calcicとは 意味・読み方・使い方

The admixture is obtained by mixing a calcic material with aluminum dross so that the ratio of the calcic material to water-soluble aluminum becomes ≥2.5 in terms of molar ratio of CaO to Al_2O_3, and adding ≥50 parts by weight of water to 100 parts by weight of the resulting mixture.例文帳に追加

アルミドロスに石灰質材料をその水溶性アルミニウム量に対してＣａＯ／Ａｌ_2Ｏ_3のモル換算比で２．５以上となるよう混合し、混合物１００重量部に水５０重量部以上を添加して混和材料を得る。 - 特許庁

The method for manufacturing a dephosphorizing material comprises the steps of: mixing lightweight cellular concrete powder having a volume-average particle size of 5 μm to 0.3 mm, a calcic raw material such as ordinary cement and water; granulating the obtained mixture; and subjecting to autoclave curing.例文帳に追加

体積平均粒径が５μｍ〜０．３ｍｍの軽量気泡コンクリートの粉体と、普通セメント等の石灰質原料と、水とを混和して造粒し、オートクレーブ養生して脱リン材とする。 - 特許庁

In the method for producing the autoclaved lightweight cellular concrete where a main raw material is a blended material at a specified ratio of a powdery silicic raw material and a calcic raw material, the autoclaved lightweight cellular concrete is produced by equivalently substituting 5-20 wt.% of the silicic raw material with calcium carbonate.例文帳に追加

粉末状の珪酸質原料と石灰質原料とを所定の割合で配合したものを主原料として製造される軽量気泡コンクリートの製造方法において、上記珪酸質原料の５〜２０重量％を炭酸カルシウムに等量置換して軽量気泡コンクリートを製造することを特徴とする。 - 特許庁

In the production method of the porous humidity controlling material, the water slurry using siliceous starting powder, calcic starting powder and activated carbon powder as main starting materials is prepared, and the slurry is coagulated and solidified after incorporating bubbles in the water slurry by a frothing agent or a foaming agent, moreover the resulting material is subjected to steam aging at high temp. and high pressure.例文帳に追加

また珪酸質原料粉末、石灰質原料粉末及び活性炭粉末を主原料とした水スラリーを調整し、該水スラリー中に発泡剤或いは起泡剤によって気泡を含有せしめた後に凝固硬化させ、さらに高温高圧にて水蒸気養生して製造する多孔質調湿材の製造方法とした。 - 特許庁

The method for manufacturing the ethylene gas-adsorptive inorganic composition comprises the steps of: reacting a siliceous raw material with a calcic raw material to obtain a low-crystalline calcium silicate hydrate; carbonating the low-crystalline calcium silicate hydrate by carbon dioxide to obtain a composition containing calcium carbonate and amorphous silica; and crushing the obtained composition together with the inorganic oxide exhibiting excellent performance of decomposing/removing ethylene gas.例文帳に追加

また本発明のエチレンガス吸着性無機組成物は、ケイ酸質原料と石灰質原料とを反応させることにより低結晶質ケイ酸カルシウム水和物を得る工程と、低結晶質ケイ酸カルシウム水和物を炭酸ガスで炭酸化処理して炭酸カルシウムと非晶質シリカとを含む組成物を得る工程と、組成物を、エチレンガスに対して分解除去性能を有する無機系酸化物とともに粉砕する工程とを経て製造することができる。 - 特許庁