At the point of time in which the liq. carburizing agent 5 is solidified, the screw 1 is made reverse, only the tip part of the screw 1 contg. the female screw part 2 is immersed into the salt bath 6 stored with the liq. carburizing agent 5 and is held to 850 to 950°C, and carburizing treatment is executed.例文帳に追加

液体浸炭剤５が凝固したところで、スクリュ１を逆さまにして、雌ネジ部２を含むスクリュ１の先端部分のみを、液体浸炭剤５を収容し８５０〜９５０℃に維持されたソルトバス６の中に浸漬し、浸炭処理を行う。 - 特許庁

The carburizing treatment process includes a heat treatment process for heat treating a component 1 to be subjected to carburizing treatment in a heat treating surface after a coating process for coating a sliding surface 3 of the component 1 to be subjected to carburizing treatment with an agent 4 which contributes to carburization.例文帳に追加

浸炭加工部品１の摺動面３に、浸炭寄与剤４を塗布する塗布工程後に、浸炭処理部品１を熱処理炉内で熱処理する熱処理工程を有する浸炭処理工程を備える。 - 特許庁

A carburizing agent and a carburization accelerator inactive to a water paint as necessary are mixed in the water paint.例文帳に追加

水性塗料中に浸炭剤及び必要に応じて上記水性塗料に対して不活性な浸炭促進剤を配合する。 - 特許庁

A liq. carburizing agent 5 is melted in a salt bath 6 and is poured into a female screw part 2 formed at the tip part of a screw.例文帳に追加

ソルトバス６の中で液体浸炭剤５を溶融し、スクリュ先端部に形成された雌ネジ部２の中に液体浸炭剤５を注ぎ込む。 - 特許庁

At this time, the temp. of the outer circumferential face of the screw tip part is held to the temp. range of 200 to 300°C, and the liq. carburizing agent 5 is solidified in the female screw part 2.例文帳に追加

このとき、スクリュ先端部の外周面の温度を２００〜３００℃の温度範囲に維持し、雌ネジ部２の中で液体浸炭剤５を凝固させる。 - 特許庁

A manufacturing method cuprites a process to adhere a carburizing agent to the inside surface of the tube 20, a process to plug the opening end of the tube 20 to tightly close the inside of the tube 20 an a process to form the carburized layer 25 on the inner surface of the tube 20 by conducting a heat treatment by heating the tube 20 and gasifying the carburizing agent by utilizing the heat at the heat treatment.例文帳に追加

この中空スタビライザ１０の製造方法は、金属管２０の内面に浸炭処理剤を付着させる工程と、管２０の開口端を塞いで管２０の内部を密閉する工程と、この管２０を加熱して熱処理を行うとともにこの熱処理時の熱を利用して前記浸炭処理剤をガス化させることにより管２０の内面に浸炭処理層２５を形成する工程とを具備している。 - 特許庁

To establish a method for efficiently producing granular metallic iron with high energy efficiency by efficiently progressing carburizing and melting of a solid metallic iron produced by heating and reducing when the metallic iron is produced by heating and reducing mixture containing iron oxide source and carbonaceous reducing agent.例文帳に追加

酸化鉄源と炭素質還元剤を含む混合物を加熱還元して金属鉄を製造する際に、加熱還元により生成する固体金属鉄の浸炭・溶融を効率よく進め、高いエネルギー効率の下で粒状の金属鉄を効率よく製造できる方法を確立すること。 - 特許庁