high bainiteとは 意味・読み方・使い方

The high tensile strength hot rolled steel sheet has a composite structure containing, by a volume ratio, 5 to 70% bainite, and the balance substantially ferrite.例文帳に追加

ベイナイトを体積率で５〜７０％含み、残部が実質的にフェライトからなる複合組織を有し、フェライト中に以下の（１）式を満たす範囲でＴｉおよびＭｏを含む析出物が分散析出している。 - 特許庁

The method for manufacturing a high-carbon cold rolled steel sheet with high hardenability, comprises hot rolling a steel containing C of 0.2-0.7 mass%, to control the structure so as to have a bainite phase with a volume factor of greater than 20%, and cold rolling and annealing it to make a spheroidizing structure.例文帳に追加

Ｃを0.2〜0.7質量％含有する鋼に熱間圧延を行い、体積率20％を超えるベイナイト相を有する組織に制御した後、冷間圧延および焼鈍を行い、球状化組織とする高焼入れ性高炭素冷延鋼板の製造方法。 - 特許庁

High strength steel having a tensile strength of ≥570MPa is subjected to regulation of components so that an Ac_4 point to form an (α+γ)2 phase in a high temperature region from a γ single phase exists in ≤1,400°C, and the structure of the weld heat-affected zone consists of a bainite single phase.例文帳に追加

引張強さが ５７０ ＭＰａ以上の高強度鋼について、γ単相から高温域における（α＋γ）２ 相となるＡｃ_４点が１４００℃以下に存在し、かつ溶接熱影響部の組織をベイナイト単相になるように成分調整を行う。 - 特許庁

To provide steel combining high toughness and free cuttability and capable of contributing to the reduction of the production cost of machine parts and the miniaturizing and lightening of the parts in bainite type non- heattreated steel.例文帳に追加

ベイナイト型非調質鋼において、時効処理を施さずに高靱性化と快削性を兼備させることが可能となり、機械部品製造コスト低減や部品の小型軽量化に貢献できる鋼を提供することである。 - 特許庁

In the method of producing the high strength steel pipe having excellent workability, a structure consisting essentially of bainite and martensite is adopted to a hot rolled sheet subjected to cold rolling, the draft in the cold rolling is controlled to 25 to 95%, annealing is performed, and joining is carried out.例文帳に追加

冷間圧延に供する熱延板をベイナイト、マルテンサイトを主体とする組織とし、冷間圧延の圧下率を２５〜９５％とし、焼鈍を行い、接合することを特徴とする加工性に優れた高強度鋼管の製造方法。 - 特許庁

A high strength steel wire rod having excellent unprocessed drawability is characterized in that the area ratio of a pearlitic structure is ≥97%, and the balance nonpearlitic structure composed of bainite, pseudo pearlite and proeutectoid ferrite, and the grain size of pearlite blocks is 20 to 45 μm.例文帳に追加

パーライト組織の面積率が９７％以上、残部がベイナイト、擬似パーライト、初析フェライトからなる非パーライト組織であり、パーライトブロック粒径が２０μｍ以上４５μｍ以下であることを特徴とする、生引き性に優れた高強度鋼線材である。 - 特許庁

Further, since its structure consists essentially of bainite and is uniform, to a high stress amplitude in a low cycle fatigue region, its yield stress is higher than that in a structure consisting essentially of ferrite such as a DP steel on the same strength level, the skid resistance of dislocation to repeated stress is high, and the generation of a fatigue crack can be suppressed.例文帳に追加

また、ベイナイト主体で均一な為、低サイクル疲労域での高い応力振幅に対しては、同一強度レベルのＤＰ鋼のようなフェライト相主体の組織よりも、降伏応力が高い為に、繰り返し応力に対する転位のすべり抵抗が高く、疲労亀裂の発生を抑制できる。 - 特許庁

This invention is a high strength and high ductility cold rolled steel sheet contg. ferrite, bainite and ≥3% residual austenite and moreover is the one in which, among 4 pieces of ΔEl measured by the following method, the maximum value is suppressed to ≤2.0% to improve the variation in elongation in the sheet width direction.例文帳に追加

フェライト、ベイナイト及び３％以上の残留オーステナイトを有する高強度高延性冷延鋼板であって、更に、下記方法で測定される４個のΔＥｌのうち、最大値が２．０％以下に抑制されることにより板幅方向における伸びのバラツキが改善された高強度高延性冷延鋼板である。 - 特許庁