As the α-brass by which the above objects can be attained, e.g. hard α-brass having the following characteristics is adopted: 451 to 519 MPa tensile strength; formability of ≥8.5 Erichsen value; stress corrosion cracking resistance of ≥6 hours time to rupture by stress corrosion cracking.例文帳に追加

上記目的を達成できるα黄銅として、引張り強さが４５１ＭＰａ〜５１９ＭＰａであり、エリクセン値で８．５以上の成形加工性を備え、且つ、応力腐食割れ破断時間が６時間以上の耐応力腐食割れ性能を備えたことを特徴とした硬質α黄銅等を採用する。 - 特許庁

To provide a method of mending a blade groove of a turbine rotor which has an excellent stress corrosion cracking (SCC) characteristics and is usable for a long period under a severe environment of corrosion.例文帳に追加

腐食環境の厳しい状態でも長時間の使用に耐えるタービンロータのＳＣＣ特性に優れた翼溝補修方法を提供すること。 - 特許庁

To provide a copper alloy for a semiconductor lead frame excellent in strength, electroconductivity, bending workability, punching press workability or the like, further small in the softening characteristics of stress relaxation, moreover low in the sensitivity of stress corrosion cracking and improved in heat resistance.例文帳に追加

強度、導電性、曲げ加工性、打抜プレス加工性などに優れ、さらに応力緩和の軟化特性が小さく、かつ応力腐食割れの感受性が低く、耐熱性を向上させた半導体リードフレーム用銅合金を提供すること。 - 特許庁

To provide an Ni-reduced austenite stainless steel having excellent recycling properties, free from the problem of the reduction in productivity caused by surface quality, and having raw material characteristics such as satisfactory workability, season cracking resistance, corrosion resistance and stress corrosion cracking resistance.例文帳に追加

リサイクル性に優れ、表面品質に起因する生産性低下の問題がなく、素材特性面では良好な加工性、耐時期割れ性、耐食性、耐応力腐食割れ性を兼ね備えたＮｉ節減型のオーステナイト系ステンレス鋼を提供する。 - 特許庁

To provide a copper alloy which has excellent stress corrosion cracking resistance and dezincification resistance while maintaining the excellent characteristics of the conventional brass, and to provide a production method thereof.例文帳に追加

従来の黄銅の優れた特性を維持しつつ、耐応力腐食割れ性および耐脱亜鉛性に優れた銅合金およびその製造方法を提供する。 - 特許庁

To provide a fine granular austenitic stainless steel sheet in which a stress-corrosion cracking as a defect is eliminated, and good workability is also obtained by regulating average crystal grain diameter to ≤10 μm in Ni content of ≤8% and the characteristics of the crystal grain boundary.例文帳に追加

８％以下のＮｉ量で平均結晶粒径を１０μｍ以下かつ結晶粒界の性格を規定して，欠点である応力腐食割れを克服し，加工性との両立を図った微細粒オーステナイト系ステンレス鋼板を提供する。 - 特許庁