impact tensile testとは 意味・読み方・使い方

The spheroidal graphite cast iron has ≥650 MPa tensile strength and ≥10% elongation and also has ≥10 J/cm^2 impact value by the Charpy impact test (U-notch) at -40°C test temperature.例文帳に追加

引張強さが６５０ＭＰａ以上、伸びが１０％以上で、また、試験温度が−４０℃におけるＵノッチシャルピー衝撃試験による衝撃値が１０Ｊ／ｃｍ^２以上の球状黒鉛鋳鉄である。 - 特許庁

To provide a film for forming with combined heat resistance, chemical resistance, flame-retardancy, impact resistance and wet heat resistance, and especially excellent in tensile elongation and numbers of flexing by an MIT flexural test.例文帳に追加

耐熱性、耐薬品性、難燃性、耐衝撃性および耐湿熱性を兼ね備え、特に引っ張り伸度とＭＩＴ屈曲試験回数が優れている成形用フィルムを提供する。 - 特許庁

To provide a non-contact type elongation measurement system capable of performing a high speed tensile test such as an impact fracture test, free from restriction by type or shape of material of a specimen and capable of measuring a change of a length between gauge points comparatively simply.例文帳に追加

衝撃破壊のような高速引張試験に対応可能で、試験片の材料の種類や形状にも制約を受けることなく、比較的簡便に標点間の長さの変化を測定可能な非接触式の伸び測定システムを提供する。 - 特許庁

The polyurethane foam contains aromatic ester groups and has properties of the total density of ≤600 kg/m3 the elongation percentage of ≥300%, the tensile strength of ≥12 kg/cm2 and the impact resistance measured by a ball drop test of ≤40%.例文帳に追加

芳香族エステル基を含有するポリウレタン発泡体は６００ｋｇ／ｍ３以下の成形密度において、伸長率３００％以上、引張強度１２ｋｇ／ｃｍ２以上の物性を有し、かつ剛球落下試験によって測定される反発弾が４０％以下である。 - 特許庁

To provide a welding wire for high strength and high toughness steel, which welding wire can achieve weld metal having a tensile strength of 1,300 MPa or higher and an absorbed energy of _VE_-40 of 27J in the 2 mm V notch Charpy impact test at -40°C.例文帳に追加

引張強さＴＳが１３００ＭＰａ以上で、かつ−４０℃での２ｍｍＶノッチシャルピー衝撃試験における吸収エネルギー_ＶＥ_−４０が２７J以上の溶接金属を達成できる、高強度高靭性鋼用溶接ワイヤを提供する。 - 特許庁

To provide a high strength link chain in which tensile strength lies in a high strength region of ≥1,650 MPa (≥1,155 MPa expressed in terms of chain strength) with a round rod test piece, which has an excellent balance in strength-ductility, and has excellent impact resistance and hydrogen embrittlement resistance, and to provide a method for producing the high strength link chain.例文帳に追加

本発明は、引張強度が丸棒試験片にて１６５０ＭＰａ以上（チェーン強度換算で１１５５ＭＰａ以上）の高強度域にて、強度−延性バランスに優れ、耐衝撃特性、耐水素脆性特性に優れた高強度リンクチェーンとその製造方法を提供する。 - 特許庁

To provide a method capable of calculating the value of a strain by which a resin material required for executing impact simulation of a resin product is broken without performing a tensile test in accordance with a strain speed of an actual product, and calculating prediction of an experimental condition reaching breakage only by the impact simulation in the small, two or three, number of times.例文帳に追加

樹脂製品の衝撃シミュレーションの実施に際し必要とされる樹脂材料が破壊する歪みの値を、実製品の歪み速度に合わせた引張試験を行わなくても算出できること、２〜３回の少ない衝撃シミュレーションだけで破壊に至る実験条件の予想を算出できること。 - 特許庁