Dm-2とは 意味・読み方・使い方

Preferably, negative electrode current density is 0.5 A/dm^2-50 A/dm^2, the temperature of plating bath is 10°C-60°C, the pH of the plating bath is 4.5-6.5, and plating period is 1 minute-30 minutes.例文帳に追加

また、陰極電流密度は０．５〜５０Ａ／ｄｍ^2、めっき浴の温度は１０〜６０℃、めっき浴のｐＨは４．５〜６．５、めっき時間は１〜３０分であることが好ましい。 - 特許庁

At this time, pulse current having an average current density of relatively low (0.5A/dm^2) and having an intermittently high current density of (5A/dm^2) is caused to flow.例文帳に追加

このとき、平均電流密度が比較的低く（０．５Ａ／ｄｍ^２）、断続的（間欠的）に高電流密度（５Ａ／ｄｍ^２）となるパルス電流を流すようにする。 - 特許庁

Specifically, the copper foil preferably has the roughening fine alloy-particle layer comprising copper of 5-13 mg/dm^2-cobalt of 6-13 mg/dm^2-nickel of 5-12 mg/dm^2, provided on the surface to be bonded with the resin substrate of the copper foil.例文帳に追加

具体的には銅箔の樹脂基板と接着される接着面に５〜１５ｍｇ／ｄｍ^２銅−６〜１３ｍｇ／ｄｍ^２コバルト−５〜１２ｍｇ／ｄｍ^２ニッケルとからなる合金微細粗化粒子層を設けてなると良い。 - 特許庁

The method includes zinc-electroplating a steel sheet at a current density of ≤150 A/dm^2 using a sulfuric acidic plating bath that contains 0.05-0.3 mol/l magnesium sulfate and has a zinc concentration of ≥1.0 mol/l.例文帳に追加

硫酸マグネシウムを0.05 〜 0.3 mol/l含有し、亜鉛濃度が1.0mol/l以上である、硫酸酸性のめっき浴を用いて、150A/dm^2以下の電流密度で電気亜鉛めっき処理する。 - 特許庁

The coating weight of silver in each silver halide emulsion unit is ≤11 g/dm2 and that of the gelatin vehicle in each silver halide emulsion unit is ≤11 mg/dm2.例文帳に追加

各々のハロゲン化銀乳剤ユニットにおける銀の付着量は11mg／dm^2 以下であり、各々のハロゲン化銀乳剤ユニットにおけるゼラチン状ベヒクルの付着量は11mg／dm^2以下である。 - 特許庁

The copper alloy layer contains 50-500 μg/dm^2 nickel and 30-300 μg/dm^2 molybdenum.例文帳に追加

本発明において、銅合金層に含有されるニッケルは５０μｇ／ｄｍ^２から５００μｇ／ｄｍ^２であり、モリブデンは３０μｇ／ｄｍ^２から３００μｇ／ｄｍ^^２である。 - 特許庁

In the anodizing step, the current density can be controlled to 0.025-0.25 A/dm^2.例文帳に追加

陽極酸化工程は、０．０２５〜０．２５Ａ／ｄｍ^２の電流密度で行うことができる。 - 特許庁