「CALCINED MAGNESIA」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

The production method has a stage where fired magnesia powder or a substance containing fired magnesia powder and CaO components is mixed with an assistant increasing the hardening strength of hydrates, and water, and the mixture is formed to obtain a formed body having a prescribed shape, and a stage where the formed body is cured to obtain a calcined magnesia briquette.例文帳に追加

焼成マグネシア粉末に、又は、焼成マグネシア粉末及びＣａＯ成分を含有する物質に、水和物の硬化強度を増加させる助剤及び水を混合して成型することにより所定形状の成型体を得る工程と、前記成型体を養成して軽焼マグネシアブリケットを得る工程と、を具備する。 - 特許庁

A slurry with a controlled concentration and produced by adding and mixing a polysaccharide solution to and with a silica-magnesia hydrate paste or a silica-alumina-magnesia hydrate paste produced by adding alumina hydrate to a silica-magnesia hydrate paste is dropwise titrated to a solution containing a polyvalent metal ion to form a spherical hydrogel, the hydrogel is aged, washed, and dried and then calcined.例文帳に追加

シリカ−マグネシア水和物ペースト、あるいはシリカ−マグネシア水和物にアルミナ水和物を添加したシリカ−アルミナ−マグネシア水和物ペーストに多糖類溶液を加えて混合し、濃度を調整したスラリーを多価金属イオンを含む溶液中へ滴下して球状のヒドロゲルを形成させ、ついで熟成し、洗浄した後乾燥、焼成することを特徴とする。 - 特許庁

A refractory lining structure of a vacuum degassing container is adapted such that non-calcined magnesia carbon bricks covered with a metal sheet only on the back side is lined partly or wholly.例文帳に追加

真空脱ガス処理容器の耐火物内張り構造を、背面側のみが金属板で被覆された不焼成マグネシアカーボン煉瓦を一部あるいは全部に内張りしたものとする。 - 特許庁

Preferably, the agent contains 2-100 pts.mass of an alkali metal silicate based on 100 pts.mass of magnesium oxide, the magnesium oxide is calcined magnesia, and the alkali metal silicate is one or more substances selected from water glass, potassium water glass, lithium water glass, powdery sodium silicate and powdery potassium silicate.例文帳に追加

好ましくは、酸化マグネシウム１００質量部に対して２〜１００質量部の珪酸アルカリ金属塩を含有し、酸化マグネシウムが仮焼マグネシア、珪酸アルカリ金属塩が水ガラス，カリウム水ガラス，リチウム水ガラス，粉末珪酸ソーダ，粉末珪酸カリウムから選択される１種以上からなる。 - 特許庁

The method for producing the fatty acid polyoxyalkylene alkyl ether includes a process for addition-reacting a fatty acid ester with an alkylene oxide in the presence of a calcined alumina-magnesia co-oxide catalyst in the coexistence of a base substance selected from alkali metal carbonates, silicates and carboxylates and organic amines having a molecular weight of <1,000 and quaternary salts thereof.例文帳に追加

アルカリ金属の炭酸塩、ケイ酸塩及びカルボン酸塩並びに分子量が1000未満の有機アミン及びその4級塩から選択される塩基性物質と共存させた焼成アルミナ・マグネシア複合酸化物触媒の存在下で、脂肪酸エステルにアルキレンオキシドを付加反応させる工程を含む脂肪酸ポリオキシアルキレンアルキルエーテルの製造方法に関する。 - 特許庁