「cathode layer arc method」に関連した英語例文の一覧と使い方 - Weblio英語例文検索

To provide a cathode suitable for depositing a metal coating layer of high quality on a superalloy base at a high speed using a cathode arc deposition method, and a manufacturing method thereof.例文帳に追加

陰極アーク堆積法を用いて超合金基体上に高品質の金属コーティング層を高速で堆積するのに適した陰極およびその製造方法を提供する。 - 特許庁

The CrN film as the 1st layer is formed by a cathode arc ion plating method in which the pressure of gaseous nitrogen is controlled to 20 to 50 mTorr, and bias voltage is controlled to 0 V.例文帳に追加

第１層のＣｒＮ膜は、窒素ガス圧を２０〜５０ｍＴｏｒｒ、バイアス電圧を０Ｖとするカソードアークイオンプレーティング法によって形成される。 - 特許庁

In covering the surface of a unidirectional silicon steel sheet after the completion of finish annealing with a plurality of ceramic film layers, a very thin TiNO film, as the first layer, is formed by a hollow cathode method (HCD method) using an arc cut bias voltage as the bias voltage and then forming thereon a ceramic film by a magnetron-sputtering method.例文帳に追加

仕上げ焼鈍済みの一方向性珪素鋼板の表面に、複数層のセラミック被膜を被覆するに際し、少なくとも第１層については、バイアス電圧としてアークカットバイアス電圧を使用する中空陰極法（ＨＣＤ法）を用いてTiNOの極薄被膜を被成し、ついでその上にマグネトロン・スパッタ法を用いてセラミック被膜を被成する。 - 特許庁

On the surface of a base material composed of metal or ceramic, an amorphous carbon film is formed by a cathode discharge type arc ion plating method using a carbon target and moreover, on the boundary between the carbon film and the base material, a mixed layer of 10 to 500 Å thickness composed of the base material constituting elements and film constituting elements is formed to obtain a high adhesion amorphous carbon film forming material.例文帳に追加

金属またはセラミックからなる基材の表面に、カーボンターゲットを用いてカソード放電型アークイオンプレーティング法により非晶質炭素膜を形成すると共に、該炭素皮膜と基材の界面に、これら基材構成元素と皮膜構成元素とからなる厚さ１０〜５００Åの混合層を形成し、高密着性非晶質炭素皮膜形成材を得る。 - 特許庁

The crack repairing method for metal parts 13 having cracks 15, whereby the crack is washed and oxide layer is removed, and a repairing alloy 17 is applied by at least either of the cathode arc evaporation process and low-pressure plasma metallization so as to cover the crack 15, and the work 13 is heated at a temperature and with pressure enough to block the crack 15.例文帳に追加

金属部品（１３）のクラック修繕方法であって、このクラック修繕方法は、クラック（１５）を有する金属部品（１３）を提供し、クラック（１５）を洗浄して酸化物層を除去し、カソードアーク蒸着および低圧プラズマ溶射の少なくとも一方によって修繕合金（１７）を施してクラック（１５）を覆い、クラック（１５）を塞ぐのに十分な温度および圧力で部品（１３）を加熱することを含む。 - 特許庁