貯蔵弾性率の英語

この際、接着時の加熱温度において、導電粒子２の貯蔵弾性率がバインダー樹脂３の貯蔵弾性率よりも高く、かつ、バインダー樹脂３の貯蔵弾性率の１０．０倍以下である。例文帳に追加

At this time, in the heating temperature at the time of adhesion, storage elastic modulus of the conductive particles 2 is higher than that of the binder resin 3, and 10.0 times or less of the storage elastic modulus of the binder resin 3. - 特許庁

貼付け硬化前の２５℃の貯蔵弾性率が１×１０^5 Ｐａ以上、８０℃の貯蔵弾性率が５×１０^4 Ｐａ以下で、貼付け硬化後の８０℃の貯蔵弾性率が１×１０^5 Ｐａ以上の性能を有する。例文帳に追加

This filmlike adhesive has performances of ≥1×105 Pa storage modulus at 25°C prior to laminating and curing, ≤5×104 Pa storage modulus at 80°C and ≥1×105 Pa storage modulus at 80°C after the laminating and curing. - 特許庁

Ｅ_0’_35／Ｅ_0’_290 ≦ ８ 但し、Ｅ_0’_35 ：動的粘弾性測定における３５℃でのシリコーン系硬化性樹脂の貯蔵弾性率、Ｅ_0’_290：動的粘弾性測定における２９０℃でのシリコーン系硬化性樹脂の貯蔵弾性率例文帳に追加

In the formula, E_0'_35 is the storage elastic modulus of the curable silicone resin measured at 35°C by dynamic viscoelasticity measurement and E_0'_290 is the storage elastic modulus of the curable silicone resin measured at 290°C by dynamic viscoelasticity measurement. - 特許庁

粘弾性カーブにおいて140℃から180℃の範囲における貯蔵弾性率又は粘度の最小値と200℃における貯蔵弾性率または粘度差を特定したトナーを用いる。例文帳に追加

In this toner, the difference between the minimum of the storage elastic modulus or viscosity in the range from 140°C to 180°C and the storage elastic modulus or viscosity at 200°C in the viscoelasticity curve is specified. - 特許庁

第２の感圧接着層３は、測定温度20℃の貯蔵弾性率Ｇ'(１Hz）が１×10^4 〜５×10^6 Ｐａで、基準温度20℃の貯蔵弾性率Ｇ'(10^-7Hz）が１×10^4 〜１×10^6 Ｐａの粘弾性特性を有する感圧接着剤で構成されている。例文帳に追加

The second pressure sensitive adhesive layer 3 is formed with a pressure sensitive adhesive having a viscoelastic character of a storage elasticity G' (1 Hz) of 1x104-5x106 Pa at the measuring temperature of 20°C and a storage elasticity G' (10-7 Hz) of 1x104-1x106 Pa at the standard temperature of 20°C. - 特許庁

接着剤層の硬化物およびコア材の動的粘弾性測定装置で測定される２５℃の貯蔵弾性率が１０〜２０００ＭＰａかつ２６０℃での貯蔵弾性率が３〜５０ＭＰａであることが好ましい。例文帳に追加

It is preferred that the storage elastic moduli at 25°C, measured by dynamic viscoelasticity measuring equipment, of the cured product of the adhesive layers and the core material are 10-2,000 MPa and, simultaneously, those at 260°C are 3-50 MPa. - 特許庁

貯蔵弾性率の低下温度が異なる２種以上のポリイミド繊維からなる繊維集合体例文帳に追加

FIBER AGGREGATE COMPOSED OF TWO OR MORE KINDS OF POLYIMIDE FIBERS HAVING DIFFERENT TEMPERATURE FOR LOWERING STORAGE ELASTIC MODULUS - 特許庁

柔軟層の３２℃における貯蔵弾性率は、５．０×１０^３〜１．６×１０^６Ｐａである。例文帳に追加

The storage elastic modulus of the soft layer 2 at 32°C is 5.0×10^3 to 1.6×10^6 Pa. - 特許庁