This prepreg obtained by impregnating a substrate with an epoxy resin composition containing (A) an epoxy resin, (B) a curing agent, (C) a curing accelerator and (D) organic short fibers having ≤500 nm mean fiber diameter, and semi-curing is used.例文帳に追加

エポキシ樹脂（Ａ）、硬化剤（Ｂ）、硬化促進剤（Ｃ）、及び平均繊維径５００ｎｍ以下の有機短繊維（Ｄ）を含有するエポキシ樹脂組成物を基材に含浸し、半硬化させて得られることを特徴とするプリプレグを用いる。 - 特許庁

The method for the spray construction of a quick setting spray cement concrete S comprises adding an accelerator to a spray cement concrete containing the fibers and then adding the setting retarder to the mixture just before sprayed.例文帳に追加

繊維を含有してなる吹付セメントコンクリートに急結材を混合した後、吹付直前に凝結遅延剤を混合してなることを特徴とする急結性吹付セメントコンクリートの吹付工法。 - 特許庁

The production is performed by injecting a liquid product obtained by heating, mixing, and melting the above (A) and (B) components into a mold provided with a reinforcing fiber base material together with a hardening accelerator, filling the spaces between reinforced fibers with the resulting liquid mixture, followed by heating, to harden the liquid mixture.例文帳に追加

その製造は、補強繊維基材を配置した成形金型に、上記（Ａ）（Ｂ）成分を加熱して混合溶解した液状物を硬化促進剤とともに注入し、これを補強繊維間に浸透させ加熱硬化させることにより行なう。 - 特許庁

Since glass cloth with a thickness of 0.10 mm or less reduced in tensile strength by heat treatment contains a resin composition obtained by compounding a thermosetting resin, a curing agent, a curing accelerator and an inorganic filler, glass fibers of the glass cloth can be made fragile by thermal deterioration and drilling properties can be enhanced.例文帳に追加

熱処理により引張り強度を低減した厚さ０．１０ｍｍ以下のガラスクロスに、熱硬化性樹脂と硬化剤と硬化促進剤と無機充填材とを配合した樹脂組成物を含有するので、ガラスクロスのガラス繊維を熱劣化させて脆くすることができ、ドリル加工性を向上させることができる。 - 特許庁