040 λor less in the direction of the optical axis.
４００ｎｍ以下の特定波長帯域で使用される光リソグラフィー用光学部材において、光学部材の波面収差のうち光軸方向の非回転対称成分のＲＭＳ値が０．００４０λ以下であることを特徴とする。 - 特許庁 - The dominant wavelength of the first light is set, so that the absolute value of the gradient (ΔK/Δλ) of the curve which represents the wavelength dependency of the internal quantum efficiency of a phosphor may be included in the wavelength range which becomes 1%/nm or more.
蛍光体の内部量子効率の波長依存性を示す曲線の勾配（ΔＫ／Δλ）の絶対値が１［％／ｎｍ］以上となる波長範囲に含まれるように第１の光の主波長が設定されている。 - 特許庁 - The chalcopyrite type fine particles have a group Ib metal element, a group IIIb metal element, and a group VIb element and have an average crystallite diameter of 2-20 nm and a single crystal particle rate of 80% or more.
また、第Ｉｂ族金属元素、第ＩＩＩｂ族金属元素、及び第ＶＩｂ族元素を有し、平均結晶子径が２ｎｍ〜２０ｎｍであり、且つ単結晶粒子の割合が８０％以上である、カルコパイライト系微粒子とする。 - 特許庁 - To provide an organic electroluminescent element of which an upper electrode is made of a metal film and moreover capable of thinning the thickness of the metal film down to 6 nm or less while maintaining conductivity of the film, and a display device equipped with the film.
上部電極を金属膜により構成すると共に、この金属膜の導電性を保ちつつ厚みを６ｎｍ以下に薄くすることが可能な有機エレクトロルミネッセンス素子およびこれを備えた表示装置を提供する。 - 特許庁 - The bleaching agent composition includes: a nano-cellulose fiber (a) having an average fiber diameter of 1 to 1,000 nm; at least one kind compound (b) selected from among hydrogen peroxide and compounds releasing hydrogen peroxide in water; and a surfactant (c).
（ａ）平均繊維径１〜１，０００ｎｍのナノセルロースファイバー、（ｂ）過酸化水素及び水中で過酸化水素を放出する化合物から選ばれる１種以上の化合物、並びに（ｃ）界面活性剤を含有する漂白剤組成物。 - 特許庁 - An embodiment in which the liposome has a volume-average dispersion particle diameter of 20 nm-20 μm and an embodiment in which the gas is at least one kind selected from oxygen, nitrogen, carbon dioxide, xenon, krypton, argon, a hydrofluorocarbon and a perfluorocarbon are preferable.
体積平均分散粒径が、２０ｎｍ〜２０μｍである態様、気体が、酸素、窒素、二酸化炭素、キセノン、クリプトン、アルゴン、ハイドロフルオロカーボン類、及びパーフルオロカーボン類から選択される少なくとも１種である態様などが好ましい。 - 特許庁 - The low refractive index composition satisfying the problem can be provided by using a borazine-based polymer or a borazine-silicon based polymer as a matrix and including 1-90 wt.% of magnesium fluoride having a particle diameter of ≤50 nm.
ボラジン系ポリマー又はボラジン珪素系ポリマーを母材とし、粒子径が５０ｎｍ以下のフッ化マグネシウムが１乃至９０重量％含まれる事により上記課題を解決した低屈折率組成物が提供可能となる。 - 特許庁 - Less than 100 pts.wt. of phenolic resin is added to 100 pts.wt. of acrylonitrile-butadiene rubber (NBR) with an acrylonitrile content of 31% or more to homogeneously disperse the phenolic resin with a particle diameter of 1-100 nm in the NBR.
アクリロニトリル含有量３１％以上のアクリロニトリルブタジエンゴム（ＮＢＲ）１００重量部に対してフェノール樹脂１００重量部未満を添加し、ＮＢＲ中にフェノール樹脂を粒径１〜１００ｎｍで均一に分散させた。 - 特許庁 - To provide an aromatic polycarbonate resin composition for inorganic physical expansion molding capable of obtaining a fine foamed article having fine and uniform bubbles having, for example, an average cell diameter of 1,000 nm or less, and a foamed article thereof.
