post-chlorinated~の英語

To provide a method for producing a chlorinated vinyl chloride-based resin by a gas-solid reaction method having excellent post treatment simplicity and an excellent installation cost property, by which the chlorinated vinyl chloride-based resin allowing a simple removal of hydrogen chloride from the polymer, and having an inherent heat resistance and excellent heat stability can be produced.例文帳に追加

後処理の簡便性と設備コスト性に優れた気固反応法による塩素化塩化ビニル樹脂の製造法を用いて、塩化水素の除去が簡便で且つ本来の耐熱性を有し、熱安定性にすぐれた塩素化塩化ビニル系樹脂を生産する。 - 特許庁

To provide a post chlorinated polyvinyl chloride resin improved in heat stability thereof and greatly improved in die pressure and extrusion torque.例文帳に追加

後塩素化塩化ビニル系樹脂のパイプ押出成形において後塩素化塩化ビニル系樹脂の熱安定性を向上するとともにダイ圧および押出トルクを大幅に改良することのできる後塩素化塩化ビニル系樹脂の製造方法を提供する。 - 特許庁

This vinyl chloride resin is a (co)polymer obtained by polymerizing or copolymerizing a vinyl chloride monomer and/or vinylidene chloride monomer, or its post-chlorinated substance, and is characterized by exhibiting ≤150 ppm amount of generated hydrogen chloride under heating at 180°C for 20 min.例文帳に追加

塩化ビニルモノマー及び／又は塩化ビニリデンモノマーを重合又は共重合して得られる（共）重合体若しくはその後塩素化物であって、１８０℃、２０分間加熱下での発生塩化水素量が１５０ｐｐｍ以下であることを特徴とする塩化ビニル系樹脂。 - 特許庁

The low shrinkage m-aramid fiber is obtained by compounding 1-20 wt.% post-chlorinated polyvinylchloride based on m-aramid weight, and performing heat treatment under relaxation to have ≤2% maximum heat-shrinkage, wherein the polyvinylchloride has ≥63 wt.% chlorine content.例文帳に追加

メタ型全芳香族ポリアミド重量を基準として、塩素含有率が６３重量％以上の後塩素化ポリ塩化ビニルを１〜２０重量％配合し、かつ弛緩熱処理を施して最大熱収縮率を２％以下とした低収縮性メタ型全芳香族ポリアミド繊維。 - 特許庁

This vinyl chloride resin is a (co)polymer obtained by polymerizing or copolymerizing a vinyl chloride monomer and/or vinylidene chloride monomer, or its post-chlorinated substance, and is characterized by exhibiting ≤18 YI yellowness index of a plate material produced by powder-compressing at 170°C and measured according to JIS K7105.例文帳に追加

塩化ビニルモノマー及び／又は塩化ビニリデンモノマーを重合又は共重合して得られる（共）重合体若しくはその後塩素化物であって、１７０℃の粉末プレスにより作成した板状体をＪＩＳ Ｋ７１０５に準拠して測定した黄色度ＹＩが１８以下であることを特徴とする塩化ビニル系樹脂。 - 特許庁

The post chlorinated polyvinyl chloride resin is prepared by chlorinating in an aqueous suspension a polyvinyl chloride resin having an average degree of polymerization of 800-1,300 using as a suspension agent polyethylene oxide alone, polyethylene oxide and a water-soluble cellulose ether or polyethylene oxide and a partially saponified polyvinyl acetate to a degree of chlorination of 67.0-68.0.例文帳に追加

ポリエチレンオキサイド単独、ポリエチレンオキサイドおよび水溶性セルロースエーテルあるいはポリエチレンオキサイドと部分鹸化ポリ酢酸ビニルを懸濁剤として使用して得られた平均重合度８００〜１３００の塩化ビニル系樹脂を水性懸濁下で塩素化度６７．０〜６８．０重量％に塩素化することにより後塩素化塩化ビニル系樹脂を製造する。 - 特許庁