To provide a crank shaft having manufacturing performance similar to or higher than that of a case of using a conventional material, although it is nitrocarburized on its surface, and also having high fatigue strength.例文帳に追加

表面に軟窒化処理が施されているにも拘わらず、これまでの材料と同等以上の製造性を有し、かつ、高い疲労強度も両立させたクランクシャフトを提供する。 - 特許庁

(2) The quenched and tempered nitrocarburized crankshaft using the rough shaped article as the stock, and obtained by machining the rough shaped article in at least 2 mm at a depth from the surface, and then subjecting the same to nitrocarburization treatment.例文帳に追加

(2)前記粗形品を素材とする軟窒化クランク軸で、前記粗形品を表面からの深さで少なくとも2mm以上切削加工してから軟窒化処理された調質型軟窒化クランク軸。 - 特許庁

In this crank shaft having a pin portion and a journal portion composed of steel having the nitrocarburized surface, a surface quenched-layer in which a quench-induced martensite phase and a strain-induced martensite phase formed by transforming residual austenite phase into martensite phase in creating the quench-induced martensite phase by plastic forming are mixed, is formed on the nitrocarburized steel surface layer portion constituting the pin portion and the journal portion.例文帳に追加

表面に軟窒化処理が施された鋼よりなる、ピン部及びジャーナル部を有するクランクシャフトにおいて、前記ピン部及びジャーナル部をなす前記軟窒化処理された鋼表層部に、焼入れ誘起マルテンサイト相と、該焼入れ誘起マルテンサイト相が生成する際の残留オーステナイト相を、塑性加工によりマルテンサイト変態させた加工誘起マルテンサイト相とが混在した表層焼入れ加工層が形成されてなる。 - 特許庁

At least one of an inner ring 1, an outer ring 2 and a rolling element 3 is composed of steel which is carburized or nitrocarburized within a temperature range of 800-1,050°C, then annealed two or more times with austenite transformation of one or more times, then quenched, and tempered.例文帳に追加

内輪１、外輪２及び転動体３のうち少なくとも一つが、８００℃〜１０５０℃の温度範囲で浸炭または浸炭窒化を施され、次いで１回以上のオーステナイト変態を伴う焼鈍を２回以上施された後、焼入れ及び焼戻し処理を施された鋼から形成されている。 - 特許庁