例えば平均気泡径が１０００ｎｍ以下の微細でかつ均一な気泡を有する微細発泡体を得ることができる無機系物理発泡成形用芳香族ポリカーボネート樹脂組成物およびその発泡体の提供。 - 特許庁 - To reduce the cost of an optical transmitter module used for a head cymbal assembly of an information recording device, and to provide optical coupling between optical devices in a near-infrared wavelength of 600 to 900 nm without using advanced aligning equipment.
情報記録装置のヘッドシンバルアセンブリに用いる光伝送モジュールの低コスト化を目的とし、６００ｎｍ以上、９００ｎｍ以下の近赤外波長にて光デバイス間の光接続を高度な調芯設備を用いず実現する。 - 特許庁 - The low reflection member has a transparent substrate and a low reflection film formed on the transparent substrate and the low reflection film is a hydrophilic low reflection material containing magnesium fluoride hydroxide ultrafine particle having 5-500 nm particle diameter.
透明基板と、該透明基板上に形成される低反射膜を有する低反射部材であって、該低反射膜が、粒子径５〜５００ｎｍの水酸化フッ化マグネシウム超微粒子を含むことを特徴とする親水性低反射材料。 - 特許庁 - The crop growing system 1 set within a field 2 includes: an ultraviolet lamp 4 for irradiating crops with ultraviolet rays with the wavelength peak in the wavelength range of 300-380 nm; and a control distribution board 5 for controlling the irradiation of the lamp 4.
作物育成システム１は、圃場２内に設置され、波長域３００〜３８０ｎｍに波長ピークを持つ紫外線を照射する紫外線ランプ４と、ランプ４の照射動作を制御する制御配電盤５とを備える。 - 特許庁 - The composite is obtained by regulating a compounded latex obtained by mixing a dispersion of particulate silica having ≤100 nm of average particle diameter with a styrene-butadiene rubber latex so as to have pH 5-9 by adding an acid or an alkali, and drying the resultant product.
スチレンブタジエンゴムラテックスと平均粒子径１００ｎｍ以下の微粒子シリカの分散液とを混合した配合ラテックスに酸又はアルカリを添加してｐＨ５〜９に調整した後、乾燥することにより得られる複合体に関する。 - 特許庁 - Especially preferably, this organic compound, as it is or in a solution state, has an absorption maximum in the region with a wavelength of 200-700 nm, and the molar absorptivity in this absorption is 100 or more.
この有機化合物はそのままの状態、又は溶液状態で、特に好ましくは、波長２００〜７００ｎｍの領域に吸収極大を有し、そのモル吸光係数が１００以上の吸収を有する化合物である。 - 特許庁 - The titanium oxide structure is of a rod, tube, or fiber type and made of fine titanium oxide particles having an average particle diameter of 1-100 nm, at least 30% of the fine titanium oxide particles being titanium oxide having crystalline morphology of Magneli phase.
平均粒子径が１〜１００ｎｍの酸化チタン微粒子からなり、前記酸化チタン微粒子の３０％以上が、マグネリ相構造の結晶形態を有する酸化チタンである、棒状、管状又は繊維状の酸化チタン構造体。 - 特許庁 - The resin structure for the mirror frame is obtained by molding a composite resin composition made of a resin containing a cellulose nanofiber having an aspect ratio of 10-1,000,000 and an average diameter of 1-800 nm.
本発明の鏡枠用樹脂構造体は、アスペクト比が１０〜１００００００であり、平均直径が１〜８００ｎｍであるセルロースナノファイバーを樹脂中に含有してなる複合樹脂組成物を、成形してなることを特徴とする。 - 特許庁 - In the biaxially oriented polyarylene sulfide film, wherein carbon black is contained in a thermoplastic resin including a polyarylene sulfide, the carbon black is dispersed at a mean dispersion diameter of 50-900 nm in the film.
ポリアリーレンスルフィドを含む熱可塑性樹脂にカーボンブラックを含有したフィルムであって、該フィルム中にカーボンブラックが平均分散径５０〜９００ｎｍで分散していることを特徴とする二軸配向ポリアリーレンスルフィドフィルムであることを骨子とする。 - 特許庁 - The alloy catalyst for an oxidation-reduction reaction includes the alloy particles of platinum and nickel, the alloy particles having crystalline lattice surfaces of Miller index of {111} on their external surfaces and an average particle size of 6-20 nm.
