Stretcher Strainとは 意味・読み方・使い方

To provide a steel sheet for a can which has excellent aging properties and workability, and in which stretcher strain and the generation of the variation in the height of a can barrel are not generated at the time of being used as the stock for a deformed can, and to provide its production method.例文帳に追加

異形缶の素材として用いた時に、ストレッチャーストレインや缶胴高さの変動を発生することのない時効性と加工性に優れた缶用鋼板とその製造方法を提案する。 - 特許庁

To provide an Al-Mg-based alloy sheet excellent in press formability in which generation of SS (stretcher-strain) marks is suppressed, without causing a new problem such as deterioration in bendability by age hardening at room temperature.例文帳に追加

室温での時効硬化による曲げ性の低下などの新たな問題が生じることなしに、ＳＳマークの発生が少なく、プレス成形性に優れたＡｌ−Ｍｇ系合金板を提供する。 - 特許庁

To prevent a stretcher strain mark from appearing at edge parts of a steel sheet, due to tension imparted thereon for improving a sheet passability, and temperature difference in a width direction generated in a cooling zone in a cooling process.例文帳に追加

通板性向上のために付与した張力及び冷却帯での冷却過程における幅方向温度差に起因して、鋼板のエッジ部（端部）にストレッチャ−ストレインが発生してしまうことを防止する。 - 特許庁

To provide a coated steel sheet in which, after ordinary hot dipping and coating/baking, yield elongation is suppressed to ≤3% to suppress deterioration in appearance due to the occurrence of buckling pattern and stretcher strain at bending.例文帳に追加

通常の溶融めっきと塗装焼付けを行った後に、降伏伸びを３％以下に抑制して曲げ加工時の腰折れ模様やストレッチャーストレインの発生に伴う外観の低下を抑制した塗装鋼板を提供する。 - 特許庁

To provide a continuous annealing facility with which the development of stretcher strain and wrinkle pattern in a baking-hardened steel sheet can be prevented by eliminating uneven temperature in the width direction of a steel strip in a rapid cooling zone outlet side having a gas-jet cooling facility.例文帳に追加

ガスジェット冷却設備を有する急冷帯出側における鋼帯幅方向の温度むらを解消し、焼付け硬化性鋼板のストレッチャーストレインやしわ模様の発生を防止することができる連続焼鈍設備を提供する。 - 特許庁

Generation of the stretcher strain marks in press molding under severe forming conditions is suppressed by devising temper treatment after the final annealing when the Al-Mg based aluminum alloy sheet consisting of a specific composition containing Mg, Zn is manufactured and making a position of a first proximity peak obtained by analyzing EELS spectrums on a K loss end of Mg to be measured by electronic energy loss spectroscopy of the sheet be within a specific range.例文帳に追加