pressure sintering methodとは 意味・読み方・使い方

To provide a pressure sintering method, by which conventional problems, such as generation of a melt, caused when a sintering-resistant Fe-based intermetallic compound alloy is subjected to pressure sintering using a graphite mold is solved, and pressure sintering of a sintering-resistant Fe-based intermetallic compound alloy can be effectively performed at a relatively low cost.例文帳に追加

グラファイト製型を用いて焼結性Fe系金属間化合物合金を加圧焼結する際の、融液の発生等の従来の問題点を解決し、難焼結性Fe系金属間化合物合金を比較的低コストで有効に加圧焼結することのできる加圧焼結方法を提供する。 - 特許庁

Further, in the method for producing a target material, the powder obtained by the above is subjected to pressure sintering.例文帳に追加

また、上記で得られた粉末を加圧焼結するターゲット材の製造方法である。 - 特許庁

To provide a sintered compact having a nano-size particle structure of high purity, by sintering a nano-size raw powder with a pulse-electrification pressure sintering method.例文帳に追加

ナノサイズの原料粉末をパルス通電加圧焼結法により焼結して純度の高いナノサイズの粒子構造を有する焼結体を得る。 - 特許庁

Preferably, a seed crystal is produced in advance by firing the amorphous powder under normal pressure and at a temperature of 500-700°C for about 12 hours, and then sintering it by an electric compression sintering method such as a discharge plasma sintering method.例文帳に追加

好ましくは、上記アモルファス粉末を常圧において温度５００℃から７００℃で１２時間程度焼成することにより、種結晶を予め作っておき、それを放電プラズマ焼結等の方法で通電加圧焼結する。 - 特許庁

Ceramics sintered by hot isostatic pressing after pressure sintering are heat-treated at a temperature in the range from (the normal sintering temperature) -200°C to (the normal sintering temperature) +100°C and defects are observed by a light transmission observation method.例文帳に追加

常圧焼結の後に熱間静水圧加圧焼結されたセラミックスを、前記常圧焼結時の温度に対して＋１００℃〜−２００℃の温度範囲内の温度で熱処理し、これを光透過観察法によって欠陥を観察する。 - 特許庁

After that, the mixed power 4 is sintered while being pressurized in a pressure-reduced atmosphere by a hot press sintering method, or the like.例文帳に追加

その後、ホットプレス焼結法などによって、減圧雰囲気中で加圧しながら加熱して、混合粉末４を焼結する。 - 特許庁

In the method of canning a precompact for sintering for sealing a pre-compacted green material for sintering is sealed into a capsule, and performing sintering at a high pressure under a pressure, the precompact for sintering is preferably subjected to wax treatment, or a plating master with a form the same as that of the precompact is subjected to electroplating, and the plated layer is used as a capsule for HIP.例文帳に追加

予め成形した焼結用グリーン材をカプセルに封止して高温・加圧下で焼結するＨＩＰ処理のための、焼結用予成形体のキャニング方法において、燒結用予成形体に、好ましくはワックス処理して、または、該予成形体と同形のめっきマスターに、電気めっきを施し、該めっき層をＨＩＰ用カプセルとして用いるキャニング方法。 - 特許庁

To simply and uniformly apply pressure in a method of sintering metal powder or metal-coated powder.例文帳に追加

金属粉末または金属被覆粉末の焼結法おいて、簡便に、しかも均質に圧力を負荷することができる方法を提供する。 - 特許庁