Hemihydrateとは 意味・読み方・使い方

It is more preferable that a gypsum hemihydrate of 0.5-1.5% is added and mixed.例文帳に追加

０．５〜１．５％の半水石膏を添加、混合するとより好ましい。 - 特許庁

PRODUCTION PROCESS OF REGENERATED HEMIHYDRATE GYPSUM AND PRODUCTION PROCESS OF SOIL SOLIDIFICATION AGENT例文帳に追加

再生半水石膏の製造方法及び土壌固化材の製造方法 - 特許庁

To provide gypsum hemihydrate requiring a long time to start the hardening.例文帳に追加

半水石膏が硬化し始めるまでの時間の長い半水石膏を製造する。 - 特許庁

The cement comprises gypsum dihydrate and gypsum hemihydrate, the percentage of gypsum hemihydrate being 50 mass% or more in terms of SO_3 based on the sum of gypsum dihydrate and gypsum hemihydrate, and comprises diethylene glycol in an amount of 150 ppm or less.例文帳に追加

セメント中の２水石膏及び半水石膏の合量に占める半水石膏量がSO_3換算で50質量％以上であり、かつ、ジエチレングリコールの含有量が150ppm以下であるセメント。 - 特許庁

In the method for manufacturing a β-type gypsum hemihydrate slurry, the slurry is made by irradiating the mixture of β-type gypsum hemihydrate and water having a water mixing ratio of 30-60 wt.% to β-type gypsum hemihydrate with ultrasonic waves.例文帳に追加

β型半水セッコウに対する水の混合率が３０〜６０重量％のβ型半水セッコウと水との混合物に、超音波を照射してスラリーにすることを特徴とするβ型半水セッコウスラリーの製造法。 - 特許庁

To provide a production process of regenerated hemihydrate gypsum, by which regenerated hemihydrate gypsum can be produced at a low cost so as to enable effective utilization of waste of gypsum formed bodies and application of the resulting regenerated hemihydrate gypsum to the production of a soil solidification agent.例文帳に追加

コスト上安価で且つ石膏成型体廃材の有効利用を図ることができ、しかも、土壌固化材への適用も可能な石膏を製造する。 - 特許庁

In the cement, ([dihydrate]+[hemihydrate])/[total SO_3] is preferably 40 mass% or more, wherein [dihydrate] represents SO_3 in gypsum dihydrate; [hemihydrate] represents SO_3 in gypsum hemihydrate; [total SO_3] represent total SO_3 in cement.例文帳に追加

上記セメントは、（〔２水〕＋〔半水〕）／〔全SO_3〕が40質量％以上であることが好ましい（なお、〔２水〕は２水石膏のSO_3、〔半水〕は半水石膏のSO_3、〔全SO_3〕はセメント中の全SO_3、を示す）。 - 特許庁

It is preferable that the ratio of SO_3 in gypsum dihydrate and gypsum hemihydrate per total SO_3 is ≥40 mass% and the ratio of gypsum hemihydrate per total of gypsum dihydrate and hemihydrate expressed in terms of SO_3 is ≥30 mass%.例文帳に追加

上記水硬性組成物においては、全SO_3に対する２水石膏及び半水石膏中のSO_3の割合が40質量％以上であり、かつ、２水石膏及び半水石膏の合量に対する半水石膏の割合がSO_3換算で30質量％以上であることが好ましい。 - 特許庁