Chrysotileとは 意味・読み方・使い方

In Fig.2, the fact that the structure of chrysotile is changed from acicular ones to grains may be confirmed from the crystal structure determined by X-ray diffraction and measurement results of a surface structure determined by an electron microscope by irradiating a sulfuric aqueous solution in which the chrysotile is immersed with electron beams with an incidence energy of 0.8 MeV.例文帳に追加

図２では、白石綿を浸漬した硫酸水溶液中に、入射エネルギー０．８ＭｅＶの電子線を照射することで、白石綿の構造が針状から粒状に変化することが、Ｘ線回折による結晶構造ならびに電子顕微鏡による表面構造の測定結果から確認できる。 - 特許庁

In the analysis method, the amount of dehydration of the chrysotile in the thermogravimetry of the serpentine sample is measured from a thermogravimetric curve or a differential thermogravimetric curve obtained by performing the thermogravimetry to the serpentine sample and a standard loaded sample, where a standard chrysotile is loaded into the serpentine sample, under the same conditions each, or a differential thermogravimetric curve.例文帳に追加

本発明の分析方法は、蛇紋石試料および該蛇紋石試料に標準クリソタイルを添加した標準添加試料を、それぞれ同条件で熱重量測定して得られる熱重量曲線または微分熱重量曲線から、前記蛇紋石試料の熱重量測定におけるクリソタイルの脱水量を測定することを特徴とする。 - 特許庁

Chrysotile changes to calcium silicate and the like owing to a chemical reaction of asbestos with unslaked lime and oxygen, and a high temperature treatment with a heat generated by adding water to unslaked lime.例文帳に追加

アスベストと生石灰と酸素の化学反応と、生石灰に水を加えると発生する熱による高温処理によって、クリソタイルはケイ酸カルシウム等に変化していく。 - 特許庁

To attain effective utilization of asbestos or serpentinite containing asbestos as a carbon dioxide fixation material useful for reduction of carbon dioxide gas (carbon dioxide) contained in the atmosphere by converting the chrysotile structure of asbestos to the forsterite structure.例文帳に追加

石綿又は石綿を含有した蛇紋岩を、石綿のクリソタイル構造をフォルステライト構造に変性させることによって、大気中の炭酸ガス（二酸化炭素）低減に有効な二酸化炭素固定化材として有効活用を図る。 - 特許庁

On the occasion of detoxification of the asbestos containing material by heating, the heating temperature that the asbestos containing material reaches in detoxification is determined on the basis of the relation between the amount of formation of akermanite obtained by heating an asbestos containing specimen which contains chrysotile and calcium, and the heating temperature.例文帳に追加

アスベスト含有材料を加熱して無害化処理するにあたり、クリソタイルとカルシウムとを含むアスベスト含有検体を加熱して得られるオケルマナイト生成量と加熱温度との関係に基づいて、アスベスト含有材料が無害化処理時に到達する加熱温度を判定する。 - 特許庁

To provide a treating method for asbestos which makes the treated product recylable stably without dumping the treated material, consuming a great quantity of energy or producing the material which is easy to react with water such as forsterite having a posibility of recrystallization to chrysotile.例文帳に追加

被処理物質を廃棄することなく、大量のエネルギーを消費することなく、クリソタイルへ再結晶化の可能性のあるフォルステライトなど水と反応し易い物質を生成することがなく、かつ処理された生成物が安定で再利用可能となる石綿の処理方法の提供。 - 特許庁

The liquid agent of preventing asbestos from scattering is produced by mixing an aqueous solution comprising magnesium chloride, a montmorillonite-type mineral, silica particles, and titanium oxide, i.e., a visible-light responsive photocatalyst, which agent decomposes chrysotile or the like, i.e., a harmful chemical substance contained in asbestos.例文帳に追加

アスベスト飛散抑制液剤は、塩化マグネシウムを含有する水溶液に、モンモリロナイト系鉱物およびシリカ粒子を添加し、可視光型光触媒である酸化チタンを添加して、アスベスト中に含まれる有害化学物質クリソタイル等を分解させる。 - 特許庁

The defanging treatment is performed on the asbestos by promoting acicular material-free decomposition accompanied with structure destruction using oxidization-reduction reaction induced in a mixed solution by illuminating from the outside a vessel containing a mixed solution of asbestos such as chrysotile, crocidolita, and amosite that are mixed in an aqueous solution.例文帳に追加

水溶液に白石綿、青石綿、茶石綿などのアスベスト（石綿）を混合したものを、その混合液を含む容器の外部からの放射線照射により、混合液中に誘起される酸化還元反応を利用して、構造破壊にともなう非針状化・分解を促進して、アスベストの無害化する処理を行う。 - 特許庁