exchangeable cationsとは 意味・読み方・使い方

The molar ratio of SiO_2/Al_2O_3 is more preferably not lower than 10 and not higher than 14; the ratio of protons to the exchangeable cations not lower than 90%; and an average particle diameter of 1 μm or more.例文帳に追加

ＳｉＯ_２／Ａｌ_２Ｏ_３のモル比はさらに１０以上１４以下、交換可能なカチオン中のプロトンの比率が９０％以上、平均粒子径が１μｍ以上であることが好ましい。 - 特許庁

By using zeolite in which 97.5 to 99.5 mol% of exchangeable cations are ion-exchanged with lithium, a nonaqueous electrolyte can be dehydrated while suppressing the elution of cationic impurities such as sodium to 50 ppm or less.例文帳に追加

交換可能なカチオンの９７．５ｍｏｌ％以上９９．５ｍｏｌ％以下がリチウムでイオン交換されたゼオライトでは、ナトリウム等のカチオン不純物の溶出を５０ｐｐｍ以下で非水電解液を脱水処理することができる。 - 特許庁

This aromatic vinyl resin composition is produced by providing a lamellar compound, preferably a treated lamellar compound obtained by substituting the exchangeable cations between the layers of the lamellar compound with organic onium ions and adding the lamellar compound to an aromatic vinyl resin having an acid value of 5-200 mgKOH/g.例文帳に追加

酸価が５〜２００ｍｇＫＯＨ／ｇの範囲である芳香族ビニル系樹脂に対し、層状化合物、好ましくは層状ケイ酸塩の層間に存在する交換性陽イオンが有機オニウムイオンで交換された処理層状化合物を添加してなる芳香族ビニル系樹脂組成物。 - 特許庁

When voltage is applied between the first electrode 3 and the second electrode 4 by a power source 6, cations and anions produced by the ionization of a residual chemical liquid are electrophoresed to the first electrode (anode) and the second electrode (cathode) and caught by the ion exchangeable material 2 to be removed.例文帳に追加

電源６により第１電極３と第２電極４との間に電圧を印加すると、残留した薬液が電離してなる陽イオンと陰イオンが第１電極（陽極）３と、第２電極（陰極）４とに電気泳動し、イオン交換性材料２に捕捉され除去される。 - 特許庁

This mica composite is obtained by ion exchange of 10-95 eq.% of exchangeable cations among the interlayer ions of a swellable synthetic mica with at least one kind of ions selected from the group consisting of K, Ba, Cu, Ag, Te, Bi, Pb, Ce, Fe, Mo, Nb, W, Sb, Sn, V, Mn, Ni, Co, Zn, Zr and Ti ions.例文帳に追加

膨潤性合成雲母の層間イオンのうち、交換性陽イオンの１０〜９５当量％を、Ｋ，Ｂａ，Ｃｕ，Ａｇ，Ｔｅ，Ｂｉ，Ｐｂ，Ｃｅ，Ｆｅ，Ｍｏ，Ｎｂ，Ｗ，Ｓｂ，Ｓｎ，Ｖ，Ｍｎ，Ｎｉ，Ｃｏ，Ｚｎ，ＺｒおよびＴｉからなる群から選ばれる１種または２種以上のイオンとイオン交換させて得られる合成雲母複合体により課題を解決できる。 - 特許庁

The objective polyamide resin compositions are obtained by melt kneading (a) a polyamide resin with (b) a lamellar silicate salt whose exchangeable cations present between the layers have been exchanged with organic onium ions, and have a ratio of the concentration A of the terminal amino groups of the polyamide resin (a) to that B of the terminal carboxy groups of the polyamide resin (a) of not less than 0.9.例文帳に追加

（ａ）ポリアミド樹脂および（ｂ）層間に存在する交換性陽イオンが有機オニウムイオンで交換された層状珪酸塩を溶融混練してなるポリアミド樹脂組成物であって、（ａ）ポリアミド樹脂の末端アミノ基濃度をＡ、末端カルボキシル基濃度をＢとしたとき、その比Ａ／Ｂの値が０．９以上であることを特徴とするポリアミド樹脂組成物。 - 特許庁