Transmissivity when the ethanol solution of Tb(acac)_3 with a concentration of 2 mass% is transmitted by 10 cm and transmissivity when the ethanol solution of Tb(acac)_3 with a concentration of 6 mass% is transmitted by 3 cm are estimated from the measured value.例文帳に追加
その値から濃度2質量％のTb(acac)_3のエタノール溶液を10cm透過したときの透過率と、濃度6質量％のTb(acac)_3のエタノール溶液を3cm透過したときの透過率とを見積もった。 - 特許庁
An ethanol solution of 0.5 mass% of terbium(III)trisacetylacetonate(Tb(acac)_3) is prepared, and the ultraviolet visible absorption spectrum of the solution is measured.例文帳に追加
テルビウム(III)トリスアセチルアセトナート（Tb(acac)_3）の0.5質量％エタノ−ル溶液を調製し、当該溶液の紫外可視吸収スペクトルを測定した。 - 特許庁
The rubber composition comprises 100 pts.wt. diene rubber and zirconium acetyl acetonate Zr(acac)_4 and iron acetyl acetonate Fe(acac)_3 in amounts yielding a total amount of metals in these compounds of 0.15-0.35 pts.wt. and a weight ratio of Zr(acac)_4/Fe(acac)_3 of from 60/40 to 20/80.例文帳に追加
ジエン系ゴム１００重量部並びに、ジルコニウムアセチルアセトナートＺｒ（ａｃａｃ）_4及び鉄アセチルアセトナートＦｅ（ａｃａｃ）_3をそれらの化合物中の金属量の和が０．１５〜０．３５重量部で、且つ、Ｚｒ（ａｃａｃ）_4／Ｆｅ（ａｃａｃ）_3の重量比率が６０／４０〜２０／８０となる量で含んでなるゴム組成物。 - 特許庁
As a result, zero-valent Ru and trivalent Ru(ACAC)_3 are produced and the Ru film can be formed.例文帳に追加
その結果、０価のＲｕと、３価のＲｕ（ＡＣＡＣ）_3が生成し、Ｒｕ膜を形成することができる。 - 特許庁
A polyol is allowed to react with an organic polyisocyanate in the presence of a catalyst composition comprising a metal complex catalyst represented by general formula (1) M(acac)_n (wherein M is Fe, Mn, Cu, Zr, Th, Ti, Ni, Al or Co; acac represents acetylacetonate; n is an integer of ≥1 and ≤4) and a compound having a cumulative double bond.例文帳に追加
下記一般式（１） Ｍ（ａｃａｃ）_ｎ （１）（式中、Ｍは、Ｆｅ、Ｍｎ、Ｃｕ、Ｚｒ、Ｔｈ、Ｔｉ、Ｎｉ、Ａｌ又はＣｏであり、ａｃａｃはアセチルアセトナートを表し、ｎは１以上４以下の値を有する整数である）で示される金属錯体触媒と累積二重結合を有する化合物とからなる触媒組成物の存在下で、ポリオールと有機ポリイソシアナートとを反応させる。 - 特許庁
This artificial superlattice nanoparticle is made by alternately laminating not less than two oxides of different chemical compositions on the concentric circle of a spherical nucleus by epitaxially growing not less than two oxides of different chemical compositions on a particle of different chemical composition in a solution, and the oxides contain barium titanate or strontium titanate, and diisopropoxide diacetylacetonate (Ti(iPrO)2(AcAc)2, TPA) is used as the source of titanium of the oxides.例文帳に追加
２種類以上の化学組成の異なる酸化物を溶液中で、化学組成の異なる粒子上にエピタキシャルに成長させることにより、球状の核の同心円上に化学組成の異なる酸化物の２種類以上を交互に積層し、球状とした人工超格子ナノ粒子であり、前記酸化物はチタン酸バリウム、またはチタン酸ストロンチウムを含み、前記酸化物のチタン源として、ジイソプロポキシドジアセチルアセトナート（Ti(iPrO)2(AcAc)2、TPA）を用いる。 - 特許庁
When the metal catalyst deposited on the carbon nanotube is manufactured by fixing the metal catalyst in the carbon nanotube, an opening and a defective part are formed on the surface of the carbon nanotube by oxidizing the carbon nanotube by using nitric acid or the like, a precursor substance (an acac complex etc.) of the metal catalyst is introduced into the carbon nanotube through the formed opening and the metal catalyst is fixed in the carbon nanotube.例文帳に追加
カーボンナノチューブに金属触媒を固定して、カーボンナノチューブに担持した金属触媒を作製するに際し、カーボンナノチューブを硝酸等で酸化処理してカーボンナノチューブ表面に開口部及び欠陥部形成し、金属触媒の前駆体物質（ａｃａｃ錯体等）を、開口部を通してカーボンナノチューブ内に導入し、金属触媒をカーボンナノチューブ内に固定する。 - 特許庁
The platinum acetylacetonato complex is produced by reacting a halogen-free platinum (IV) oxo- or hydroxo-compound with a reducing agent in an aqueous solution in the presence of a stoichiometric or higher amount of acetylacetone (acac), potassium acetylacetonate (Kacac), sodium acetylacetonate (Naacac), hexafluoroacetylacetone (hfac), trifluoroacetylacetone (tfac), or alkyl-substituted acetylacetones or their salts and an H^+ donor.例文帳に追加
ハロゲン不含の白金（ＩＶ）オキソ化合物またはヒドロキソ化合物を還元剤と水溶液中で化学量論量またはそれを上回る量のアセチルアセトン（ａｃａｃ）、カリウムアセチルアセトナート（Ｋａｃａｃ）ナトリウムアセチルアセトナート（Ｎａａｃａｃ）、ヘキサフルオロアセチルアセトン（ｈｆａｃ）、トリフルオロアセチルアセトン（ｔｆａｃ）またはアルキル置換アセチルアセトンまたはそれらの塩およびＨ^＋供与体の存在下で反応させることによって、白金アセチルアセトナト錯体を製造する。 - 特許庁