Copper foil by electrolysisとは 意味・読み方・使い方

To provide a method of manufacturing an electrode for electrolysis having excellent durability in the industrial electrolysis such as, in particular, electrolytic copper foil manufacture followed by oxygen generation on an anode, power supply in an aluminum liquid or continuous electrolytic hot dip galvanized steel sheet manufacture.例文帳に追加

特に陽極において酸素発生を伴う電解銅箔製造、アルミニウム液中給電、連続電気亜鉛メッキ鋼板製造等の工業電解において優れた耐久性を有する電解用電極の製造方法の提供。 - 特許庁

A rolled foil of, for example, a thickness of 26 μm composed of face-roughened copper of which the surface is formed in recessed and projected shapes by the deposition of copper by an electrolysis is prepared as a negative electrode current collector.例文帳に追加

負極集電体として、電解法により銅が析出されることにより表面が凹凸状に形成された粗面化銅からなる例えば厚さ２６μｍの圧延箔を用意する。 - 特許庁

The method for manufacturing the copper foil includes electrolysis by using an electrolytic solution that is an aqueous solution of sulfuric acid and copper sulfate, in which Cl^- ion concentration is controlled to 2.0 mg/l or less and protein concentration is controlled to 0.5 mg/l or less.例文帳に追加

電解液としてＣｌ^−イオン濃度が２．０ｍｇ／ｌ以下、タンパク質濃度が０．５ｍｇ／ｌ以下の硫酸−硫酸銅水溶液を用いて電解する銅箔の製造方法。 - 特許庁

To provide a method for manufacturing a electrolytic copper foil which adequately eliminates curls and pinholes, by removing an influence of generated gas from a normally electrodeposited part during an electrolysis, when manufacturing the electrolytic copper foil by means of passing a current of a high current density by using an auxiliary anode at the beginning of an electrodeposition, and to provide an apparatus used for it.例文帳に追加

電着開始時に補助陽極を用いて高電流密度の電流を通電して電解銅箔を製造する際、通常の電着部の電解に発生するガスの影響をなくして、カールとピンホールを十分に除去することができる電解銅箔の製造方法とそれに用いる装置を提供する。 - 特許庁

The surface-treated copper foil is manufactured by performing electrolysis at the predetermined current density by using cobalt plating liquid containing cobalt sulfide (7-hydrate) to form the rustproof layer on the coarse surface of an electrolytic copper foil or the like, and a method for water-rinsing and drying the rustproof layer is employed.例文帳に追加

また、当該表面処理銅箔の製造は、電解銅箔等の粗面上に、硫酸コバルト（７水和物）を含むコバルトメッキ液を用いて、所定の電流密度で電解し、防錆処理層を形成し、水洗し、乾燥する手法等を採用する。 - 特許庁

In the method of producing electrolytic copper foil by electrolysis of an aqueous acidic copper plating solution containing sulfuric acid, the aqueous acidic copper plating solution containing sulfuric acid comprises a copolymer of a diallyl dialkyl ammonium salt and sulfur dioxide, polyethylene glycol and 3-mercapto-1-sulfonic acid.例文帳に追加

硫酸酸性銅めっき液の電気分解による電解銅箔の製造方法において、ジアリルジアルキルアンモニウム塩と二酸化硫黄との共重合体と、ポリエチレングリコールと塩素と３−メルカプト−１−スルホン酸とを含有することを特徴とする硫酸酸性銅めっき液を用いる。 - 特許庁

The electrolytic copper foil is manufactured by an electrolytic method using a sulfuric acid-type copper electrolysis solution containing a compound having a structure comprising a sulfone group attached to the benzene ring, a sulfonic acid salt of an active sulfur compound, and a quaternary ammonium salt polymer having a cyclic structure.例文帳に追加

この電解銅箔は、ベンゼン環にスルホン基が結合した構造を有する化合物、活性硫黄化合物のスルホン酸塩、環状構造を持つ４級アンモニウム塩重合体とを含む硫酸系銅電解液を用い、電解法により製造する。 - 特許庁

Alternatively, the method includes arranging an anode 3 on the rough surface side 2 of the electrolytic copper foil and a cathode 5 on a glossy surface side, performing a smooth plating treatment on the rough surface by electrolysis, and then performing a reverse electropolishing treatment on the glossy surface.例文帳に追加

電解銅箔の粗面側２にアノード３を配置し光沢面側にカソード５を配置して、電解処理を行うことにより、銅箔粗面に平滑めっき処理を行うとともに、銅箔光沢面に逆電解研磨処理を行うことを特徴とする電解銅箔光沢面の電解研磨方法。 - 特許庁