carboxyl endとは 意味・読み方・使い方

The water repellent should preferably be of fluorine type as it exerts excellent anti-rusting effect, the most preferably of one having carboxyl radical at the end.例文帳に追加

さらに、優れた防錆効果を示すことから、前記撥水剤はフッ素系撥水剤を用いるのがよく、中でも末端にカルボキシル基を有するものが好ましい。 - 特許庁

There is provided a polyester film which has a carboxyl end group concentration of 20 eq/ton or less and at least one surface of which is uneven, or there is provided a film comprising a polyester film having a carboxyl end group concentration of 20 eq/ton or less and a base layer which is provided on at least one surface of this polyester film and the surface of which is uneven.例文帳に追加

カルボキシル末端基濃度が２０ｅｑ／ｔｏｎ以下、かつ、少なくとも一方の表面が凹凸を有するポリエステルフィルム、または、カルボキシル末端基濃度が２０ｅｑ／ｔｏｎ以下であるポリエステルフィルムとその少なくとも一方の表面に設けられた下地層を有し、該下地層の表面が凹凸であるフィルム。 - 特許庁

This polyamide resin composition comprises (A) a polyamide wherein the mole ratio of the carboxyl end group to the amino end group is >1, (B) an aromatic diamine, and (C) a base with a pKa (25°C) of ≥10 or a salt thereof.例文帳に追加

ポリアミド樹脂組成物は、（Ａ）カルボキシル末端基とアミノ末端基との比率が、前者／後者（モル比）＞１であるポリアミドと、（Ｂ）芳香族ジアミンと、（Ｃ）ｐＫａ（２５℃）１０以上の塩基又はその塩とを含有する。 - 特許庁

To provide a polyester composition having excellent dispersibility of titanium dioxide and a low carboxyl end group content, and a white polyester film using the same and suitable for solar cell application.例文帳に追加

酸化チタンの分散性に優れ、カルボキシル末端基が低いポリエステル組成物およびそれを用いた太陽電池用途に適した白色ポリエステルフィルムを提供する。 - 特許庁

After a carbon nanotube 107 incorporated in a prescribed fraction is subjected to acid and ultrasonic treatment and its end is carboxylated, biotin 109 is modified by using a carboxyl group.例文帳に追加

所定の画分に含まれるカーボンナノチューブ１０７を酸および超音波処理に供し、末端をカルボキシル化した後、カルボキシル基を用いてビオチン１０９を修飾する。 - 特許庁

This photo-reactive hot melt adhesive composition comprises a resin prepared by reacting a carboxyl group at the end of a polyester and a multifunctional epoxy compound, and a photo-cation polymerization initiator.例文帳に追加

ポリエステル末端のカルボキシル基と多官能エポキシ化合物とを反応させてなる樹脂と、光カチオン重合開始剤とからなる光反応性ホットメルト接着剤組成物。 - 特許庁

This modified polyester resin is made by using as a raw material a poly(ethylene terephthalate) resin and by using as a modifying agent an amine-containing compound having in the molecule an amino-group or/and an imino group each to be reactive with a carboxyl end group, and by reacting the carboxyl end group of the poly(ethylene terephthalate) resin with the amine-containing compound to thereby form an acid amide linkage.例文帳に追加

ポリエチレンテレフタレート樹脂を原料として用い、改質剤として、分子内にカルボキシル基末端と反応するアミノ基又は／及びイミノ基を有するアミン含有化合物を用いて、前記ポリエチレンテレフタレート樹脂のカルボキシル基末端と、前記アミン含有化合物とを反応させて、酸アミド結合を形成して改質ポリエステル樹脂とした。 - 特許庁

The polyamide resin composition comprises (A) a polyamide wherein the molar ratio of the carboxyl end group to the amino end group is >1, (B) an aminocarboxylic acid having a molecular weight of ≤15,000, and (C) a base having a pKa (25°C) of ≥10 or a salt thereof.例文帳に追加

ポリアミド樹脂組成物は、（Ａ）カルボキシル末端基とアミノ末端基との比率が、前者／後者（モル比）＞１であるポリアミドと、（Ｂ）分子量１５０００以下のアミノカルボン酸と、（Ｃ）ｐＫａ（２５℃）１０以上の塩基又はその塩とを含有する。 - 特許庁