austenitizingとは 意味・読み方・使い方

Next, the cast iron article is heated to about 900°C which is an austenitizing temperature and held for 3.5 hours.例文帳に追加

次に、鋳鉄品を、オーステナイト化温度である約９００℃に加熱して３．５時間保持させる。 - 特許庁

Upon austenitizing treatment including the quenching, cooling is performed at a cooling rate slower than that in cooling by liquid immersion.例文帳に追加

焼入れをはじめとしたオーステナイト化処理時に、液体浸せきによる冷却よりも遅い冷却速度で冷却を行う。 - 特許庁

When the push block for CVT belt is quenched, the length of time where the push block is held at a temperature not lower than the austenitizing temperature at heating and holding in the quenching is made to 5 to 40 min.例文帳に追加

ＣＶＴベルト用押しブロックを焼入れする際に、焼入れ時の加熱保持の際に押しブロックがオーステナイト化温度以上に保持される時間を５〜４０分とした。 - 特許庁

Preferably, the treating temperature is set to at least the perfect austenitizing temperature or higher of the martensitic stainless steel, and the treating pressure is set to the tensile strength or higher of the martensitic stainless steel at this treating temperature.例文帳に追加

好ましくは、処理温度は少なくとも前記マルテンサイト系ステンレス鋼の完全オーステナイト化温度以上とし、処理圧力は前記処理温度における前記マルテンサイト系ステンレス鋼の引張強さ以上とする。 - 特許庁

After reheating a panel B2 after preforming up to the austenitizing temperature with a heating furnace 3, the shape of a pressed part is adjusted by performing the restrike forming by press quenching method by supplying the panel to a drawing die 2.例文帳に追加

予備成形後のパネルＢ２をオーステナイト化温度まで加熱炉３にて再度加熱した上で、絞り成形型２に投入してプレス焼入れ法によるリストライク成形を行うことにより成形品の形状を整える。 - 特許庁

A continuous furnace 4 is composed of: a heating furnace 41 consisting of a preheating region 411 and an austenitizing region 312; and a cooling furnace 45, nitrogen and hydrogen produced by subjecting ammonia 42 to heating decomposition by a modification furnace 43 are passed through a drying apparatus 44, propane 46 is added thereto by a gas mixing apparatus 47, and it is introduced into the continuous furnace.例文帳に追加

連続炉４を４１１予熱領域４１１及びオーステナイト化領域３１２からなる加熱炉４１領域及び冷却炉４５から構成し、変成炉４３でアンモニア４２を加熱分解して生成した窒素及び水素を乾燥器４４を経て気体混合器４７でプロパン４６を加えて、連続炉に導入する。 - 特許庁

The method for manufacturing the above iron-based alloy comprises the first heat treatment process for obtaining a mixed structure of martensite, matrix of retained austenite, and unmelted carbides, by solution treatment of rapidly cooling from the higher temperature than austenitizing temperature, and the second heat treatment process for precipitating the low carbon austenite by cooling after precipitating MC type carbides in a temperature region of eutectoid transformation.例文帳に追加

オーステナイト化温度以上の温度から急冷して固溶化処理を施し、これによってマルテンサイトと残留オーステナイトの基地組織と未溶解炭化物の混合組織を得る第１の熱処理工程と、共析変態温度区間でＭＣ型炭化物を析出させた後に冷却し、これによって低炭素オーステナイトを析出させる第２の熱処理工程とにより、上記鉄基合金を得る。 - 特許庁