To provide a steel sheet excellent in characteristics of stopping initiation of fatigue crack and characteristics of stopping propagation thereof which, when undergoing joint welding, provides the satisfactory shape of a toe-of-weld part in a bead cross-section and hardly initiates fatigue cracks and even if fatigue cracks is initiated, exhibits a long propagation life until the fatigue crack induces a fracture.例文帳に追加

継手溶接を行った場合に、ビード断面における止端部の形状が良好で疲労き裂が発生し難く、またたとえ疲労き裂が発生したとしても破断に到るまでの伝播寿命が長い、疲労き裂の発生阻止特性と伝播阻止特性の両者に優れた鋼材を提供する。 - 特許庁

Steel which restrains at least one of the initiation and progress of a fatigue crack is used as at least one of a web and a flange of an I-girder or a box girder jointed by welding in the steel structure, and reinforcement is performed against the fatigue of the toe of a weld part by toe grinding, pinning, using a low-temperature transformation hot charge, or the like.例文帳に追加

鋼構造物において、溶接による接合がなされるＩ桁または箱桁の、ウエブとフランジの少なくとも一方に、疲労亀裂の発生と進展の少なくとも一方を抑制する鋼材を用い、止端研削、ピンニング、低温変態溶材の使用等による溶接部止端の疲労に対する強化をしてなることを特徴とする。 - 特許庁

To provide a fillet welded joint having high fatigue strength by improving stress concentration, without depending excessively on imposition of compressive residual stress in a weld toe part by a welding material, free from a crack, and excellent also in toughness, and a gas shielded arc welding method for obtaining the fillet welded joint.例文帳に追加

溶接材料による止端部の圧縮残留応力の付与に過度に頼らず、応力集中を改善することで高い疲労強度を有すると共に、割れがなく、靭性にも優れたすみ肉溶接継手、および、このすみ肉溶接継手を得るためのガスシールドアーク溶接方法を提供する。 - 特許庁

To provide a method for designing a joint excellent in fatigue strength, which improves fatigue crack generation property at a weld toe, and increases the fatigue life of the fillet welded joint obtained by lap fillet welding or fillet boxing welding of a sheet or a plate with a thickness of 1-20 mm.例文帳に追加

板厚１〜２０ｍｍの薄板または厚板を重ね隅肉溶接または回し隅肉溶接して得られる隅肉溶接継手の疲労寿命を長大化させるために、溶接止端部の疲労き裂発生特性を改善させた、疲労強度に優れた継ぎ手設計方法を提供する。 - 特許庁