vanadium nitrideとは 意味・読み方・使い方

The production method of a carbon steel material by surface treatment of a carbon steel includes: a nitriding treatment process of forming a nitride or nitrogen-diffusion layer on the surface of the carbon steel; and a molten salt treatment process of immersing the carbon steel after the nitriding treatment in a molten salt bath containing vanadium so as to convert the nitride or nitride-diffusion layer into a coating layer containing vanadium nitride and vanadium carbide.例文帳に追加

炭素鋼材を表面処理した炭素鋼材料の製造方法であって、前記炭素鋼材表面に窒化物ないし窒素拡散層を形成する窒化処理工程と、前記窒化処理後の炭素鋼材をバナジウムを含む溶融塩浴に浸漬し、前記窒化物ないし窒素拡散層をバナジウム窒化物およびバナジウム炭化物を含む被覆層とする溶融塩処理工程とを含むことを特徴とする炭素鋼材料の製造方法。 - 特許庁

A thin film 1 containing vanadium dioxide and consisting mainly of vanadium oxide is formed, directly or through a tin oxide film 2, on a glass plate 7 by a thermal decomposition process (for example, CVD method) and a nitride film 4 is formed as a reflection preventing film, on the thin film 1 by the thermal decomposition process.例文帳に追加

ガラス板７上に直接または酸化錫膜２を介して、二酸化バナジウムを含み、酸化バナジウムを主成分とする薄膜１を熱分解法（例えばＣＶＤ法）により形成し、この薄膜１の上に、反射防止膜として、窒化膜４を熱分解法により形成する。 - 特許庁

The coated layer 14 comprises carbide or carbon nitride containing one element belonging to the IV-B titanium group, the V-B vanadium group or the VI-B chromium group, and the film thickness is 0.1 to 20 μm.例文帳に追加

同被覆層(14)はIV−Ｂチタン族、Ｖ−Ｂバナジウム族、VI−Ｂクロム族のうちの一つの元素を含有する炭化物系又は炭窒化物系の化合物からなり、その膜厚は０．１〜２０μｍである。 - 特許庁

To provide a film formation method and a wear-resistant member capable of obtaining hardness excellent in wear resistance and sufficient adhesiveness by forming, as an intermediate layer, the film of nitride or carbonitride of Ti which is a metal different from vanadium-based metals between a substrate and a vanadium carbide (VC) film coated on an outermost surface.例文帳に追加

基材と最表面層に被膜される炭化バナジウム（ＶＣ）膜との間に中間層としてバナジウム系金属とは異なる異種金属であるＴｉの窒化物膜又は炭窒化物膜を形成することにより、耐摩耗性に優れた硬度及び十分な密着性を得ることができる成膜方法及び耐摩耗性部材を提供する。 - 特許庁

A soln., in which a hard material such as diamond, cubic boron nitride, boron carbide, silicon carbide and silicon nitride or the carbide, nitride, boride, silicide or the like of titanium, zirconium, hafnium, vanadium, niobium, tantalum, chromium and molybdenum, and a hard material of metallic carbonyl such as iron pentacarbonyl are suspended, is heated and decomosed, and a metallic layer is formed on the surface of the hard material.例文帳に追加

ダイヤモンド、立方晶窒化ホウ素、炭化ホウ素、炭化ケイ素、窒化ケイ素、或はチタン、ジルコニウム、ハフニウム、バナジウム、ニオブ、タンタル、クロム、及びモリブデンの炭化物、窒化物、ホウ化物、ケイ化物等の硬質物質を、鉄ペンタカルボニル等の金属カルボニルの硬質物質が懸濁した液を加熱分解し、硬質物質の表面に金属層を生成させる。 - 特許庁

The graphite crucible 4 which is disposed on the lower part in a heating furnace body 2 has on its inner face, a coated film 5 comprising the nitride of at least one material selected from hafnium, niobium, zirconium, tungsten, vanadium, molybdenum, rhenium, iridium, ruthenium and osmium.例文帳に追加

加熱炉本体２内の下部に配置される黒鉛るつぼ４の内側面に、ハフニウム、ニオブ、ジルコニウム、タングステン、バナジウム、モリブデン、レニウム、イリジウム、ルテニウム、オスミウムから選ばれる少なくとも１種の材料の窒化物でなる被覆膜５を形成した。 - 特許庁

A protective coating is provided to a metal surface by applying a nickel or tantalum plate layer to the metal surface and dispersing particles of a hard material such as diamond, alumina, vanadium nitride, tantalum carbide, and/or tungsten carbide within the nickel or tantalum plate layer as the plating is occurring.例文帳に追加

金属表面にニッケル又はタンタルのめっき層を塗工し、めっきを行いながらダイヤモンド、アルミナ、窒化バナジウム、炭化タンタル及び／又は炭化タングステンなどの硬質材料の粒子をニッケル又はタンタルのめっき層の中に分散させることによって、金属表面に保護皮膜を設ける。 - 特許庁

This engine is provided with the cylinder block having a cylinder liner made of aluminum base composite reinforced by ceramic including at least one of silicon carbide and alumina, and the piston rings coated by nitride film 20 containing vanadium nitride layer 21 exposed to an outer circumference slide surface 17.例文帳に追加

本発明のエンジンは、シリンダライナが炭化珪素またはアルミナの少なくともいずれかを含むセラミックで強化されたアルミニウム基複合材で形成されたシリンダブロックと、外周摺動面１７に露出する窒化バナジウム層２１を含む窒化物皮膜２０が被覆されているピストンリングとを備えることを特徴とする。 - 特許庁