An aluminum alloy molten metal having the above composition is cast into a slab with a thickness of 5 to 15 mm at a solidification cooling rate of 20 to 200°C/sec in the 1/4 part of the slab thickness by a thin slab continuous casting machine, and the slab is subjected to cold rolling or is further annealed.例文帳に追加

上記組成のアルミニウム合金溶湯を薄スラブ連続鋳造機にて、スラブ厚み１／４箇所の凝固冷却速度２０〜２００℃／secで厚み５〜１５ｍｍのスラブに鋳造し、冷間圧延を施す、または更に焼鈍する。 - 特許庁

To provide a method for passing a welded point by which the welded point of a steel sheet can be passed through a secondary cold-rolling mill with which a thin steel sheet is heavily reduced at the post stage of a continuous annealing furnace without risk of the breaking of the sheet and the rolling can be rapidly returned to the normal state after passing of the welded point.例文帳に追加

連続焼鈍炉の後段で薄手鋼板を高圧下する２次冷間圧延機を、鋼板の溶接点を板破断を生ずるおそれなく通過させることができ、しかも溶接点通過後の定常状態への復帰を迅速に行わせることができる溶接点通過方法を提供する。 - 特許庁

When the welded point of the steel sheet is passed through the secondary cold-rolling mill 6 with which the thin steel sheet delivered from the continuous annealing furnace 4 is heavily reduced, passing speed is lowered and also rolling load is lowered to ≤200 ton and, furthermore, interstand tension is made into a state of low tension constant control of ≤120 N/mm^2.例文帳に追加

連続焼鈍炉４から出た薄手鋼板を高圧下する２次冷間圧延機６を鋼板の溶接点が通過する際、通板速度を低下させるとともに圧延荷重を２００ｔｏｎ以下にまで低下させ、さらにスタンド間張力を１２０Ｎ/ｍｍ^２以下定の低張力一定制御とした状態とする。 - 特許庁

In the method for producing an Fe-Ni based alloy thin sheet, after final cold rolling, straightening by a leveler is performed, stress relieving annealing by a continuous annealing furnace is performed subsequently to the straightening by the leveler, and thereafter, thread coiling-slit processing is performed.例文帳に追加

Ｆｅ−Ｎｉ系合金薄板材の製造方法において、最終の冷間圧延後にレベラーによる矯正を行い、該レベラーによる矯正の後に連続焼鈍炉による歪取焼鈍を行った後、条取りスリット加工を行うＦｅ−Ｎｉ系合金薄板材の製造方法である。 - 特許庁