modulus of elasticity in shearとは 意味・読み方・使い方

To obtain a rubber composition for laminates good in shear modulus of elasticity and breaking strength, having a great shear strain during breaking and improved in fracture characteristics.例文帳に追加

剪断弾性率、破断強度が良好で、かつ、破断時の剪断歪みが大きな、破壊特性を向上させた積層体用ゴム組成物の提供。 - 特許庁

This compsn. exhibits an elasticity ratio of modulus M100 to static shear modulus Gs at the third time in a repeated 100% tensile deformation test with an autograph of 1.4 or higher and a ratio of modulus M300 at the third time in a repeated 300% tensile deformation test to M100 of 3.6 or lower.例文帳に追加

１００％モジュラスＭ_100 と静的剪断弾性率Ｇｓとの比（Ｍ_100／Ｇｓ）が１．４以上である免震積層体用ゴム組成物。 - 特許庁

The flexible resin sheet is characterized in that the shear modulus of elasticity is ≥2×10^6 and ≤1×10^7 Pa at 20°C, ≥5×10^4 Pa at 80°C and ≥3×10^3 and ≤3×10^5 Pa at 120°C.例文帳に追加

２０℃におけるせん断弾性率が２×１０^6Pa以上１×１０^7Pa以下で８０℃におけるせん断弾性率が５×１０^4Pa以上で１２０℃におけるせん断率が３×１０^3Pa以上３×１０^5Pa以下であることを特徴とする。 - 特許庁

The golf ball includes a constituent member formed of a polyurethane composition containing a polyurethane elastomer as a resin component, and satisfying the following physical properties: a shear loss elastic modulus G" measured in a shear mode using a dynamic viscoelasticity device at a temperature of 0°C and an oscillation frequency of 10 Hz is 5.03×10^6 Pa or below, and repulsive elasticity is 54% or above.例文帳に追加

本発明のゴルフボールは、樹脂成分として、ポリウレタンエラストマーを含有し、動的粘弾性装置を用いて、加振周波数１０Ｈｚ、温度０℃の測定条件で、剪断モードで測定した剪断損失弾性率Ｇ”が５．０３×１０^6Ｐａ以下であって、反発弾性が５４％以上の物性を満足するポリウレタン組成物から形成された構成部材を有することを特徴とする。 - 特許庁