酸化還元反応用合金触媒は、白金と、ニッケルとの合金粒子からなるものであって、該合金粒子が外表面にミラー指数｛１１１｝の結晶格子面を備えるとともに、６〜２０ｎｍの範囲の平均粒子径を備える。 - 特許庁 - The first spectral distribution has a peak at a wavelength λ, the transmission material 4 contains particulates having a particulate diameter d, and the particulates have a particulate diameter parameter of ≤0.5 defined by πd/λ and the particulate diameter d of ≤100 nm.
第１の分光分布は、波長λにおいてピークを有し、透過材４は、粒子径ｄの微粒子を含有し、この微粒子は、πｄ／λにより規定される粒径パラメータを０．５以下、又は粒子径ｄを１００ｎｍ以下とした。 - 特許庁 - The toner contains phosphorescent pigment particles having sizes of 5 to 50 μm, and a resin coating on at least a part of the phosphorescent pigment surface where the phosphorescent pigment shows an excitation wavelength of 200 to 750 nm.
５ミクロン〜５０ミクロンのサイズを有する燐光顔料粒子と、前記燐光顔料の表面の少なくとも一部の上の樹脂コーティングと、を含み、前記燐光顔料の励起波長が２００ｎｍ〜７５０ｎｍである、トナーを提供する。 - 特許庁 - The exhaust gas purifying catalyst comprises an oxide support having a pore and noble metal particles carried by the oxide support, wherein the average particle size of the noble metal particle is less than 10 nm and larger than the average pore diameter of the oxide support.
細孔を有する酸化物担体に貴金属粒子を担持させてなり、貴金属粒子の平均粒子径が１０ｎｍ未満であって且つ酸化物担体の平均細孔径よりも大きいことを特徴とする排ガス浄化触媒。 - 特許庁 - The metal-compounded organic resin particles include the metal, metal oxide, or metal salt in pores of porous organic resin particles, wherein the porous organic resin particles have a ≤300 nm mean pore diameter.
金属、金属酸化物又は金属塩を多孔質有機樹脂粒子の細孔内に有する金属複合有機樹脂粒子であって、前記多孔質有機樹脂粒子は、平均細孔径が３００ｎｍ以下である金属複合有機樹脂粒子。 - 特許庁 - The ultrathin boron nitride nanosheet having a thickness of ≤10 nm is obtained by applying an ultrasonic treatment to a dispersion liquid prepared by dispersing the powders of hexagonal boron nitride into an organic solvent and then applying a centrifugal operation.
この超薄窒化ホウ素シートは、六方晶系窒化ホウ素粉末を有機溶媒に分散させた分散液に超音波処理を施した後、遠心分離操作を施すことにより、１０ｎｍ以下の超薄窒化ホウ素ナノシートとすることができる。 - 特許庁 - The hydrophobic zirconium oxide particle has a silica coating layer having a trialkylsilyl group bonded to the surface of the zirconium oxide particle, and an average particle diameter of 5-30 nm and a refractive index of 1.58-2.0.
疎水性酸化ジルコニウム粒子は、酸化ジルコニウム粒子の表面に、トリアルキルシリル基が結合したシリカ被覆層を有し、平均粒子径が５〜３０ｎｍの範囲にあり、屈折率が１．５８〜２．０の範囲にあることを特徴とする。 - 特許庁 - By constituting the contents of the copper, sulfur and iron in the glass in this way, the copper ruby glass exhibiting satisfactory red with the main wavelength (λd) of 593 to 625 nm can be produced with excellent reproducibility without performing the reheating treatment.
ガラス中の銅、硫黄、鉄の量をこのように構成することで、主波長（λｄ）が５９３〜６２５ｎｍの良好な赤色を呈する銅赤ガラスを、再加熱処理を行うことなく、優れた再現性をもって製造できる。 - 特許庁 - The ink composition comprises: initiator particles which include a water-insoluble polymerization initiator and a water-soluble polymer and have a volume-average particle size of 500 nm or less; a water-soluble polymerizable compound; a pigment; and water.
インク組成物を、水不溶性重合開始剤および水溶性ポリマーを含むとともに体積平均粒子径が５００ｎｍ以下である開始剤粒子と、水溶性重合性化合物と、顔料と、水と、を含んで構成する。 - 特許庁 - The composition keeps fluorescence efficiency of the dye molecules, does not aggregate in a solution, forms starburst dendrimer, can absorb or emit light in near infrared region (longer than 800 nm) and may be supposed to be tissue specific.
