耐熱れんがの英語

表面に少なくとも１種の耐熱性樹脂にポリテトラフルオロエチレン樹脂を配合した塗膜を形成し、裏面に表面と同系の耐熱性樹脂にポリテトラフルオロエチレンが無配合の塗膜を形成し、表裏面での対塗膜の静摩擦係数が０．１以上にした。例文帳に追加

A coating film in which a polytetrafluoroethylene(PTFE) resin is incorporated into at least one heat resistant resin is formed on a surface, a coating film in which no polytetrafluoroethylene is added into a heat resistant resin similar to that of the surface is formed on a back, and the friction coefficients of the coating films in the surface and the back are made at least 0.1. - 特許庁

従来材質の酸化アルミニウム−酸化クロム系耐火煉瓦の酸化アルミニウム部分をスピネル粒子と置き換えることにより、耐食性・耐熱衝撃性に優れたス酸化クロム−スピネル質耐火煉瓦を得た。例文帳に追加

The chromium oxide-spinel-based refractory brick having excellent corrosion resistance and thermal shock resistance is obtained by substituting aluminum oxide parts of an aluminum oxide-chromium oxide refractory brick being a conventional material with spinel particles. - 特許庁

緻密性の高い電鋳煉瓦が金属被膜で被覆された、耐久性が高く耐熱構造材として有用な金属被膜付き電鋳煉瓦を提供する。例文帳に追加

To provide an electrocast brick with a metal film which is obtained by coating the electrocast brick having high denseness with the metal film and which has high durability and is useful as a heat resistant structural material. - 特許庁

耐酸化性、耐食性及び耐熱衝撃性に優れた、溶融金属容器の内張り用耐火れんが又は溶融金属流路用耐火物として好適な炭素含有耐火物を提供すること。例文帳に追加

To provide a carbon-containing refractory having excellent oxidation resistance, corrosion resistance and thermal shock resistance and suitable as a refractory brick for the lining of a molten metal vessel or a refractory for a molten metal flow passage. - 特許庁

耐食性と耐熱衝撃性とともに高熱間強度、さらには、耐スラグ浸透性に優れ、十分な耐用性を有するカーボンピックアップを生じにくい低カーボン不焼成れんがを提供すること。例文帳に追加

To provide a low carbon unfired brick being excellent in corrosion resistance, thermal shock resistance, high high-temperature strength and slag penetration resistance and having sufficient service durability and hardly causing carbon pick-up. - 特許庁

リボンド質マグネシア−クロム質れんがにおいて、高熱間強度・高耐食性と耐熱衝撃性を兼ね備え、高耐用が得られる材質を提供すること。例文帳に追加

To provide a material having both of high hot strength-high corrosion resistance and thermal shock resistance and attaining high durability in a rebonded magnesia-chromium based brick. - 特許庁

溶射時における溶融性に優れ、溶射後における炉壁れんがとの熱膨張率の一致性、圧縮強度、耐熱性に優れる溶射補修材料を提供する。例文帳に追加

To provide a material for repair by thermal spraying, which is superior in meltability in a thermal spraying operation, superior in conformity of a coefficient of thermal expansion with that of a furnace wall brick after the thermal spraying operation, and superior in compressive strength and heat resistance. - 特許庁

長寿命でエネルギーロスが少なく溶銑に対する耐食性に優れ、さらに耐熱衝撃性にも優れた耐用性の高い高炉炉床用れんがを提供すること。例文帳に追加

To provide a highly durable brick for a blast furnace hearth having a long lifetime, less liable to cause energy loss, excellent in corrosion resistance to molten iron, and excellent also in thermal shock resistance. - 特許庁