austemperとは 意味・読み方・使い方

AUSTEMPER TREATMENT OF SPHEROIDAL GRAPHITE CAST IRON例文帳に追加

球状黒鉛鋳鉄のオーステンパー処理方法 - 特許庁

This process imparts abrasive resistance as austemper ductile iron to the oscillating pipe 6a, and the cast iron article is held at the atmosphere adjusting sub-temperature for a predetermined time prior to so-called austemper processing, thereby reducing the distortion amount due to thermal treatment as compared with the case where austemper treatment is merely performed.例文帳に追加

これにより、揺動管６ａに、オーステンパダクタイルアイアンとしての耐摩耗性を付与させると共に、所謂オーステンパ処理の前に雰囲気調整副温に所要時間保持することで、熱処理に伴う歪量を、単なるオーステンパ処理を行う場合に比して低減させる。 - 特許庁

Further, after the austemper treatment of the cast iron, the cast iron dipped into the molten tin, is taken out and the cast iron is dipped into cooling liquid for a prescribed time (rapid cooling process) to remove the stuck molten tin.例文帳に追加

また、鋳鉄のオーステンパ処理後、溶融錫に浸漬した鋳鉄を取り出し、鋳鉄を冷却液に所定時間浸漬して（急冷却工程）付着した溶融錫を除去した。 - 特許庁

Besides, in an austemper treatment, after dipping the cast iron into the molten tin, the cast iron is exposed to the atmosphere having the same temperature as the temperature of the metal bath (atmospheric bath process) to remove the molten tin under sticking process.例文帳に追加

また、オーステンパ処理で、鋳鉄を溶融錫に浸漬後、金属浴と同じ温度の大気雰囲気に晒して（大気浴工程）付着過程にある溶融錫を除去した。 - 特許庁

One pair of bills 14, 15 in the break-down machine for casting gate, with which the cast product and a feeder head or a runner are separated from the gate portions, are constituted by integrally forming with a casting of a spheroidal graphite cast iron and applying an austemper treatment.例文帳に追加

鋳物製品と押湯または湯道を堰の部分より分離する鋳物堰破断機における一対のビル１４，１５を、球状黒鉛鋳鉄による鋳造で一体成型し、オーステンパ処理を施した構成とする。 - 特許庁

To obtain high strength spheroidal graphite cast iron as cast which includes a dense structure free from bainite and cementite and having satisfactory machinability, includes high strength satisfying the tensile strength of ≥900 MPa and satisfactory elongation of ≥4% even without the addition of Al, includes excellent machinability, is substitutible for forged steel, cast steel and austemper spheroidal graphite cast iron, and can contribute to the service life and lightening as parts.例文帳に追加

鋳放しで、ベイナイトやセメンタイトのない被削性の良好な緻密な組織からなり、Ａｌの添加なしでも、引張強さ９００ＭＰａ以上の高強度と、４％以上の良好な伸びを有し、優れた被削性を有し、鍛鋼や鋳鋼、オーステンパ球状黒鉛鋳鉄の代替化、部品としての寿命や軽量化に寄与できる鋳放し高強度球状黒鉛鋳鉄を得ることを目的とする。 - 特許庁