本発明組成物は、染料分子の蛍光効率を保ち、溶液中では凝集せず、スターバストデンドリマーを形成し、近赤外線領域(８００ｎｍを越える)での光線を吸収または放射し得、そして組織特異的とされ得る。 - 特許庁 - The method for producing the gene transfer agent by a photo-living polymerization in a solution is characterized by making to exist a light-emitting compound which is decomposed in the solution to emit light having a peak wavelength of 360 to 375 nm.
溶液中での光リビング重合により遺伝子導入剤を製造する方法において、該溶液中に、分解することによりピーク波長３６０〜３７５ｎｍの光を放出する光放出性化合物を存在させる。 - 特許庁 - The polymer of the ethylenic unsaturated monomer (b) constituting the graft copolymer is a crosslinked product in which a number average dispersed particle diameter is 100-1,000 nm and standard deviation relative to the average dispersed particle diameter is 5-20%.
前記グラフト共重合体を構成するエチレン性不飽和単量体（ｂ）の重合体は、その数平均粒径が１００〜１０００ｎｍで数平均粒径に対する標準偏差が５〜２０％で分散した架橋体である。 - 特許庁 - To provide a plasma light source and a plasma light generating method that achieve higher output of EUV light by substantially shortening an emission cooling time of excitation level at which EUV light in an effective wavelength region (nearby 13.5 nm) is emitted.
有効波長領域（１３．５ｎｍ近傍）のＥＵＶ光を発する励起準位の輻射冷却時間を実質的に短縮し、ＥＵＶ光の高出力化を達成できるプラズマ光源とプラズマ光発生方法を提供する。 - 特許庁 - To provide a method for efficiently producing microfibrous cellulose by which the microfibrous cellulose having a low value of YI (yellowing index) and the maximum fiber width of ≤1,000 nm is efficiently produced by a simple method.
本発明は、微細繊維状セルロースを効率よく製造する方法であり、低ＹＩ値でかつ最大繊維幅１０００ｎｍ以下の微細繊維状セルロースを簡便な方法により効率的に製造する方法を提供する。 - 特許庁 - The base cloth for air bag is the fabric of synthetic fiber consisting of warp and weft of multifilament whose single fiber fineness is 1-2 dtex and silicon dioxide having an average particle size of 10-50 nm adheres to the fabric.
合成繊維からなり単繊維繊度が１〜２ｄｔｅｘであるマルチフィラメントをタテ糸およびヨコ糸として構成された織物であり、該織物に平均粒子径１０〜５０ｎｍの二酸化ケイ素が付着しているエアバッグ用基布。 - 特許庁 - If light generated by the blue LED 42, that is, light having a peak of its intensity at a wavelength of 464 nm or so strikes on the sleeping person, melatonin secretion in the brain of the sleeping person is suppressed, and the sleeping person is easily wakes up.
青色ＬＥＤ（42）が発生させる光、即ち波長４６４ｎｍ前後に強度のピークを持つ光が就寝者に当たると、就寝者の脳内におけるメラトニン分泌が抑制され、就寝者が覚醒しやすくなる。 - 特許庁 - In addition, a p-side electrode is arranged on the surface of the second layer, electrically connected with the second layer, formed with one metal selected from a group composed of Pt, Rh and Pd, and includes a thickness of 1-8 nm.
ｐ側電極が第２の層の表面上に配置され、第２の層に電気的に接続され、Ｐｔ、Ｒｈ及びＰｄからなる群より選択された１つの金属で形成されており、その厚さが１ｎｍ〜８ｎｍである。 - 特許庁 - An electron emission device is manufactured by forming a semiconductor film having a thickness of 50 nm or less and an electron affinity of 4.0 eV or less on a metallic or semiconductor substrate having a spinto type cold cathode, a carbon nano-tube, a carbon nano-fiber and unevenness.
スピント型冷陰極やカーボンナノチューブやカーボンナノファイバおよび凹凸を有する金属や半導体基板に厚さ５０ｎｍ以下の電子親和力４．０ｅＶ以下の半導体膜を設けて電子放出装置を作製する。 - 特許庁
- 特許庁