活性炭は、石炭系または石油系重質油由来の活性炭であって、直径が２〜５０ｎｍのポアの全ポアに対する容積比率が２０〜７０％の範囲内にある。例文帳に追加

The activated carbon is activated carbon originating in coal-based or petroleum oil-based heavy oil and characterized in that the volume ratio of pores each having a pore diameter of 2-50 nm is 20-70% based on the total pores. - 特許庁

廃木材、廃竹材、古紙、トウモロコシの芯部破砕品、使用済みプラスチック等の有機系廃棄物を用いて、石炭を原料とする活性炭と同等の強度並びに性能を有する活性炭を安価に且つ安定して製造する。例文帳に追加

To provide a method for producing activated carbon, by which the activated carbon having the same strength and performance as those of activated carbon produced from coal can stably be produced at a low cost from organic wastes such as waste wood, waste bamboo, waste paper, crushed corn cores or used plastics. - 特許庁

木質炭化物粉末と石炭粉末とにバインダーを添加したものを原料とし、混練、成型、炭化、賦活して木質系粒状活性炭化物を製造する。例文帳に追加

A raw material prepared by adding a binder to a mixture of a woody carbide powder and a coal powder is subjected to kneading, molding, carbonization, and activation, thus producing the woody granular active carbide. - 特許庁

活性炭の製造方法は、キノリン不溶分を２〜５０質量％含む石炭系または石油系重質油のいずれか一方またはそれらの混合物を生コークス化する生コークス化工程と、得られる生コークスを賦活する賦活工程とを有する。例文帳に追加

The method for producing activated carbon comprises: a raw coke forming process comprising converting one kind or a mixture of coal-based heavy oil and petroleum oil-based heavy oil, each containing 2-50 mass% of components insoluble in quinoline, into a raw coke; and an activation process for activating the obtained raw coke. - 特許庁

レニウムが担体としての石炭系、ココナッツ系又はピート系活性炭中に極めて均一に分布して担持されており、かつ、水素化圧力を著しく低くしても、ジカルボン酸類に対する著しく良好な水素化能及びラクトン類等への非常に高い選択性を有する新規なパラジウム‐レニウム系触媒を提供する。例文帳に追加

To produce a novel palladium-rhenium catalyst having rhenium extremely uniformly distributed and carried on a coal, coconut or peat type activated carbon as a carrier and having a good hydrogenation capability for dicarboxylic acids and very high selectivity to lactones even if hydrogenation pressure is extremely lowered. - 特許庁

活性炭の製造方法は、キノリン不溶分を２〜５０質量％含む石炭系または石油系重質油のいずれか一方またはそれらの混合物を生コークス化する生コークス化工程と、得られる生コークスに周期表第４周期の金属を添着する金属添着工程と、金属を添着した生コークスを賦活する賦活工程とを有する。例文帳に追加

This manufacturing method of an activated carbon includes a green coking process in which either one of coal or petroleum-based heavy oil containing 2-50 mass% quinoline insoluble or their mixture is made into a green coke, a metal impregnation process in which a metal in the forth period of the Periodic Table is impregnated on the resultant green coke, and an activation process in which the metal-impregnated green coke is activated. - 特許庁

石油系重質油および/または石炭系重質油を熱処理して得られたコークスに、カルシウム化合物を添加混合し、該混合物中のカルシウム含有量が100重量ppm以上10,000重量ppm以下となるように調製された炭素質物または該炭素質物に焼成および微粉砕処理を施した低温焼成炭素粉末を電気二重層キャパシタ用活性炭の製造原料として用いる。例文帳に追加

A calcium compound is mixed with cokes which are obtained by heat-treating petroleum heavy oil or coal heavy oil, and a carbonaceous material which is prepared so that the calcium content of the mixture is 100 wtppm to 10,000 wtppm, or a low temperature sintered carbon powder which is obtained by sintering and pulverizing the carbonaceous material is used as a manufacturing material of an activated carbon for an electric double layer capacitor. - 特許庁

また、活性炭の製造方法は、人造黒鉛電極試験法によって測定される熱膨張係数が４．０〜７．０の範囲内にある石炭系または石油系重質油のいずれか一方またはそれらの混合物を生コークス化する生コークス化工程と、得られる生コークスを賦活する賦活工程とを有する。例文帳に追加

Also, the method for producing activated carbon comprises: a raw coke forming process comprising converting one kind or a mixture of coal-based heavy oil and petroleum oil-based heavy oil, each having a coefficient of thermal expansion of 4.0-7.0, measured by an artificial graphite electrode testing method, into a raw coke; and an activation process for activating the obtained raw coke. - 特許庁

バイオマス、ごみ、下水汚泥などの有機資源、及び石炭等を炭化水素系固体燃料として利用するガス化炉を用いたガス化システムにおいて、下流に設けられたタール吸収塔から抜き出された活性炭の有効利用を図ると同時に、ガス化炉内でのチャーのガス化を促進させて、総合的なガス化効率を図ることのできるガス化システムを提供する。例文帳に追加

To provide a gasification system, which uses a gasification furnace for utilizing organic resources of biomass, refuse, sewer sludge, etc. and coal or the like as hydrocarbon-based solid fuels, as can make effective use of an active charcoal drawn out of a tar absorptioon tower provided in the downstream and as can achieve a comprehensive gasification efficiency by promoting the gasification of char inside the gasification furnace. - 特許庁