PROCESS FOR STRENGTHENING QUARTZ GLASS MEMBER AND STRENGTHENING-TREATED QUARTZ GLASS CRUCIBLE例文帳に追加

石英ガラス部材の強化方法と強化処理した石英ガラスルツボ - 特許庁

The crucible demonstrates reduced bubble growth during a Czochralski process.例文帳に追加

るつぼは、チョクラルスキー工程の間、減少した気泡成長を示す。 - 特許庁

In the necking process and the following diameter increasing process, the rotation number of the crucible is set similarly not higher than 0.1 rpm.例文帳に追加

絞り工程およびこれに続く増径工程で、ルツボ回転数を、同じく０．１ｒｐｍ以下とする。 - 特許庁

Further, the resultant synthetic silica glass powder is molded into a quartz glass crucible by arc-fusion process, and thus obtained quartz glass crucible has a high DF rate.例文帳に追加

また、得られる合成シリカガラス粉は、アーク溶融法により石英ガラスルツボに成型され、高いＤＦ率の石英ガラスルツボが得られる。 - 特許庁

There are provided an anti-corrosion crucible and a method for manufacturing the same in which colloid-like alumina solution is coated on a crucible for a melting operation, and then alumina is dispersed and immersed into the crucible through its heating process.例文帳に追加

溶解用ルツボにコロイド状アルミナ溶液を塗布し、加熱することによりアルミナを拡散含浸させたことを特徴とする耐浸食性ルツボおよびその製造方法。 - 特許庁

REFLECTOR, HEATING CRUCIBLE EQUIPPED WITH THE REFLECTOR, AND PROCESS FOR PREPARATION OF RADIATION IMAGE TRANSFORMING PANEL例文帳に追加

リフレクタ、それを備えた加熱用るつぼおよび放射線像変換パネルの製造方法 - 特許庁

When the silicon single crystal is manufactured by a CZ process, a crucible (C/C crucible) consisting of a carbon fiber reinforced carbon material having an ash content of ≤1 ppm is used as the crucible for housing the quartz crucible and the silicon single crystal is pulled up at a pulling up speed of 0.3 to 0.5 mm/min.例文帳に追加

ＣＺ法によりシリコン単結晶を製造する場合に、石英坩堝を収容する坩堝として、灰分1ppm以下の炭素繊維強化炭素材からなる坩堝（Ｃ／Ｃ坩堝）を使用し、0.3〜0.5mm／minの引き上げ速度でシリコン単結晶を引き上げる。 - 特許庁

As there is no magnetic field, the unstableness at squeezing process is avoided by increasing the rotational frequency of the crucible.例文帳に追加

無磁場としているので、坩堝回転数を高めたことによる絞りの不安定が回避される。 - 特許庁