The ceramic block is constituted so that porcelainized aggregates having ≤2 mm maximum particle size are integrated by a porcelainized firing binder and the ceramic block has 40-80 wt.% aggregates and 20-60 wt.% firing binder, ≤4% water absorptivity and ≥16 MPa bending strength.例文帳に追加

本発明のセラミックブロックは、最大粒径が２mm以下である磁器質の骨材を、磁器質化した焼結バインダーで一体化して構成されたセラミックブロックであって、該骨材の含有量が４０〜８０重量％、該焼結バインダーの含有量が２０〜６０重量％であり、吸水率が４％以下、曲げ強度が１６ＭＰａ以上であることを特徴とするものである。 - 特許庁

The production method of the ceramic block comprises pulverizing the porcelainized aggregated and classifying them to obtain powdery aggregates having 2 mm maximum particle size, further classifying them into coarser aggregates and finer aggregates, mixing and kneading the coarser aggregates with water, mixing and kneading the kneaded coarser aggregates with the finer aggregates and a plastic firing binder, press forming the kneaded mixture and firing the formed body to porcelainize the firing binder.例文帳に追加

本発明のセラミックブロックの製造方法は、磁器質化した骨材を粉砕、分級して、最大粒径が２mmの粒状骨材にし、これを、さらに分級して、粗粒骨材と細粒骨材とに分け、まず、該粗粒骨材を水に混合して混練し、そこへ該細粒骨材と可塑性焼結バインダーとを混合して混練した後、この混合物をプレス成形して、この成型体を焼成し、該焼結バインダーを磁器質化させることを特徴とするものである。 - 特許庁