refractory materialsとは 意味・読み方・使い方

A refractory fine powder and a refractory aggregate are used as main raw materials, and thin refractory bubbles, each having a particle diameter of ≤2 mm and a thickness of 1/4 to 1/20 of the outer diameter, are incorporated in an amount of 20 to 90 mass % as the refractory aggregate, so that the thermal conductivity becomes ≤2.0.例文帳に追加

耐火性微粉末と耐火性骨材を主材料とし、粉径が２ｍｍ以下で、その肉厚が外径の１／４〜１／２０と薄い耐火性バブルを骨材として２０〜９０質量％含有させて、熱伝導率が２．０以下とした。 - 特許庁

The refractory material for repairing the coke oven which is provided with the desired characteristics is obtained by blending ≥2 refractory materials in three kinds of refractory materials described in claims 1, 2 and 3.例文帳に追加

また、本願請求項１，２及び３の耐火材のうち２以上を配合して用いることにより、所望の特性を備えたコークス炉補修用耐火材を得る。 - 特許庁

To provide a surface treatment method for a refractory for furnace materials, a furnace, and furnace walls by which the erosion of corrosion gas to the refractory and the sticking of heat-treated materials and the ashes thereof can be prevented, and simultaneously, the wear resistance of the refractory can be improved.例文帳に追加

耐火物への腐食ガスの浸食と、加熱処理物やその灰分の付着防止、耐火物の耐磨耗性の向上が同時に図れる炉材用耐火物および炉ならびに炉壁の表面処理方法を提供する。 - 特許庁

The porosity of the granulated aggregate used for the graphite-containing monolithic refractory and mixed with the graphite and refractory materials is controlled to ≤2 vol.%.例文帳に追加

黒鉛含有不定形耐火物に使用される、黒鉛と耐火原料とを混合して造粒された造粒骨材の気孔率を２体積％以下とする。 - 特許庁

To provide a phenol resin composition for carbon materials and for refractory materials having good fluidity in melting, having residual carbon ratio after burning and suitably useable as a binder used when producing carbon materials and refractory materials or as a raw material used when producing carbon materials.例文帳に追加

溶融時の流動性が良好で、且つ、焼成後の残炭率が高く、炭素材料や耐火物を製造する際の結合剤として、又は炭素材料を製造する際の原料として、好適に用いられ得る炭素材料用及び耐火物用フェノール樹脂組成物を提供すること。 - 特許庁

This magnesia-carbon type refractory mainly comprising a magnesia-based refractory material and a carbonaceous refractory material is constituted by comprising 80-97 pts.mass magnesia-based refractory material and 3-20 pts.mass carbonaceous refractory material, in which materials with ≤0.1 mm particle size occupy less than 7 mass% within the 80-97 pts.mass magnesia-based refractory material.例文帳に追加

マグネシア系耐火材と炭素系耐火材とを主成分とするマグネシア−カーボン質耐火物において、８０〜９７質量部のマグネシア系耐火材と、３〜２０質量部の炭素系耐火材とを含んで構成され、前記マグネシア系耐火材８０〜９７質量部のうち、粒度０．１ｍｍ以下の材料の含有率が７質量％未満であることを特徴とするマグネシア−カーボン質耐火物。 - 特許庁

To provide a method for manufacturing a wet refractory material low in mass and high in adhesion strength and heat insulating properties by uniformly kneading refractory materials largely different in specific gravity, an apparatus for manufacturing the wet refractory material and a wet refractory material spraying device.例文帳に追加

比重の大きく異なる耐火材の材料を均一に混練することにより、質量が小さく、付着力及び断熱性の大きい湿潤耐火材を製造する方法とその装置及びその耐火材を吹付ける装置を提供することを課題とする。 - 特許庁