The composite material contains the calcined magnetic ceramic powder of 40-60 vol.% as a matrix component and the calcined or sintered semiconducting ceramic powder as aggregate for the rest.例文帳に追加

磁性体磁器材料の仮焼体粉末をマトリックス材として４０〜６０体積％含み、半導体磁器材料の仮焼体粉末若しくは焼結体粉末を骨材として残部含む。 - 特許庁

The semiconducting ceramic is composed of a sintered compact having 2MgO.SiO_2 as an essential crystal phase and at least one kind of a crystal selected from MgFe_2O_4, Fe_3O_4 and Fe_2O_3 and the crystal of MgO as sub-components.例文帳に追加

２ＭｇＯ・ＳｉＯ_2を主結晶相とし、副結晶相としてＭｇＦｅ_2Ｏ__4、Ｆｅ_3Ｏ_4及びＦｅ_2Ｏ_3から選ばれる少なくとも１種の結晶とＭｇＯの結晶とを有する焼結体からなる半導電性セラミックスである。 - 特許庁

At the time of manufacturing the strontium titanate-based grain-boundary-insulated semiconductor ceramic containing a semiconducting agent, the rate of titanium atoms in a composition from which a component electrically insulating crystal grain boundaries and the semiconducting agent are removed is made larger than the stoichiometric ratio of the composition and, in addition, the 20-80% of strontium atoms is replaced with calcium atoms.例文帳に追加

半導体化剤を含有したチタン酸ストロンチウム系の粒界絶縁型半導体セラミックスを作製するにあたり、結晶粒界を電気的に絶縁している成分及び半導体化剤をそれぞれ除いた組成でのチタン原子の割合を化学量論比よりも多くし、かつ、ストロンチウム原子の２０〜８０％をカルシウム原子で置換することによって解決した。 - 特許庁

The strontium titanate-based grain-boundary-insulated semiconductor ceramic containing a semiconducting agent is manufactured in a state where the rate of titanium atoms in a composition from which a component electrically insulating crystal grain boundaries and the semiconducting agent are removed is made larger than the stoichiometric ratio of the composition and, in addition, the ≤10% of strontium atoms is replaced with magnesium atoms.例文帳に追加

半導体化剤を含有したチタン酸ストロンチウム系の粒界絶縁型半導体セラミックスを作製するにあたり、結晶粒界を電気的に絶縁している成分及び半導体化剤をそれぞれ除いた組成でのチタン原子の割合を化学量論比よりも多くし、かつ、ストロンチウム原子の１０％以下をマグネシウム原子で置換することによって解決した。 - 特許庁

The semiconducting ceramic material is powder calcined or sintered at temperatures from 100°C lower than its sintering temperature to its sintering temperature and the magnetic ceramic material is powder calcined at 700-800°C.例文帳に追加

半導体磁器材料はその焼結温度より１００℃低い温度ないしその焼結温度で仮焼若しくは焼成してなる仮焼体粉末若しくは焼結体粉末であり、磁性体磁器材料は７００〜８００℃の温度で仮焼してなる仮焼体粉末である。 - 特許庁

The material is a composite sintered compact 11 of a semiconducting ceramic material having a spinel structure comprising ≥2 kinds of metal oxides selected from MnO, CoO, NiO, CuO, Fe2O3, and Al2O3 and a magnetic ceramic material comprising Ni-Zn-Cu-based ferrite.例文帳に追加

複合型半導体磁器材料はＭｎＯ，ＣｏＯ，ＮｉＯ，ＣｕＯ，Ｆｅ_2Ｏ_3及びＡｌ_2Ｏ_3からなる群より選ばれた２種以上の金属酸化物からなるスピネル構造の半導体磁器材料と、Ｎｉ−Ｚｎ−Ｃｕ系フェライトを主成分とする磁性体磁器材料との混合焼結体１１である。 - 特許庁

A holding tool 20 has an air intake path 2 formed in a support 16 comprising ceramic having a semiconducting property, and the holding tool 20 has a region in which the surface 4 of the air intake path 2 has a surface resistance value smaller than that of the other surface 6 in the support 16.例文帳に追加

半導電性を有するセラミックスからなる支持体１６に吸気路２を形成した保持用治具２０であって、吸気路２の表面４は支持体１６における他の表面６より表面抵抗値が小さい領域を有している保持用治具２０とする。 - 特許庁