room-temperature ferromagnetismとは 意味・読み方・使い方

The obtained GaN exhibits ferromagnetism at room temperature.例文帳に追加

このＧａＮは室温において強磁性を示す。 - 特許庁

The thin semiconductor thin film 24 shows ferromagnetism at room temperature.例文帳に追加

希薄磁性半導体薄膜２４は、常温で強磁性を示す。 - 特許庁

In a room temperature, the magnetic thin film shows ferromagnetism and can provide the large ratio of the spin polarization.例文帳に追加

室温において、強磁性を示し大きなスピン分極率が得られる。 - 特許庁

Where the ferromagnetic fluorine compound represents an alloy with the rare-earth element, iron or cobalt and a compound exhibiting a ferromagnetism at room temperature (approximately 20°C).例文帳に追加

ここで強磁性フッ素化合物とは、希土類元素，鉄又はコバルトとの合金であって、室温（約２０℃）で強磁性を示す化合物をいう。 - 特許庁

A write once type information recording medium is obtained by selecting two kinds of substances 102, 103 the simple of which does not show ferromagnetism at room temperature and forming a film by using the substances 102, 103 so that they coexist on a transparent substrate 101.例文帳に追加

単体では室温で強磁性を示さない物質１０２，１０３を２種類選択し、それを透明基板１０１上に混在するように製膜して追記型情報記録媒体とする。 - 特許庁

To provide a magnetic semiconductor which comprises the zinc oxide thin film in which saturation magnetization and remanent magnetization have the ferromagnetism of a large value in a room temperature, by controlling the carrier density without adding impurities for obtaining carriers while maintaining the crystallinity (quality) of a zinc oxide thin film, and also to provide a method for manufacturing the same, and a ferromagnetism revelation method.例文帳に追加

酸化亜鉛薄膜の結晶性（品質）を維持したまま、キャリアを得るための不純物を添加せずにキャリヤ濃度を制御して、室温において飽和磁化と残留磁化が大きな値の強磁性を発現する酸化亜鉛薄膜からなる磁性半導体とその製造方法及び強磁性発現方法を提供する。 - 特許庁

An object exhibiting ferromagnetism at room temperature is installed in the vicinity of a raw material target holding face in a sputtering cathode having balance type magnetic flux arrangement, thus the magnetic flux arrangement is changed into an unbalance type, and is returned into the balance type by its removal, so that its switching is made possible.例文帳に追加

バランス型磁束配置を有するスパッタリング陰極の原料ターゲット保持面近傍に室温で強磁性を示す物体を設置することにより磁束配置をアンバランス型に変更、取り外すことでバランス型に戻すことによって、切替可能とする。 - 特許庁