coating bath temperatureとは 意味・読み方・使い方

In pulling up the metallic band 11 from a plating bath 17 of a hot-dip coating line via the sink roll 18 after immersing the metallic band 11 into the plating bath 17, the advancing sheet temperature of the metallic band 11 into the plating bath 17 is so controlled that the surface temperature of the sink roll 18 attains the temperature higher than the temperature of the plating bath 17.例文帳に追加

溶融めっきラインのめっき浴１７に金属帯１１を浸漬させた後、シンクロール１８を介して前記めっき浴１７から引き上げるにあたり、前記めっき浴１７への前記金属帯１１の進入板温度を、前記シンクロール１８の表面温度が前記めっき浴１７の温度より高くなるように制御する。 - 特許庁

In the method for regenerating the metal bath contaminated with a solid solution, particularly a tin bath 17 in a hot-dip coating process, a partial stream of the tin bath 17 is removed from a coating tank 15 and is first of all heated above its liquid temperature in a heating unit 24.例文帳に追加

固溶体により汚染された金属溶融物、特に錫溶融物(17)を溶融めっき工程で再生するための方法において、錫溶融物(17)の部分流が被覆槽(15)から取り出され、そしてまず加熱ユニット(24)でその液体温度以上に加熱される。 - 特許庁

Subsequently, the regenerated tin bath 17a is heated in a melting tank to a process temperature, and returned from there to the coating tank 15.例文帳に追加

引き続き、再生された錫溶融物(17a) が溶融槽で工程温度に加熱され、そしてそこから被覆槽(15)の中へ戻される。 - 特許庁

The lowest film-forming temperature of a cation electrodeposition paint is set to be lower by 5°C or more than the coating temperature when electrodeposition coating a material to be coated in a cation electrodeposition paint bath.例文帳に追加

カチオン電着塗料浴中で被塗物を電着塗装する際に、カチオン電着塗料の最低造膜温度を塗装温度より５℃以上低く設定することを特徴とするカチオン電着塗装方法。 - 特許庁

This steel sheet is coated by dipping it into a hot dipping coating bath having the above chemical composition and after gas-wiping and applying gas-water cooling are performed, and this steel sheet is held in the temperature range of the solidifying point of the coated layer -130°C for ≥10 sec and the post-heat treatment is applied to produce this coated steel sheet.例文帳に追加

この鋼板は、上記化学組成の溶融めっき浴で浸漬してめっきし、ガスワイピング後気水冷却を施した後、めっき層の凝固温度〜１３０℃の温度領域で１０秒以上保持する後熱処理を施すことにより製造される。 - 特許庁

In the temperature-measuring device 10, a resistance bulb 102 is coated with a coating member 105 consisting of a fluororesin; the circumference of the member 105 is surrounded with a gap by double tubes 106 consisting of a fluororesin to be protected from the outside; the tubes 106 are inserted into a quartz glass tube 101 and the resistance bulb 102 is placed in the APM in a cleaning bath 60.例文帳に追加

温度測定装置１００は，測温抵抗体１０２をフッ素樹脂からなるコーティング部材１０５で被覆し，このコーティング部材１０５の周囲をフッ素樹脂からなる二重チューブ１０６により隙間をもって囲んで外部から保護し，二重チューブ１０６を石英ガラス管１０１内に挿入して測温抵抗体１０２を洗浄槽６０内のＡＰＭ中に入れている。 - 特許庁