bead polymerizationとは 意味・読み方・使い方

The process for manufacturing the bead polymer comprises subjecting a reaction system consisting of a disperse phase containing at least a vinyl monomer and a dispersion medium to suspension-polymerization by using a polymerization apparatus comprising a polymerization vessel and an agitation means rotatably arranged in the polymerization vessel.例文帳に追加

重合槽と、該重合槽内で回転可能に配置された攪拌手段とを含む重合装置を用いて、少なくともビニル系単量体を含む分散相と分散媒とからなる反応系を懸濁重合するビーズ状重合体の製造方法。 - 特許庁

This bead-like polymer is obtainable by washing a polymer after suspension polymerization with water in which electrolytes are dissolved at 1-1,000 ppm, favorably at 5-850 ppm.例文帳に追加

懸濁重合後に電解質が１〜１０００ｐｐｍ、好ましくは５〜８５０ｐｐｍ溶解した水で洗浄して得られる、ビーズ状重合物。 - 特許庁

Disclosed herein is the polymerization of monodisperse microencapsulated monomer droplets in water dispersion to produce monodisperse non-microencapsulated bead polymers through the addition of strong alkalis or strong acids during the polymerization.例文帳に追加

単分散性のマイクロカプセル化されたモノマー液滴を水性分散液の形で重合させるマイクロカプセル化されていない単分散性の粒状ポリマーの製造方法において、重合の間にこの分散液に強酸又は強アルカリを添加することを特徴とする方法 - 特許庁

This anion-exchanger is manufactured starting with a monodisperse bead polymer having a swelling index of 2.5-7.5, with more than one feed processes and modification without separation between polymerization processes.例文帳に追加

前記課題は膨潤指数２.５〜７.５を有する単分散ビーズポリマーから出発し、重合工程間の分離なしに、１回を越えるフィード工程および変性によりアニオン交換体を製造することにより解決する。 - 特許庁

This method of producing the monodisperse crosslinked bead polymer is carried out through seed/feed-polymerization, wherein the seed comprising monomer droplets incompletely polymerized, monodispersed, and microencapsulated is used to obtain the objective polymer low in a soluble polymer content.例文帳に追加

可溶性重合体含量の低い、単分散の架橋されたビーズ重合体は、種が不完全に重合した単分散のミクロカプセル化された単量体小滴を含んでなる種／供給法によって得ることができる。 - 特許庁

As the condition in the case of applying simultaneously plural PVA coating liquids 14 in multilayer on a web 12 using a slide bead coating device 10, polyvinyl alcohol contained in the PVA coating liquid 14A forming the lowermost layer in the multiple layer coating films has polymerization degree of 1000-4000 and a thickener is added to becomes 0.05-0.5 wt.% per the content of polyvinyl alcohol.例文帳に追加

スライドビード型塗布装置１０を使用して複数のＰＶＡ塗布液１４をウエブ１２に同時に多層塗布する場合の条件として、多層塗布膜のうちの最下層を形成するＰＶＡ塗布液１４Ａに関して、含有するポリビニルアルコールの重合度を１０００〜４０００とすると共に、増粘剤をポリビニルアルコールの含有量に対して０．０５〜０．５重量％になるように添加するようにした。 - 特許庁